Extraction of zinc and lead from their sulfides
Assignee: Individual
•
Filing: 1974-05-06
•
Granted: 1976-05-18
•
Expires: 1994-05-06
Abstract
Abstract Sulfidic ores of lead or zinc such as galena or sphalerite are smelted under vacuum in the absence of CO 2 and oxygen with a flux consisting of solid NaOH or KOH to free the lead or zinc as free metal and to form sodium or potassium disulfides which are used as flux in smelting additional sulfidic ores to liberate more metal and form still higher polysulfides of sodium or potassium also usable as flux up to the pentasulfide form. By the process of the invention, substantially complete use is made of the sulfur atoms initially combined with the lead or zinc to remove the sulfur combined with said metals. Potassium hydroxide, its lower sulfur content polysulfides can be reconstituted by exposing to air a leach solution of potassium pentasulfide.
Inventors
- 👤 Rollan Swanson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 20:09
CPC Classifications
C; C22; C22B; C22B15/00; C22B15/0002; C22B15/001; C22B15/0021; C22B1/00; C22B1/11; C22B13/00; C22B13/02; C22B15/0013; C22B15/0017; C22B19/00; C22B5/00; C22B5/02
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
66 words
A process for extracting zinc and/or lead from a sulfidic ore thereof, comprising smelting said ore under vacuum in the absence of water, CO 2 and oxygen with a flux consisting of the tetrasulfide of sodium or potassium thereby liberating said zinc and/or lead in the free state and forming the pentasulfides of said potassium or sodium and separating the zinc and/or lead from the pentasulfide.
Claim 2
Dependent Claim
66 words
A process for extracting zinc and/or lead from a sulfidic ore thereof, comprising smelting said ore under vacuum in the absence of water, CO 2 and oxygen with a flux consisting of the tetrasulfide of sodium or potassium thereby liberating said zinc and/or lead in the free state and forming the pentasulfides of said potassium or sodium and separating the zinc and/or lead from the pentasulfide.
Claim 3
Dependent Claim
32 words
The process of claim 1 wherein said smelting is carried out with potassium tetrasulfide and further including the step of thermally decomposing the separated potassium pentasulfide to potassium tetrasulfide and recycling same.
Claim 4
Dependent Claim
26 words
The process of claim 1, wherein said smelting is carried out with potassium tetrasulfide at a temperature in the range of over 206°C. but below 300°C.
Claim 5
Dependent Claim
202 words
A process for extracting zinc and/or lead from a sulfidic ore thereof, comprising: A. smelting said ore under vacuum in the absence of water, carbon dioxide and oxygen by intimately mixing said ore with a flux consisting of fused sodium or potassium hydroxide to form lead and/or zinc metal, lead and/or zinc oxide and the disulfide of sodium or potassium; B. separating said metal from said disulfide; C. smelting additional amounts of said sulfidic ore under the above stated conditions of the first step but using a flux consisting of the separated disulfide to form additional metal and the trisulfide of sodium or potassium; D. separating said additional metal from said trisulfide; E. smelting further amounts of said sulfidic ore under the above stated conditions of the first step but using a flux consisting of the separated trisulfide to form further metal and the tetrasulfide of sodium or potassium; F. separating said further metal and said tetrasulfide; G. smelting more of said sulfidic ore under the above stated conditions of the first step but using a flux consisting of the separated tetrasulfide to form more metal and the pentasulfide of sodium or potassium; H. separating said last formed metal and said pentasulfide.
Claim 6
Dependent Claim
202 words
A process for extracting zinc and/or lead from a sulfidic ore thereof, comprising: A. smelting said ore under vacuum in the absence of water, carbon dioxide and oxygen by intimately mixing said ore with a flux consisting of fused sodium or potassium hydroxide to form lead and/or zinc metal, lead and/or zinc oxide and the disulfide of sodium or potassium; B. separating said metal from said disulfide; C. smelting additional amounts of said sulfidic ore under the above stated conditions of the first step but using a flux consisting of the separated disulfide to form additional metal and the trisulfide of sodium or potassium; D. separating said additional metal from said trisulfide; E. smelting further amounts of said sulfidic ore under the above stated conditions of the first step but using a flux consisting of the separated trisulfide to form further metal and the tetrasulfide of sodium or potassium; F. separating said further metal and said tetrasulfide; G. smelting more of said sulfidic ore under the above stated conditions of the first step but using a flux consisting of the separated tetrasulfide to form more metal and the pentasulfide of sodium or potassium; H. separating said last formed metal and said pentasulfide.
Claim 7
Dependent Claim
13 words
The process of claim 4, further including the step of dehydrating said ore.
Claim 8
Dependent Claim
57 words
The process of claim 4, wherein the separation of step H comprises heating the last formed metal and said pentasulfide under vacuum and in the absence of carbon dioxide, water and oxygen whereby the pentasulfide forms the tetrasulfide and sulfur, and said sulfur is recoverable as a layer between the tetrasulfide and last formed metal upon cooling.
Claim 9
Dependent Claim
18 words
The process of claim 4, wherein zinc and/or lead sulfide is present in an excess over said hydroxide.
Claim 10
Dependent Claim
39 words
The process according to claim 4, wherein lead is formed and said lead is separated from the polysulfides of sodium or potassium by heating the melt to about 320°C. and pouring out the melted polysulfides, leaving behind said lead.
Claim 11
Dependent Claim
38 words
The process of claim 4, wherein zinc is formed and said zinc is separated from the polysulfides of sodium or potassium by heating the melt to around 325°C. and pouring out the melted polysulfides leaving behind said zinc.
Claim 12
Dependent Claim
12 words
The process of claim 4, wherein said ores are galena or sphalerite.
Claim 13
Dependent Claim
57 words
The process according to claim 4, wherein said mixing of step (A) comprises completely melting said hydroxide, adding about one third of the stoichiometric amount of said sulfidic ore, reducing the temperature of the resulting melt, adding about another third of said amount of said ore, further reducing the temperature and adding the rest of said ore.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-05-18 | 1979-11-17 | 1980-05-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-05-18 | 1983-11-17 | 1984-05-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-05-18 | 1987-11-17 | 1988-05-18 | $7700.00 | Window Closed / Lapsed |