Concrete pipes
Assignee: Hanson Quarry Products Europe Ltd
•
Filing: 1973-06-14
•
Granted: 1976-04-13
•
Expires: 1993-06-14
Abstract
Abstract A pipe of concrete, cement mortar or other cementitious material is formed by an integrally cast cementitious mass which is reinforced with a glass fibre strand or roving forming a substantially helical winding extending around the pipe and incorporated in the cement matrix of the cementitious mass. Preferably there are two windings, one incorporated in the outer periphery of the mass and the other incorporated in the inner periphery of the mass. The pipe is preferably made by a centrifugal casting operation in which a centrifugal casting mould is rotated and the glass fibre strand or roving is fed from a feeding device within the mould and is caused to adhere to the internal peripheral face of the mould and then the feeding device is moved axially along the mould as the mould rotates so that the winding is formed from the roving around the internal peripheral face of the mould. The concrete or other cementitious material is introduced into the mould at the same time as the glass fibre roving or subsequently and the winding becomes incorporated in the cement matrix of the cementitious material as the mould continues to be rotated.
Inventors
- 👤 Robert M. Farahar
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 17:57
CPC Classifications
B; B28; B28B; B28B21/00; B28B21/56; B28B21/60; B28B21/62; F; F16; F16L; F16L9/00; F16L9/08
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
201 words
A method of making a tubular structure comprising a body formed by an integrally cast mass of cementitious material including a Portland or aluminous cement which forms a cement matrix, and a glass fibre roving consisting essentially of a plurality of glass monofilaments, which are resistant to deterioration by said cementitious material incorporated in said cement matrix, said method including the steps of providing a centrifugal casting mould having an internal peripheral surface, rotating said mould to move said peripheral surface at a speed sufficient to produce a centrifugal effect, positively feeding said glass fibre roving from a feeding device within said mould at a speed at least as great as the speed of movement of said peripheral surface, projecting said roving from said feeding device onto said mould to rotate therewith, moving said feeding device axially of said mould as said mould is rotated whereby said winding is formed on said peripheral surface, introducing said cementitious material including a suspension of cement particles in water forming said cement matrix into said mould, and continuing to rotate said mould to compact said cementitious material and cause said roving to be impregnated with and incorporated into and bonded to said cement matrix.
Claim 2
Independent Claim
201 words
A method of making a tubular structure comprising a body formed by an integrally cast mass of cementitious material including a Portland or aluminous cement which forms a cement matrix, and a glass fibre roving consisting essentially of a plurality of glass monofilaments, which are resistant to deterioration by said cementitious material incorporated in said cement matrix, said method including the steps of providing a centrifugal casting mould having an internal peripheral surface, rotating said mould to move said peripheral surface at a speed sufficient to produce a centrifugal effect, positively feeding said glass fibre roving from a feeding device within said mould at a speed at least as great as the speed of movement of said peripheral surface, projecting said roving from said feeding device onto said mould to rotate therewith, moving said feeding device axially of said mould as said mould is rotated whereby said winding is formed on said peripheral surface, introducing said cementitious material including a suspension of cement particles in water forming said cement matrix into said mould, and continuing to rotate said mould to compact said cementitious material and cause said roving to be impregnated with and incorporated into and bonded to said cement matrix.
Claim 3
Dependent Claim
103 words
A method as claimed in claim 1, further comprising the steps of introducing concrete including a cement matrix into said mould to form a further part of said cementitious mass and, after introducing said concrete, feeding a second glass fibre roving from said feeding device onto the internal surface of said concrete and moving said feeding device axially along said mould while still continuing to rotate said mould to form a second winding extending around an internal peripheral face of said concrete and continuing further to rotate said mould to incorporate and bond said second winding in said cement matrix of said concrete.
Claim 4
Dependent Claim
43 words
A method as claimed in claim 1, wherein said roving is fed from said feeding device at a speed greater than the peripheral speed of said internal face of said mould whereby said roving is laid along an undulating path in said winding.
