Light stabilized polyester resin composition
Assignee: General Electric Co
•
Filing: 1974-08-01
•
Granted: 1976-04-13
•
Expires: 1994-08-01
Abstract
Abstract Ultraviolet light stable polyester resin compositions are provided by this invention. These compositions include as the stabilizer system, a stabilizing amount of a hydroxybenzotriazole ultraviolet light absorber.
Inventors
- 👤 Karl J. Balog
- 👤 Donald I. Craft
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 08:34
CPC Classifications
C; C08; C08K; C08K5/00; C08K5/16; C08K5/34; C08K5/3467; C08K5/3472; C08K5/3475; C08K3/00; C08K3/01; C08K3/013; C08K3/02; C08K3/18; C08K3/20; C08K3/22; C08K5/49; C08K7/00; C08K7/02; C08K7/04; C08L; C08L67/00; C08L67/02; C08L69/00; C08L67/04; Y; Y10; Y10S; Y10S260/00; Y10S260/24
Claims Analysis
Total Claims: 38
Claim 1
Independent Claim
108 words
A stabilized polyester composition consisting essentially of a. a high molecular weight polyester resin; b. a flame retardant additive in minor proportion but in an amount at least sufficient to render the polyester resin non-burning or self-estinguishing. c. a stabilizing amount of a hydroxybenzotrianzole selected from compounds of the formula: ##EQU5## wherein A represents an o-phenylene radical bound by two neighboring carbon atoms to two nitrogen atoms of the triazole ring, and B represents a phenyl radical which contains in the 2-position an OH group and in further positions a member selected from the group consisting of H, lower alkyl, lower alkoxy, lower carbalkoxy, cyclohexyl, phenyl and halogen.
Claim 2
Dependent Claim
108 words
A stabilized polyester composition consisting essentially of a. a high molecular weight polyester resin; b. a flame retardant additive in minor proportion but in an amount at least sufficient to render the polyester resin non-burning or self-estinguishing. c. a stabilizing amount of a hydroxybenzotrianzole selected from compounds of the formula: ##EQU5## wherein A represents an o-phenylene radical bound by two neighboring carbon atoms to two nitrogen atoms of the triazole ring, and B represents a phenyl radical which contains in the 2-position an OH group and in further positions a member selected from the group consisting of H, lower alkyl, lower alkoxy, lower carbalkoxy, cyclohexyl, phenyl and halogen.
Claim 3
Dependent Claim
24 words
The composition as defined in claim 1 wherein the polyester resin includes repeating units of the formula: ##SPC6## wherein n is 2 to 6.
Claim 4
Dependent Claim
13 words
The composition as defined in claim 2 wherein said polyester is poly(ethylene terephthalate).
Claim 5
Dependent Claim
13 words
The composition as defined in claim 2 wherein said polyester is poly(1,4-butylene terephathalate).
Claim 6
Dependent Claim
27 words
The composition as defined in claim 1 wherein the polyester resin is a combination of a poly(ethylene terephthalate) resin and a poly(butylene terephthalate) resin or copolyesters thereof.
Claim 7
Dependent Claim
64 words
The composition as defined in claim 5 wherein the polyester resin combination comprises: a. from about 1 to about 99 parts by weight of a poly(ethylene terephthalate) resin and b. from about 99 to about 1 part by weight of a poly(1,4-butylene terephthalate) resin or a copolyesteer thereof formed with a minor amount of an aliphatic or aromatic dicarboxylic acid or an aliphatic polyol.
Claim 8
Dependent Claim
47 words
The composition as defined in claim 1 wherein the polyester resin is a combination of a poly(1,4-butylene terephthalate) resin or a copolyester thereof and a linear aliphatic polyester resin; said copolyester formed with a minor amount of an aliphatic or aromatic dicarboxylic acid or an sliphatic polyol.
Claim 9
Dependent Claim
61 words
The composition as defined in claim 7 wherein the polyester combinarion comprises: a. from about 99 to about 60 parts by weight of a poly(1,4-butylene terephthalate) resin or a copolyester thereof with a minor amount of an aliphatic or aromatic dicarboxylic acid or aliphatic polyol and b. from about 1 to about 40 parts by weight of alinear aliphatic polyester resin.
Claim 10
Dependent Claim
15 words
The composition as defined in claim 8 wherein component (a) is a poly(1,4-butylene terephthalate) resin.
Claim 11
Dependent Claim
31 words
The composition as defined in claim 8 wherein the linear aliphatic polyester resin component (b) is poly(betapropiolactone), poly (gammabutyrolactone), poly(deltavalerolactone), poly(epsiloncaprolactone) or a mixture of at least two of the foregoing.
Claim 12
Dependent Claim
28 words
The composition as defined in claim 1 wherein the polyester resin contains units providing branching sites and is derived from compounds containing at least three ester forming groups.
Claim 13
Dependent Claim
15 words
The composition as defined in cliam 1 wherein the hydroxybenzotriazole is 2-(2'-hydroxy-3', 5'-di-tert-amyl phenyl) benzotriazole.
Claim 14
Dependent Claim
15 words
The composition as defined in cliam 1 wherein the hydroxybenzotriazole is 2-(2'-hydroxy-3', 5'-di-tert-amyl phenyl) benzotriazole.
Claim 15
Dependent Claim
70 words
A composition as defined in claim 1 wherein the flame retardant additive is a halogen-containing compound; a halogen-containing compound is admixture with antimony oxide; elemental phosphorus or a phosphorus compound; a halogen-containing compound in admixture with a phosphorus compound; a compound containing phosphorus-nitrogen bonds; or a mixture of the foregoing, and said compound is present in an amount of from 0.5 to 50 parts by weight per hundred parts resin.
