US3957600A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of and anodes for use in electrowinning metals
Assignee: IMI Refinery Holdings Ltd
•
Filing: 1974-12-20
•
Granted: 1976-05-18
•
Expires: 1994-12-20
Abstract
Abstract Anodes of alloys, which may be fragmented and used in baskets, of passive film-forming metals and elements having atomic numbers 23-29 for use in electrowinning metals, methods of using such anodes, and electrowinning cells incorporating such anodes.
Inventors
- 👤 Andrew George Ives
- 👤 John Roger Bawden Gilbert
- 👤 Jan Stephan Jacobi
- 👤 Ian Robert Scholes
- 👤 David John Astley
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 16:13
CPC Classifications
C; C25; C25C; C25C7/00; C25C7/02; C25D; C25D7/00; C25D7/02
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
94 words
A method of electrowinning metal comprising electrolysing an aqueous solution of metal using as an anode an alloy containing one or more high melting point passive film-forming metals selected from the group consisting of titanium, zirconium, niobium and tantalum and one or more of the elements of atomic numbers 23- 29 in the Periodic System of Elements, the amount of elements 23- 29 being greater than that at which passivation of the alloy occurs and less than that amount at which dissolution of the alloy occurs at more than half the faradaic dissolution rate.
Claim 2
Independent Claim
94 words
A method of electrowinning metal comprising electrolysing an aqueous solution of metal using as an anode an alloy containing one or more high melting point passive film-forming metals selected from the group consisting of titanium, zirconium, niobium and tantalum and one or more of the elements of atomic numbers 23- 29 in the Periodic System of Elements, the amount of elements 23- 29 being greater than that at which passivation of the alloy occurs and less than that amount at which dissolution of the alloy occurs at more than half the faradaic dissolution rate.
Claim 3
Dependent Claim
25 words
A method as claimed in claim 1 in which the dissolution rate does not exceed 20mm/year at a current density of 500 amps/m 2 .
Claim 4
Dependent Claim
16 words
A method as claimed in claim 2 in which the dissolution rate does not exceed 10mm/year.
Claim 5
Dependent Claim
27 words
A method as claimed in claim 1 in which the anode material is a copper-titanium alloy, copper being present in an amount in the range 35- 80wt%.
Claim 6
Dependent Claim
97 words
A method as claimed in claim 4 in which the alloy contains in addition one or more of the elements selected from the group consisting of hydrogen up to 2000 parts per million; aluminium up to 5wt%; chromium up to 10%; tin up to 5%; oxygen up to 1.5%; vanadium up to 2%; molybdenum up to 5%; silicon up to 1%; manganese up to 30%; palladium up to 0.5%; platinum up to 0.5%; ruthenium up to 0.5%; iridium up to 0.5%; phosphorus up to 10%; carbon up to 15%, the additional elements totalling no more than 40%.
Claim 7
Dependent Claim
27 words
A method as claimed in claim 4 in which the anode material is a copper-titanium alloy, copper being present in an amount in the range 40- 60wt%.
Claim 8
Dependent Claim
24 words
A method as claimed in claim 1 in which the alloy is a titanium-manganese alloy, manganese being present in an amount of 30- 85wt%.
Claim 9
Dependent Claim
18 words
A method as claimed in claim 7 in which manganese is present in an amount of 40- 60wt%.
Claim 10
Dependent Claim
26 words
A method as claimed in claim 1 in which the alloy is a nickel-titanium alloy, nickel being present in an amount in the range 35- 80%.
Claim 11
Dependent Claim
22 words
A method as claimed in claim 9 in which nickel is present in an amount in the range 40- 60% by weight.
Claim 12
Dependent Claim
19 words
A method as claimed in claim 1 in which the anode is a solid anode formed of the alloy.
Claim 13
Dependent Claim
25 words
A method as claimed in claim 1 in which the alloy is an iron-titanium alloy, iron being present in the range 80- 20% by weight.
Claim 14
Dependent Claim
28 words
A method as claimed in claim 1 in which the alloy is a titanium-cobalt alloy, cobalt being present by an amount in the range 30- 55% by weight.
Claim 15
Independent Claim
156 words
A method of recovering an electrowinnable metal from an aqueous solution of the metal which comprises the steps of inserting an anode and a cathode into the aqueous solution, connecting the anode to a positive potential with respect to the cathode, passing an electrical current through the anode and the cathode to electrodeposit the metal onto the cathode and removing the cathodically deposited metal from the solution, characterised in that the anode has as its electrically conducting surface an alloy containing one or more high melting point passive film-forming metals selected from the group consisting of titanium, zirconium, niobium and tantalum and one or more of the elements of atomic numbers 23- 29 of the Periodic System of Elements, the amount of elements 23- 29 being greater than that at which passivation of the alloy occurs and less than that amount at which dissolution of the alloy occurs at more than half the faradaic dissolution rate.
Claim 16
Independent Claim
156 words
A method of recovering an electrowinnable metal from an aqueous solution of the metal which comprises the steps of inserting an anode and a cathode into the aqueous solution, connecting the anode to a positive potential with respect to the cathode, passing an electrical current through the anode and the cathode to electrodeposit the metal onto the cathode and removing the cathodically deposited metal from the solution, characterised in that the anode has as its electrically conducting surface an alloy containing one or more high melting point passive film-forming metals selected from the group consisting of titanium, zirconium, niobium and tantalum and one or more of the elements of atomic numbers 23- 29 of the Periodic System of Elements, the amount of elements 23- 29 being greater than that at which passivation of the alloy occurs and less than that amount at which dissolution of the alloy occurs at more than half the faradaic dissolution rate.
Claim 17
Dependent Claim
27 words
A method as claimed in claim 14 in which the dissolution rate does not exceed 20mm/year at a current density of 500 amps/m 2 at the anode.
Claim 18
Dependent Claim
16 words
A method as claimed in claim 15 in which the dissolution rate does not exceed 10mm/year.
Claim 19
Independent Claim
108 words
A method of electrowinning metal comprising electrolysing an aqueous solution of metal using as an anode a basket of foraminate high melting point passive, film-forming metal containing in particulate form an alloy containing one or more high melting point passive film-forming metals selected from the group consisting of titanium, zirconium, niobium and tantalum, and one or more of the elements of Atomic Numbers 23- 29 in the Periodic System of Elements, the amount of Elements 23- 29 being greater than that at which passivation of the alloy occurs and less than that amount at which dissolution of the alloy occurs at more than half the faradaic dissolution rate.
Claim 20
Independent Claim
108 words
A method of electrowinning metal comprising electrolysing an aqueous solution of metal using as an anode a basket of foraminate high melting point passive, film-forming metal containing in particulate form an alloy containing one or more high melting point passive film-forming metals selected from the group consisting of titanium, zirconium, niobium and tantalum, and one or more of the elements of Atomic Numbers 23- 29 in the Periodic System of Elements, the amount of Elements 23- 29 being greater than that at which passivation of the alloy occurs and less than that amount at which dissolution of the alloy occurs at more than half the faradaic dissolution rate.
Claim 21
Dependent Claim
18 words
A method as claimed in claim 17 in which the particulate material is periodically added to the basket.
References Cited (Backward Citations)
US2117284A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-05-18 | 1979-11-17 | 1980-05-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-05-18 | 1983-11-17 | 1984-05-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-05-18 | 1987-11-17 | 1988-05-18 | $7700.00 | Window Closed / Lapsed |