Claim 5
Dependent Claim
131 words
A method as claimed in claim 1, wherein further comprising the steps of allowing said cement slurry with said winding incorporated therein to harden in said mould to form a reinforced cylindrical shell, removing said shell from said mould, introducing said shell into a vertical pipe casting mould whereby said shell forms an outer peripheral face of said vertical pipe casting mould, providing an internal peripheral face of said vertical pipe casting mould and introducing concrete between said shell and said internal peripheral face of said vertical pipe casting mould, consolidating said concrete to form a concrete pipe, allowing said concrete to harden and removing said concrete and said shell from said vertical pipe casting mould to form a concrete pipe reinforced with said glass fibre roving winding in said shell.
Claim 6
Dependent Claim
153 words
A method as claimed in claim 1, wherein further comprising the steps of allowing said cement slurry to harden with said winding incorporated therein to form a first shell, removing said shell from said centrifugal mould, replacing said centrifugal mould by a further centrifugal mould of smaller diameter, forming a second shell in said further mould, removing said second shell from said further mould, introducing both of said shells into a vertical casting mould, said first shell forming an outer peripheral wall of said vertical pipe casting mould and said second shell forming an inner peripheral wall of said vertical pipe casting mould, introducing concrete into said vertical pipe casting mould between said shells, consolidating said concrete to form a concrete pipe, allowing said concrete to harden and removing said concrete and said shells from said vertical pipe casting mould whereby said concrete forms a pipe reinforced by said windings in said shells.
Claim 7
Dependent Claim
17 words
A method as claimed in claim 1 in which said roving comprises about six thousand continuous filaments.
Claim 8
Independent Claim
235 words
A method of making a tubular structure comprising a body formed by an integrally cast mass of cementitious material including a Portland or aluminous cement matrix, and a glass fibre roving consisting essentially of a plurality of glass monofilaments, which are resistant to deterioration by said cementitious material incorporated in said cement matrix, said method including the steps of providing a centrifugal casting mould having an internal peripheral surface, rotating said mould to move said peripheral surface at a speed sufficient to produce a centrifugal effect, providing a feeding device in said mould, positively feeding said glass fibre roving up to and through said feeding device, supplying cementitious material and water to said feeding device, projecting said cementitious material and water in at least one inwardly directed stream onto said roving passing through said feeding device to impregnate said roving with cement slurry, discharging said slurry impregnated roving from said feeding device at a speed at least as great as said speed of movement of said peripheral surface, projecting said slurry impregnated roving in a stream of slurry onto said mould to rotate therewith, and moving said feeding device axially of said mould as said mould rotates whereby said winding is formed on said peripheral surface and said stream of slurry builds up at least part of said body of cementitious material in said mould, and continuing to rotate said mould to compact said body.
Claim 9
Independent Claim
235 words
A method of making a tubular structure comprising a body formed by an integrally cast mass of cementitious material including a Portland or aluminous cement matrix, and a glass fibre roving consisting essentially of a plurality of glass monofilaments, which are resistant to deterioration by said cementitious material incorporated in said cement matrix, said method including the steps of providing a centrifugal casting mould having an internal peripheral surface, rotating said mould to move said peripheral surface at a speed sufficient to produce a centrifugal effect, providing a feeding device in said mould, positively feeding said glass fibre roving up to and through said feeding device, supplying cementitious material and water to said feeding device, projecting said cementitious material and water in at least one inwardly directed stream onto said roving passing through said feeding device to impregnate said roving with cement slurry, discharging said slurry impregnated roving from said feeding device at a speed at least as great as said speed of movement of said peripheral surface, projecting said slurry impregnated roving in a stream of slurry onto said mould to rotate therewith, and moving said feeding device axially of said mould as said mould rotates whereby said winding is formed on said peripheral surface and said stream of slurry builds up at least part of said body of cementitious material in said mould, and continuing to rotate said mould to compact said body.
References Cited (Backward Citations)
US2191025A
Cited
US2585446A
Cited
US3340115A
Cited
US3150219A
Cited
US3491171A
Cited
US3768943A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-04-13 | 1979-10-13 | 1980-04-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-04-13 | 1983-10-13 | 1984-04-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-04-13 | 1987-10-13 | 1988-04-13 | $7700.00 | Window Closed / Lapsed |