Methods of making reactive metal silicide
Assignee: Haynes International Inc
•
Filing: 1974-07-02
•
Granted: 1976-04-27
•
Expires: 1994-07-02
Abstract
Abstract A method is provided for making reactive metal silicide, particularly for use in adding lanthanum or other reactive metals to metal melts, by reacting reactive metal oxide with a metal silicide or silicon in an ESR furnace.
Inventors
- 👤 Robert B. Herchenroeder
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 04:05
CPC Classifications
C; C22; C22C; C22C29/00; C22C29/18; C01; C01B; C01B33/00; C01B33/06
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
72 words
A method of making lanthanum silicide comprising the steps of reducing a mixture of lanthanum oxide with at least a stoichiometric amount of metal silicide in which the metal has a stronger affinity for oxygen than silicon has in an electro-slag refining furnace having a cooled metal crucible using a non-consumable electrode having one end immersed in a molten oxide slag over said mixture and separating the resulting oxide slag and alloy.
Claim 2
Independent Claim
72 words
A method of making lanthanum silicide comprising the steps of reducing a mixture of lanthanum oxide with at least a stoichiometric amount of metal silicide in which the metal has a stronger affinity for oxygen than silicon has in an electro-slag refining furnace having a cooled metal crucible using a non-consumable electrode having one end immersed in a molten oxide slag over said mixture and separating the resulting oxide slag and alloy.
Claim 3
Dependent Claim
19 words
A method as claimed in claim 1 wherein a slag fluxing agent is added to the furnace during melting.
Claim 4
Dependent Claim
18 words
A method as claimed in claim 2 wherein the fluxing agent is fluorspar and the electrode is carbon.
Claim 5
Dependent Claim
24 words
A method as claimed in claim 1 wherein the metal silicide is a silicide selected from the group consisting of Ca, Al, and Zr.
Claim 6
Independent Claim
127 words
A method of making a lanthanum silicon master alloy comprising the steps of: a. feeding a mixture of lanthanum oxide and metal silicide in which the metal has a stronger affinity for oxygen than has silicon into a slag pool formed between a non consumable electrode having an end immersed in said pool and the base in a cooled metal container for a molten melt in the form of an electro-slag refining unit to form lanthanum-silicon alloy and slag, b. continuing to add said mixture of lanthanum oxide and metal silicide as the mixture melts in the container, c. raising the electrode as the molten bath rises in the container to permit lanthanum-silicon alloy to solidify beneath the slag and d. separating slag from the lanthanum-silicon alloy.
Claim 7
Independent Claim
127 words
A method of making a lanthanum silicon master alloy comprising the steps of: a. feeding a mixture of lanthanum oxide and metal silicide in which the metal has a stronger affinity for oxygen than has silicon into a slag pool formed between a non consumable electrode having an end immersed in said pool and the base in a cooled metal container for a molten melt in the form of an electro-slag refining unit to form lanthanum-silicon alloy and slag, b. continuing to add said mixture of lanthanum oxide and metal silicide as the mixture melts in the container, c. raising the electrode as the molten bath rises in the container to permit lanthanum-silicon alloy to solidify beneath the slag and d. separating slag from the lanthanum-silicon alloy.
Claim 8
Dependent Claim
19 words
A method as claimed in claim 5 wherein a slag fluidizing agent is added to the furnace during melting.
Claim 9
Dependent Claim
13 words
A method as claimed in claim 6 wherein the fluidizing agent is fluorspar.
Claim 10
Dependent Claim
12 words
A method as claimed in claim 5 wherein the electrode is carbon.
Claim 11
Dependent Claim
27 words
A method as claimed in claim 5 wherein the metal silicide is one selected from the group consisting of Ca, Al, and Zr silicides and mixtures thereof.
Claim 12
Independent Claim
73 words
A method of making rare earth metal silicides comprising the steps of reacting rare earth metal oxides with at least a stoichiometric amount of metal silicide in which the metal has a stronger affinity for oxygen than silicon has in an electro-slag refining furnace having a cooled metal crucible using a non consumable electrode having an end immersed in a molten slag over said mixture and separating the resulting oxide slag and alloy.
Claim 13
Independent Claim
73 words
A method of making rare earth metal silicides comprising the steps of reacting rare earth metal oxides with at least a stoichiometric amount of metal silicide in which the metal has a stronger affinity for oxygen than silicon has in an electro-slag refining furnace having a cooled metal crucible using a non consumable electrode having an end immersed in a molten slag over said mixture and separating the resulting oxide slag and alloy.
Claim 14
Dependent Claim
15 words
A method as claimed in claim 10 wherein the reactive metal oxide is yttrium oxide.
Claim 15
Dependent Claim
15 words
A method as claimed in claim 10 wherein the reactive metal oxide is cerium oxide.
References Cited (Backward Citations)
US3264093A
Cited
US3364015A
Cited
US3332741A
Cited
US3326637A
Cited
US3250609A
Cited
US3440040A
Cited
US3440041A
Cited
US3539334A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-04-27 | 1979-10-27 | 1980-04-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-04-27 | 1983-10-27 | 1984-04-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-04-27 | 1987-10-27 | 1988-04-27 | $7700.00 | Window Closed / Lapsed |