Agent for the treatment of cellulosic fiber materials and process

Claim 2

In a process for treating native cellulose fiber material to remove natural fatty, collenchymatous, pectin and lignin substances as well as residues of seed coats and oily contaminations due to spinning and weaving, comprising treating said fiber material at an elevated temperature of between about 90° and 140°C. with a strongly alkaline aqueous bath containing between about 5 and 10 g./l. of alkali metal hydroxide, the improvement which comprises said alkaline bath containing a phosphonic acid compound selected from the group consisting of an amino alkylene phosphonic acid, a 1-hydroxy lower alkane-1,1-diphosphonic acid alkali metal salts thereof and mixtures thereof.

Claim 3

The process as defined by claim 1 wherein said fiber material is cotton.

Claim 4

The process as defined by claim 1, wherein said alkaline bath further comprises a water-soluble sequestering agent selected from the group consisting of alkali metal polyphosphates, amino polycarboxylic acids, citric acid, gluconic acid, salts thereof and mixtures thereof.

Claim 5

The process as defined by claim 1, wherein said alkaline bath further comprises a wetting agent capable of retaining its wetting power in said alkaline bath and being compatable with said phosphonic acid compound.

Claim 6

The process as defined by claim 1, wherein said phosphonic acid compound is present in the alkaline bath in an amount of about 0.3 g./l. and about 5 g./l.

Claim 7

The process as defined by claim 5, wherein said alkaline bath further comprises a sequestering agent selected from the group consisting of alkali metal polyphosphates, amino polycarboxylic acids, citric acid, gluconic acid, salts thereof and mixtures thereof in an amount between about 0.25:1 and about 4:1 with respect to said phosphonic acid compound.

Claim 8

The process as defined by claim 1, wherein said phosphonic acid compound is amino tris-(methylene phosphonic acid).

Claim 9

The process as defined by claim 1, wherein said phosphonic acid compound is ethylene diamino tetra-(methylene phosphonic acid).

Claim 10

The process as defined by claim 1, wherein said phosphonic acid compound is a 1-hydroxy alkane-1,1-diphosphonic acid.

Claim 11

The process as defined by claim 1, wherein said phosphonic acid compound is selected from the group consisting of amino alkylene phosphonic acids of the formula: ##EQU10## wherein R 1 is the group of the formula ##EQU11## while R 2 is a member selected from the group consisting of the group of the formula ##EQU12## the group of the formula ##EQU13## wherein X is one of the numerals 2 and 3; y is one of the numerals 0 to 4; while R and R 3 are members selected from the group consisting of hydrogen and the group of the formula ##EQU14## and the group of the formula ##EQU15## wherein R 4 is hydrogen; R 5 is a member selected from the group consisting of lower alkyl and R 4 and R 5 together form lower alkylene; R 6 is a member selected from the group consisting of hydrogen and the group of the formula ##EQU16## and z is one of the numerals 0 and 1; and the alkali metal salts thereof.

Claim 12

The process as defined by claim 10, wherein said alkaline bath further comprises an alkali metal polyphosphate of the formula: Me.sub.n.sub.+2 P.sub.n O.sub.3n.sub.+1 wherein Me is an alkali metal and n is one of the numerals 2 to 24.

Claim 13

The process as defined by claim 1, wherein said alkaline bath further comprises sodium dithionite in an amount sufficient to inhibit degradation of the cellulose chain by atmospheric oxygen.

Claim 14

The process as defined by claim 12, wherein said sodium dithionite is present in an amount of about 1 g./l.

Claim 15

The process as defined by claim 1, wherein said alkaline bath comprises between about 0.3 and 5 g./l. of said phosphonic acid compound, a sequestering compound selected from the group consisting of alkali polyphosphates, amino polycarboxylic acids, citric acid, gluconic acid, their salts, and mixtures thereof, the proportion of phosphonic acid compound to sequestering compound being between about 0.15:1 and about 4.0:1, and sodium dithionite in an amount sufficient to inhibit degradation of the cellulose chain by atmospheric oxygen.

Claim 16

The process as defined by claim 10 wherein said phosphonic acid compound is selected from the group consisting of amino tris-(methylene phosphonic acid); diethylene triamino penta-(methylene phosphonic acid); 1,2- and 1,3-propylene diamino tetra-(methylene phosphonic acid); ethylene diamino tetra-(methylene phosphonic acid); 1,2-cyclohexane diamino tetra-(methylene phosphonic acid); 1-amino methyl cyclopentylamino-(2)-tetra-(methylene phosphonic acid; dipropylene triamino penta-(methylene phosphonic acid) and

Claim 17

3-diamino-2-propylene tetra-(methylene phosphonic acid).

Claim 18

3-diamino-2-propylene tetra-(methylene phosphonic acid).

Claim 19

The process as defined in claim 9, wherein said diphosphonic acid comprises 1-hydroxy ethylene-1,1-diphosphonic acid.

Claim 20

The process as defined in claim 11, wherein said alkali metal polyphosphate is sodium tripolyphosphate.