Non-combustible light-weight inorganic shaped articles and process of manufacture
Assignee: Sekisui Chemical Co Ltd
•
Filing: 1972-09-26
•
Granted: 1976-05-18
•
Expires: 1992-09-26
Abstract
Abstract A method of producing a non-combustible light-weight shaped article, which comprises shaping a mixture comprising (a) powders of silicon or a silicon alloy, (b) inorganic powders having a porous or hollow structure and (c) water glass, and maintaining the resulting shaped article at a temperature of 15 DEG to 120 DEG C. thereby to foam and cure it.
Inventors
- 👤 Tadashi Matsuda
- 👤 Kazuo Tanaka
- 👤 Kazuma Taura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 08:17
CPC Classifications
C; C04; C04B; C04B28/00; C04B28/24; C04B28/26; Y; Y10; Y10S; Y10S264/00; Y10S264/06; Y10S264/17; Y10S264/63
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
155 words
A method of producing a non-combustible light weight shaped article, which consists essentially of shaping a mixture consisting essentially of: a. 100 parts by weight of powders of silicon or a silicon alloy containing at least 50% by weight of silicon, b. 100-200 parts by weight of inorganic powders having a porous or hollow structure, c. 100-1200 parts by weight of water glass, d. up to 80 parts by weight, per 100 parts by weight of the sum total of (a), (b) and (c), of a fibrous material and e. up to 80 parts by weight, per 100 parts by weight of the sum total of (a), (b), and (c), of a fire-proofness improving agent; compressing the resulting shaped article until the bulk density of the shaped article is increased to 1.5 to 12 times that before shaping; and maintaining the resulting shaped article at a temperature of 15°-120°C. thereby to foam and cure it.
Claim 2
Independent Claim
155 words
A method of producing a non-combustible light weight shaped article, which consists essentially of shaping a mixture consisting essentially of: a. 100 parts by weight of powders of silicon or a silicon alloy containing at least 50% by weight of silicon, b. 100-200 parts by weight of inorganic powders having a porous or hollow structure, c. 100-1200 parts by weight of water glass, d. up to 80 parts by weight, per 100 parts by weight of the sum total of (a), (b) and (c), of a fibrous material and e. up to 80 parts by weight, per 100 parts by weight of the sum total of (a), (b), and (c), of a fire-proofness improving agent; compressing the resulting shaped article until the bulk density of the shaped article is increased to 1.5 to 12 times that before shaping; and maintaining the resulting shaped article at a temperature of 15°-120°C. thereby to foam and cure it.
Claim 3
Dependent Claim
31 words
The method of claim 1 wherein said silicon alloy is selected from the group consisting of ferrosilicon, calcium silicide, ferrosilicon aluminum, silicon manganese aluminum, calcium silicon manganese, silicon manganese and silicochromium.
Claim 4
Dependent Claim
36 words
The method of claim 1 wherein said porous or hollow inorganic powders are selected from the group consisting of powders of pearlite rock, pumice microballoon, carbon micro-balloon, glass microballoon, foamed shale pumice, foamed clay and vermiculite.
Claim 5
Dependent Claim
33 words
The method of claim 1 wherein said mixture contains 1 to 10 parts by weight of the fibrous material, per 100 parts by weight of the sum total of (a), (b) and (c).
Claim 6
Dependent Claim
40 words
The method of claim 4 wherein said fibrous material is selected from the group consisting of chrysotile asbestos, hard serpentine asbestos, anthophyllite asbestos, amosite asbestos, tremolite asbestos, actinolite asbestos, crocidolite asbestos, rock wool, slag wool, glass fibers and metal fibers.
Claim 7
Dependent Claim
34 words
The method of claim 1 wherein said mixture contains 10 to 50 parts by weight of the fire-proofness improving agent per 100 parts by weight of the total amount of (a), (b) and (c).
Claim 8
Dependent Claim
53 words
The method of claim 6 wherein said fire-proofness improving agent is selected from the group consisting of (i) inorganic powders which contain water of crystallization and release it at high temperatures to form water vapor, (ii) inorganic powders which decompose and absorb heat at high temperatures, and (iii) a mixture of these powders.
Claim 9
Dependent Claim
69 words
The method of claim 7 wherein said inorganic powders (i) are selected from the group consisting of powders of aluminum hydroxide, calcium hydroxide, clays, alum, hydrated gypsum, sodium sulfate hydrate and disodium phosphate hydrate, and said inorganic powders, (ii) are selected from the group consisting of powders of calcium carbonate, magnesium carbonate, zinc carbonate, cadmium carbonate, sodium nitrate, lead nitrate, aluminum sulfate, ammonium phosphate, ammonium carbonate and ammonium sulfate.
Claim 10
Independent Claim
188 words
A method of continuously producing a non-combustible light-weight shaped article which consists essentially of: 1. compression molding a mixture consisting essentially of: a. 100 parts by weight of powders of silicon or a silicon alloy containing at least 50% by weight of silicon, b. 100-200 parts by weight of inorganic powders having a porous or hollow structure, c. 100-1200 parts by weight of water glass, d. up to 80 parts by weight, per 100 parts by weight of the sum total of (a), (b) and (c), of a fibrous material and e. up to 80 parts by weight, per 100 parts by weight of the sum total of (a), (b) and (c), of a fire-proofness improving agent by feeding it into a compression space formed between an endless belt, the inside surface of which contacts compression rolls and a feed plate moving at substantially the same speed as the endless belt and in the same direction as the movement of the endless belt, to an extent such that the bulk density of the compressed article is 1.5 to 12 times that of the shaped article before compression, and
Claim 11
Independent Claim
188 words
A method of continuously producing a non-combustible light-weight shaped article which consists essentially of: 1. compression molding a mixture consisting essentially of: a. 100 parts by weight of powders of silicon or a silicon alloy containing at least 50% by weight of silicon, b. 100-200 parts by weight of inorganic powders having a porous or hollow structure, c. 100-1200 parts by weight of water glass, d. up to 80 parts by weight, per 100 parts by weight of the sum total of (a), (b) and (c), of a fibrous material and e. up to 80 parts by weight, per 100 parts by weight of the sum total of (a), (b) and (c), of a fire-proofness improving agent by feeding it into a compression space formed between an endless belt, the inside surface of which contacts compression rolls and a feed plate moving at substantially the same speed as the endless belt and in the same direction as the movement of the endless belt, to an extent such that the bulk density of the compressed article is 1.5 to 12 times that of the shaped article before compression, and
Claim 12
Dependent Claim
23 words
introducing the shaped article into reaction chambers maintained at a temperature of 15° to 120°C. thereby to foam and cure the shaped article.
Claim 13
Dependent Claim
23 words
introducing the shaped article into reaction chambers maintained at a temperature of 15° to 120°C. thereby to foam and cure the shaped article.
Claim 14
Dependent Claim
9 words
The product produced by the process of claim 1.
References Cited (Backward Citations)
US3103254A
Cited
US3150988A
Cited
US3218683A
Cited
US3203813A
Cited
US3707386A
Cited
US3480509A
Cited
US3450547A
Cited
US3707385A
Cited
US3586747A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-05-18 | 1979-11-17 | 1980-05-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-05-18 | 1983-11-17 | 1984-05-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-05-18 | 1987-11-17 | 1988-05-18 | $7700.00 | Window Closed / Lapsed |