Assignee: Nichias Corp
•
Filing: 1975-07-10
•
Granted: 1976-04-27
•
Expires: 1995-07-10
Abstract
Abstract This invention pertains to a method of making inorganic vitreous fibers having small protrusions, such that the fiber produces a high strength reinforced molded product. The fibers are formed by introducing high melting constituents such as glass fiber, rock wool, ceramic fiber, silica particles, alumina particles, zirconia particles or mullite particles to molten inorganic material such that the constituents when flung from a ratary device are incorporated into the molten inorganic material.
Inventors
- 👤 Susumu Aoki
- 👤 Toshiaki Minaki
- 👤 Kentaro Mori
- 👤 Kenichi Shibata
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 15:32
CPC Classifications
C; C03; C03C; C03C13/00; C03B; C03B37/00; C03B37/01; C03B37/02; C03B37/022; C03B37/04; C03B37/05; C03B37/06; C03C13/06; C04; C04B; C04B14/00; C04B14/38; C04B14/42; E; E04; E04C; E04C5/00; E04C5/07; E04C5/073; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2927; Y10T428/2973; Y10T428/2976
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
121 words
A process for making a length of inorganic vitreous fiber for use as a reinforcing element in the matrix of cementituous mixtures wherein said fiber is comprised of a body of a single vitreous fiber and at least one small protrusion formed integrally with said fiber body on the surface thereof comprising simultaneously but separately feeding molten inorganic material to form the body of the vitreous fiber and heat corrosion reistance mineral particles onto a high speed rotating rotor whereby the mineral particles are incorporated into the molten inorganic material and thereafter the incorporated molten inorganic material is released outwardly from the rotor due to the rotating centrifugal force, thereby fibrilating the molten material into a plurality of the vitreous fibers.
Claim 2
Dependent Claim
121 words
A process for making a length of inorganic vitreous fiber for use as a reinforcing element in the matrix of cementituous mixtures wherein said fiber is comprised of a body of a single vitreous fiber and at least one small protrusion formed integrally with said fiber body on the surface thereof comprising simultaneously but separately feeding molten inorganic material to form the body of the vitreous fiber and heat corrosion reistance mineral particles onto a high speed rotating rotor whereby the mineral particles are incorporated into the molten inorganic material and thereafter the incorporated molten inorganic material is released outwardly from the rotor due to the rotating centrifugal force, thereby fibrilating the molten material into a plurality of the vitreous fibers.
Claim 3
Dependent Claim
12 words
The process of claim 1 wherein the rotor is a rotor disc.
Claim 4
Dependent Claim
52 words
The process of claim 2 wherein the mineral particles are fed through a tube or tubes provided around an axis of the rotor onto the rotor disc while the molten inorganic material is fed from outward of the tube or tubes whereby the both materials are mixed together on the rotor disc.
Claim 5
Dependent Claim
42 words
The process of claim 1 wherein at the moment when the incorporated molten inorganic material is released outwardly from the motor, steam or compressed air is blown through the material to thereby fibrilate the molten material into a plurality of vitreous fibers.
Claim 6
Dependent Claim
23 words
The process of claim 1 wherein the inorganic material is selected from the group consisting of glass fiber, rock wool and ceramic fiber.
Claim 7
Dependent Claim
24 words
The process of claim 1 wherein the heat corrosion resistance material particles are slected from the group consisting of silica, alumina, zirconia and mullite.
Claim 8
Dependent Claim
14 words
The process of claim 1 wherein the heat corrosion resistance mineral particles are pre-heated.
References Cited (Backward Citations)
US2150945A
Cited
US2215150A
Cited
US2612679A
Cited
US3377233A
Cited
US3830638A
Cited
US3684474A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-04-27 | 1979-10-27 | 1980-04-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-04-27 | 1983-10-27 | 1984-04-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-04-27 | 1987-10-27 | 1988-04-27 | $7700.00 | Window Closed / Lapsed |