Method for embossing plastic material
Assignee: Tredegar Corp
•
Filing: 1975-05-07
•
Granted: 1976-04-13
•
Expires: 1995-05-07
Abstract
Abstract A method for embossing thermoplastic material and the thermoplastic material produced thereby. A transverse section of a continuous length of preformed thermoplastic film is heated by a nondirect contact heat source to raise the temperature of the film above its softening point. The film is then fed immediately between adjacent, counter-rotating embossing rollers, thereby embossing a raised pattern onto the film. The rollers are cooled to fix the embossed pattern on the film. The embossed film has good moduli, low surface gloss or light reflectance, deep embossed pattern, high tensile strength and high impact strength.
Inventors
- 👤 James M. Adams
- 👤 Randall R. Hopper
- 👤 Robert R. Pease
- 👤 Garland E. Raley
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 22:05
CPC Classifications
B; B29; B29C; B29C59/00; B29C59/02; B29C59/04; B29K; B29K2995/00; B29K2995/0018; B29K2995/0024; B29K2995/0037; B29K2995/0077; B29L; B29L2007/00; B29L2007/001; B29L2031/00; B29L2031/48; B29L2031/4871; B29L2031/4878; B29L2031/712; B29L2031/7128
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
211 words
In a method for embossing a thermoplastic film prepared from a crystalline or semi-crystalline polymer or copolymer, the steps comprising: a. continuously passing a vertically extending length of said film through a narrow, transverse heating zone extending the full width of said film; b. applying a high velocity stream of air heated to a temperature of from about 200°F to about 800°F to each side of said film over opposite areas defined by said heating zone to raise the temperature of the film as it leaves said heating zone to a uniform temperature within the range of about ±20°F of the crystalline melting point of the polymer or copolymer; and c. simultaneously quenching and embossing said heated film at one end of said heating zone by passing said heated film between the nip of a pair of embossing rolls, one of said rolls being an engraved metal roll having its surface temperature maintained in a range of from about 70°F to about 170°F lower than the crystalline melting temperature of the polymer or copolymer, and the other of said rolls being a resilient covered roll having its surface temperature maintained in the range of from about 125°F to about 180°F lower than the crystalline melting temperature of the polymer or copolymer.
Claim 2
Dependent Claim
211 words
In a method for embossing a thermoplastic film prepared from a crystalline or semi-crystalline polymer or copolymer, the steps comprising: a. continuously passing a vertically extending length of said film through a narrow, transverse heating zone extending the full width of said film; b. applying a high velocity stream of air heated to a temperature of from about 200°F to about 800°F to each side of said film over opposite areas defined by said heating zone to raise the temperature of the film as it leaves said heating zone to a uniform temperature within the range of about ±20°F of the crystalline melting point of the polymer or copolymer; and c. simultaneously quenching and embossing said heated film at one end of said heating zone by passing said heated film between the nip of a pair of embossing rolls, one of said rolls being an engraved metal roll having its surface temperature maintained in a range of from about 70°F to about 170°F lower than the crystalline melting temperature of the polymer or copolymer, and the other of said rolls being a resilient covered roll having its surface temperature maintained in the range of from about 125°F to about 180°F lower than the crystalline melting temperature of the polymer or copolymer.
Claim 3
Dependent Claim
26 words
The method of claim 1 wherein the polymer or copolymer is a polymer or copolymer of an alpha-olefinic hydrocarbon having from two to four carbon atoms.
Claim 4
Dependent Claim
20 words
The method of claim 1 wherein the crystalline or semi-crystalline polymer or copolymer is a polymer or copolymer of ethylene.
Claim 5
Dependent Claim
158 words
In a method for embossing a thermoplastic film prepared from a polymer or copolymer of an alpha-olefinic hydrocarbon having from two to four carbon atoms, the steps comprising: a. continuously passing a vertically extending length of said film through a narrow, transverse heating zone extending the full width of said film; b. applying a high velocity stream of air heated to a temperature of from about 200°F to about 800°F to each side of said film over opposite areas defined by said heating zone to raise the temperature of the film as it leaves said heating zone to a uniform temperature in the range of from about 220°F to about 250°F; and c. simultaneously quenching and embossing said heated film at one end of said heating zone by passing said heated film between the nip of a pair of embossing rolls having their surfaces maintained at a temperature in the range of from about 60°F to about 170°F.
Claim 6
Dependent Claim
158 words
In a method for embossing a thermoplastic film prepared from a polymer or copolymer of an alpha-olefinic hydrocarbon having from two to four carbon atoms, the steps comprising: a. continuously passing a vertically extending length of said film through a narrow, transverse heating zone extending the full width of said film; b. applying a high velocity stream of air heated to a temperature of from about 200°F to about 800°F to each side of said film over opposite areas defined by said heating zone to raise the temperature of the film as it leaves said heating zone to a uniform temperature in the range of from about 220°F to about 250°F; and c. simultaneously quenching and embossing said heated film at one end of said heating zone by passing said heated film between the nip of a pair of embossing rolls having their surfaces maintained at a temperature in the range of from about 60°F to about 170°F.
Claim 7
Dependent Claim
52 words
The method of claim 4 wherein said pair of embossing rolls includes an engraved metal roll having its surface maintained at a temperature in the range of from about 70°F to about 170°F and a resilient covered roll maintained at a temperature in the range of from about 60°F to about 115°F.
Claim 8
Dependent Claim
47 words
The method of claim 5 including the steps of supplying a cooling liquid having a temperature of from about 20°F to about 150°F to said metal roll and supplying a cooling liquid having a temperature of from about 5°F to about 100°F to said resilient covered roll.
Claim 9
Dependent Claim
21 words
The method of claim 4 wherein said heating zone has a height of from about 6 inches to about 14 inches.
Claim 10
Dependent Claim
17 words
The method of claim 4 wherein the polymer or copolymer is a polymer or copolymer of ethylene.
References Cited (Backward Citations)
US2567275A
Cited
GB719964A
Cited
US2928124A
Cited
US3170974A
Cited
US3311692A
Cited
US3540959A
Cited
US3283378A
Cited
US3502765A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-04-13 | 1979-10-13 | 1980-04-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-04-13 | 1983-10-13 | 1984-04-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-04-13 | 1987-10-13 | 1988-04-13 | $7700.00 | Window Closed / Lapsed |