Powdery composition for heat retention of feeder head
Assignee: Aikoh Co Ltd
•
Filing: 1974-09-20
•
Granted: 1976-04-27
•
Expires: 1994-09-20
Abstract
Abstract A powdery composition for heat retention of feeder head comprising carbonized plant (i.e., baked vegetable material) containing a large amount of fibrous matter and at least one substance selected from refractory material, easily oxidizable metal, metal oxide and inorganic material effective for heat retention of feeder head, each of said substances having a particle size distribution of less than 50% in parts by weight of 48 to 200 mesh particles with the remainder being particles larger than 48 mesh and smaller than 200 mesh and the amount of said substance having a particle size of larger than 48 mesh being approximately equal to that of said substance having a particle size of smaller than 200 mesh.
Inventors
- 👤 Masaru Takashima
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 11:25
CPC Classifications
B; B22; B22D; B22D27/00; B22D27/04; B22D27/06; C; C09; C09K; C09K5/00; C09K5/16
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
129 words
In a powdery composition for heat retention of feeder head which comprises from about 5 to about 25% by weight of a carbonized plant material and from about 75 to about 95% by weight of a mixture including at least one refractory material, at least one easily oxidizable metal, at least one metal oxide and at least one inorganic material effective for heat retention of feeder head; the improvement comprising each of the ingredients in said mixture having a particle size distribution, by the Tyler Standard Sieve System, of less than 50% by weight of 48 to 200 mesh particles, with the remainder being coarser than 48 mesh particles plus finer than 200 mesh particles which are present in a ratio of coarser to finer particles of approximately 1:1.
Claim 2
Dependent Claim
129 words
In a powdery composition for heat retention of feeder head which comprises from about 5 to about 25% by weight of a carbonized plant material and from about 75 to about 95% by weight of a mixture including at least one refractory material, at least one easily oxidizable metal, at least one metal oxide and at least one inorganic material effective for heat retention of feeder head; the improvement comprising each of the ingredients in said mixture having a particle size distribution, by the Tyler Standard Sieve System, of less than 50% by weight of 48 to 200 mesh particles, with the remainder being coarser than 48 mesh particles plus finer than 200 mesh particles which are present in a ratio of coarser to finer particles of approximately 1:1.
Claim 3
Dependent Claim
33 words
A powdery composition for heat retention of feeder head as claimed in claim 1 wherein the carbonized plant is selected from the group consisting of carbonized chaff, straw, vegetable shell and mixtures thereof.
Claim 4
Dependent Claim
38 words
A powdery composition for heat retention of feeder head as claimed in claim 1 wherein the refractory material is selected from the group consisting of aluminum residual ash, quartz, sand, fire clay, vermiculite, diatomaceous earth and mixtures thereof.
Claim 5
Dependent Claim
35 words
A powdery composition for heat retention of feeder head as claimed in claim 1 wherein the easily oxidizable metal is selected from the group consisting of metallic aluminum, aluminum alloy, calcium-silicon alloy and mixtures thereof.
Claim 6
Dependent Claim
36 words
A powdery composition for heat retention of feeder head as claimed in claim 1 wherein the metal oxide is selected from the group consisting of ferrous oxide, ferric oxide, triiron tetroxide, manganese dioxide and mixtures thereof.
Claim 7
Dependent Claim
37 words
A powdery composition for heat retention of feeder head as claimed in claim 1 wherein the inorganic material is selected from the group consisting of metallic fluorides, alkali metal nitrates, alkaline earth metal nitrates and mixtures thereof.
Claim 8
Dependent Claim
138 words
In the method for the heat retention of feeder head comprising applying to the surface of molten metal while in a mold a composition including from about 5 to about 25% by weight of a carbonized plant and from about 75 to about 95% of a mixture including at least one refractory material, at least one easily oxidizable metal, at least one metal oxide and at least one inorganic material effective for heat retention of feeder head; the improvement comprising providing a particle size distribution of each component of said mixture, by the Tyler Standard Sieve System, of less than 50% by weight of 48 to 200 mesh particles with the remainder being coarser than 48 mesh particles plus finer than 200 mesh particles which are present in a ratio of coarser to finer particles of approximately 1:1.
Claim 9
Dependent Claim
138 words
In the method for the heat retention of feeder head comprising applying to the surface of molten metal while in a mold a composition including from about 5 to about 25% by weight of a carbonized plant and from about 75 to about 95% of a mixture including at least one refractory material, at least one easily oxidizable metal, at least one metal oxide and at least one inorganic material effective for heat retention of feeder head; the improvement comprising providing a particle size distribution of each component of said mixture, by the Tyler Standard Sieve System, of less than 50% by weight of 48 to 200 mesh particles with the remainder being coarser than 48 mesh particles plus finer than 200 mesh particles which are present in a ratio of coarser to finer particles of approximately 1:1.
Claim 10
Dependent Claim
24 words
The method of claim 7 wherein the carbonized plant is selected from the group consisting of carbonized chaff, straw, vegetable shell and mixtures thereof.
Claim 11
Dependent Claim
29 words
The method of claim 7 wherein the refractory material is selected from the group consisting of aluminum, residual ash, quartz, sand, fire clay, vermiculite, diatomaceous earth and mixtures thereof.
Claim 12
Dependent Claim
26 words
The method of claim 7 wherein the easily oxidizable metal is selected from the group consisting of metallic aluminum, aluminum alloy, calcium-silicon alloy and mixtures thereof.
Claim 13
Dependent Claim
28 words
The method of claim 7 wherein the metal oxide is selected from the group consisting of ferrous oxide, ferric oxide, tri-iron tetroxide and manganese dioxide and mixtures thereof.
Claim 14
Dependent Claim
29 words
The method of claim 7 wherein the inorganic material is selected from the group consisting of metallic fluorides, alkali metal nitrates and alkaline earth metal nitrates and mixtures thereof.
References Cited (Backward Citations)
US2798818A
Cited
US3082104A
Cited
US3162558A
Cited
US3612155A
Cited
US3713852A
Cited
US3848655A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-04-27 | 1979-10-27 | 1980-04-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-04-27 | 1983-10-27 | 1984-04-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-04-27 | 1987-10-27 | 1988-04-27 | $7700.00 | Window Closed / Lapsed |