Assignee: Armstrong World Industries Inc
•
Filing: 1974-06-28
•
Granted: 1976-04-27
•
Expires: 1994-06-28
Abstract
Abstract A process for producing a decorative surface covering wherein granular dryblend is deposited on a releasable carrier and heated to form a porous cohesive layer. Settable resinous inks are then applied to selected surface portions of the dryblend to form design areas which may overlap at the points of application. The inked areas extend partially or completely through the layer so that they are visible from the bottom surface of the sheet which ultimately becomes the face of the surface covering, after final fusion of all of the resinous materials. The ink may optionally be set by heat prior to or simultaneously with the subsequent application and gelling of a resinous back coating, if one is used. The back coating may be reinforced by included or attached material to form a permanent carrier. Depending on the backing used, heat may be applied to fuse the composite structure before or after the release carrier is removed. Clearly defined, in-register, design areas are obtained which extend from the back of the wear layer up to or toward the wear surface of the sheet without the need for printing in register.
Inventors
- 👤 Elvin M. Weidman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 22:34
CPC Classifications
D; D06; D06N; D06N7/00; D06N7/0005; D06N7/0028; D06N7/0034; B; B44; B44C; B44C1/00; B44C1/04
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
264 words
A process for producing a thermoplastic resinous decorative surface covering, comprising: a. depositing a layer of unfused thermoplastic granules of a resinous dryblend onto a releasable substrate, b. heating said layer to cause partial melting of at least surface portions of the granules at their points of contact, c. cooling and thereby bonding adjacent granules to form a cohesive, porous layer having an upper and a lower surface, d. applying in a design to the upper surface of said layer, an amount of a first colored settable resinous ink having a viscosity sufficient to at least partially penetrate said porous layer, e. applying at least one additional settable resinous ink to the upper surface of said porous layer to cover at least portions of the design formed by the first applied ink, and also at least portions of the upper surface of the porous layer not covered by the first applied ink, said additional ink having a different color than that of said first ink, said inks being applied to penetrate into said porous layer in sufficient amounts so that the ink design is visible from the lower surface thereof after final fusion of all resinous material in said layer, f. heating said layer for final fusion of all resinous material in the ink-containing porous layer to form a non-porous sheet, g. cooling said fused sheet, and h. removing said substrate whereby there is formed a surface covering having a clearly defined in-register, multi-colored, decorative design visible from said lower surface of said sheet, which in use becomes the upper surface of said covering.
Claim 2
Dependent Claim
264 words
A process for producing a thermoplastic resinous decorative surface covering, comprising: a. depositing a layer of unfused thermoplastic granules of a resinous dryblend onto a releasable substrate, b. heating said layer to cause partial melting of at least surface portions of the granules at their points of contact, c. cooling and thereby bonding adjacent granules to form a cohesive, porous layer having an upper and a lower surface, d. applying in a design to the upper surface of said layer, an amount of a first colored settable resinous ink having a viscosity sufficient to at least partially penetrate said porous layer, e. applying at least one additional settable resinous ink to the upper surface of said porous layer to cover at least portions of the design formed by the first applied ink, and also at least portions of the upper surface of the porous layer not covered by the first applied ink, said additional ink having a different color than that of said first ink, said inks being applied to penetrate into said porous layer in sufficient amounts so that the ink design is visible from the lower surface thereof after final fusion of all resinous material in said layer, f. heating said layer for final fusion of all resinous material in the ink-containing porous layer to form a non-porous sheet, g. cooling said fused sheet, and h. removing said substrate whereby there is formed a surface covering having a clearly defined in-register, multi-colored, decorative design visible from said lower surface of said sheet, which in use becomes the upper surface of said covering.
Claim 3
Dependent Claim
63 words
The process accordng to claim 1 wherein the dryblend is transparent after final fusion and wherein the additional settable resinous ink is applied in amounts and viscosities sufficient to result in penetration thereof through the porous layer to degrees different from the degree of penetration of said first-applied settable resinous ink, whereby an in-register, multi-color, multi-level design is achieved in the surface covering.
Claim 4
Dependent Claim
38 words
The process according to claim 1 wherein at least one of said settable resinous inks is applied in an amount and viscosities sufficient to result in penetration thereof through substantially the entire thickness of the porous dryblend layer.
Claim 5
Dependent Claim
89 words
The process according to claim 1 wherein the additional settable resinous ink comprises a plurality of differently colored inks applied in side-by-side overlapping relationship with each other and with said first-applied ink, all of said inks being applied onto the porous dryblend layer in amounts and viscosities sufficient to result in penetration through substantially the entire thickness of the layer, whereby a multi-colored, clearly defined design is achieved with no overlapping of the differently colored inks in the design being visible from the upper surface of the surface covering.
Claim 6
Dependent Claim
17 words
The process according to claim 1 wherein the granules of the resinous dryblend have an adhesive coating.
Claim 7
Dependent Claim
74 words
The process according to claim 1 wherein the resin in the dryblend granules is vinyl resin, the layer of unfused resinous granules has a thickness in the range of from about 25 mils to 100 mils, and wherein the dryblend layer is formed into a cohesive porous layer having a thickness in the range of about 20 mils to 85 mils by heating to a temperature in the range of about 270°F. to 290°F.
Claim 8
Dependent Claim
16 words
The process according to claim 6 wherein the resin in the dryblend granules is poly(vinyl chloride).
References Cited (Backward Citations)
GB658530A
Cited
US3359352A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-04-27 | 1979-10-27 | 1980-04-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-04-27 | 1983-10-27 | 1984-04-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-04-27 | 1987-10-27 | 1988-04-27 | $7700.00 | Window Closed / Lapsed |