Solder glass with refractory filler
Assignee: OI Glass Inc
•
Filing: 1974-07-30
•
Granted: 1976-05-04
•
Expires: 1994-07-30
Abstract
Abstract Disclosed is a physical blend of particulate lead borate sealing glass and particulate refractory filler for use in forming thermal fusion seals for workpieces having a lower coefficient of thermal expansion than the sealing glass. The particulate refractory filler has a particle size diameter in excess of about 37 microns (i.e. plus 400 U.S. Sieve) to lower the expansion while maintaining adequate flow during fusion. The blend is especially useful as a package sealant for electronic components.
Inventors
- 👤 Josef Francel
- 👤 Robert F. Palermo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 23:12
CPC Classifications
B; B23; B23K; B23K35/00; B23K35/22; B23K35/24; C; C03; C03C; C03C27/00; C03C3/00; C03C3/04; C03C3/062; C03C3/07; C03C3/072; C03C3/074; C03C3/0745; C03C3/12; C03C3/14; C03C3/142; C03C8/00; C03C8/24; C03C8/245
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
124 words
In a physical blend of particulate lead-borate solder glass and particulate low expansion refractory filler said filler having a coefficient of thermal expansion of less than about 65 × 10.sup. -7 /°C (0-300°C), for use in thermal fusion sealing to a workpiece having a lower coefficient of thermal expansion than said solder glass, the improvement wherein said refractory filler has a particle size diameter in excess of about 37 microns and not substantially in excess of 150 microns whereby the flow is increased and the coefficient of thermal contraction is decreased upon fusion sealing when compared to the flow and thermal contraction properties of a blend of the same composition which has a refractory filler particle size substantially less than 37 microns in diameter.
Claim 2
Dependent Claim
124 words
In a physical blend of particulate lead-borate solder glass and particulate low expansion refractory filler said filler having a coefficient of thermal expansion of less than about 65 × 10.sup. -7 /°C (0-300°C), for use in thermal fusion sealing to a workpiece having a lower coefficient of thermal expansion than said solder glass, the improvement wherein said refractory filler has a particle size diameter in excess of about 37 microns and not substantially in excess of 150 microns whereby the flow is increased and the coefficient of thermal contraction is decreased upon fusion sealing when compared to the flow and thermal contraction properties of a blend of the same composition which has a refractory filler particle size substantially less than 37 microns in diameter.
Claim 3
Dependent Claim
16 words
The blend of claim 1 wherein said refractory filler is a lithium aluminosilicate, aluminosilicate, or zircon.
Claim 4
Dependent Claim
25 words
The blend of claim 1 wherein said particulate refractory filler is present in the proportion of about 1 to 25% by weight of said blend.
Claim 5
Dependent Claim
25 words
The blend of claim 1 wherein said particulate refractory filler is present in the proportion of about 5 to 20% by weight of said blend.
Claim 6
Dependent Claim
35 words
The blend of claim 1 wherein said solder glass has the composition consisting essentially of: Oxide % by Weight
______________________________________
PbO 70-85
ZnO 0-20
B.sub.2 O.sub.3 5-15
SiO.sub.2 0-10
BaO 0-3
SnO.sub.2 0-5 .
______________________________________
Claim 7
Dependent Claim
35 words
The blend of claim 1 wherein said solder glass has the composition consisting essentially of: Oxide % by Weight
______________________________________
PbO 75-85
ZnO 2-16
B.sub.2 O.sub.3 8-15
SiO.sub.2 0-15
BaO 0-2
SnO 0-2 .
______________________________________
Claim 8
Dependent Claim
85 words
The method of forming a fusion seal on a workpiece comprising applying the blend of the solder glass and particulate refractory filler of claim 1 to said workpiece and thermally fusing said blend at temperature in the range of 350° to 500°C and for a time period in the range of about 1 minute to about 1 hour to flow and fuse said blend into a strong, hermetic seal having a coefficient of thermal contraction less than the solder glass initially present in said blend.
Claim 9
Dependent Claim
32 words
The method of claim 7 wherein said temperature is in the range of about 350° to 450°C and said time is in the range of about 5 minutes to about 30 minutes.
Claim 10
Dependent Claim
85 words
The method for forming a fusion seal on a workpiece comprising applying the blend of the solder glass and particulate refractory filler of claim 2 to said workpiece and thermally fusing said blend at temperature in the range of 350° to 500°C and for a time period in the range of about 1 minute to about 1 hour to flow and fuse said blend into a strong, hermetic seal having a coefficient of thermal contraction less than the solder glass initially present in said blend.
References Cited (Backward Citations)
US2863782A
Cited
US3250631A
Cited
US3275358A
Cited
US3454408A
Cited
US3425817A
Cited
US3258350A
Cited
US3778242A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-05-04 | 1979-11-03 | 1980-05-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-05-04 | 1983-11-03 | 1984-05-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-05-04 | 1987-11-03 | 1988-05-04 | $7700.00 | Window Closed / Lapsed |