Claim 16
Dependent Claim
40 words
A composition as defined in claim 1 wherein said flame retardant additive is selected from the group consisting of elemental phosphorus; organic phosphonic acids, phosphonates, phosphinates, phosphonites, phosphinites, phosphine oxides, phosphines, phosphites, phosphates and mixtures of any of the foregoing.
Claim 17
Dependent Claim
107 words
A flame retardant composition as defined in claim 1 wherein said flame retardant additive is either a. a low molecular weight polymer of a carbonate of a halogenated dihydric phenol, said polymer containing from 2 to 10 repeating units of the formula ##SPC7## wherein R 1 and R 2 are hydrogen, (lower) alkyl or phenyl, X 1 and X 2 are bromo or chloro and m and r are from 1 to 4, said polymer having low volatility when heated above about 200°C., and a softening point of less than about 300°C. or b. a combination of said polymer (a) and an inorganic or organic antimony-containing compound.
Claim 18
Dependent Claim
50 words
A flame retardant composition as defined in claim 15 wherein said low molecular weight polymer (a) is of the formula ##SPC8## wherein the average number of repeating units, n, is from about 3 to 7, and the softening point of said polymer is in the range of from 200°to 260°C.
Claim 19
Dependent Claim
50 words
A flame retardant composition as defined in claim 1 wherein said flame retardant additive is either a. a carbonate polymer which is the reaction product of a halogen substituted dihydric phenol and a dihydric phenol or b. a combination of said polymer (a) and an inorganic or organic antimony-containing compound.
Claim 20
Dependent Claim
23 words
A flame retardant composition as defined in claim 17 wherein said carbonate polymer is the reaction product of a halogenated bisphenol-A and bisphenol-A.
Claim 21
Dependent Claim
17 words
The composition as defined in claim 1 which also includes a reinforcing amount of a reinforcing filler.
Claim 22
Dependent Claim
26 words
A composition as defined in claim 19 wherein said reinforcing filler is selected from the group consisting of reinforcing metals, ceramics, silicas, quartz, glass and carbons.
Claim 23
Dependent Claim
27 words
A composition as defined in claim 20 wherein said reinforcing filler if filamentous glass, in an amount of from about 1 to about 50 percent by weight.
Claim 24
Dependent Claim
94 words
A stabilized polyester composition consisting essentially of a. a high molecular weight polyester resin; b. a reinforcing amount of a reinforcing filler; and c. a stabilizing amount of a hydroxybenzotriazole selected from compounds of the formula: ##EQU6## wherein A represents an o-phenylene radical bound by two neighboring carbon atoms to two nitrogen atoms of the triazole ring, and B represents a phenyl radical which contains in the 2-position an OH group and in further position a member selected from the group consisting of H, lower alkyl, lower alkoxy, lower carbalkoxy, cyclohexyl, phenyl and halogen.
Claim 25
Dependent Claim
94 words
A stabilized polyester composition consisting essentially of a. a high molecular weight polyester resin; b. a reinforcing amount of a reinforcing filler; and c. a stabilizing amount of a hydroxybenzotriazole selected from compounds of the formula: ##EQU6## wherein A represents an o-phenylene radical bound by two neighboring carbon atoms to two nitrogen atoms of the triazole ring, and B represents a phenyl radical which contains in the 2-position an OH group and in further position a member selected from the group consisting of H, lower alkyl, lower alkoxy, lower carbalkoxy, cyclohexyl, phenyl and halogen.
Claim 26
Dependent Claim
24 words
The composition as defined in claim 22 wherein the polyester resin includes repeating units of the formula: ##SPC9## wherein n is 2 to 6.
Claim 27
Dependent Claim
13 words
The composition as defined in claim 22 wherein said polyester is poly(ethylene terephthalate).
Claim 28
Dependent Claim
13 words
The composition as defined in claim 22 wherein said polyester is poly(1,4-butylene terephthalate).
Claim 29
Dependent Claim
27 words
The composition as defined in claim 22 wherein the polyester resin is a combination of a poly(ethylene terephthalate) resin and a poly(butylene terephthalate) resin or copolyesters thereof.
Claim 30
Dependent Claim
64 words
The composition as defined in claim 26 wherein the polyester resin combination comprises: a. from about 1 to about 99 parts by weight of a poly(ethylene terephthalate) resin and b. from about 99 to about 1 part by weight of a poly(1,4butylene terephathalate) resin or a copolyester thereof formed with a minor amount of an aliphatic or aromatic dicarboxylic acid or an aliphatic polyol.
Claim 31
Dependent Claim
47 words
The composition as defined in claim 22 wherein the polyester resin is a combination of a poly(1,4-butylene terephthalate) resin or a copolyester thereof and a linear aliphatic polyester resin; said copolyester formed with a minor amount of an aliphatic or aromatic dicarboxylic acid or an aliphatic polyol.
Claim 32
Dependent Claim
62 words
The composition as defined in claim 28 wherein the polyester combination comprises: a. from about 99 to about 60 parts by weight of poly(1,4-butylene terephthalate) resin or a copolyester thereof with a minor amount of an aliphatic or aromatic dicarboxylic acid or an aliphatic polyol and b. from about 1 to about 40 parts by weight of a linear aliphatic polyester resin.
Claim 33
Dependent Claim
15 words
The composition as defined in claim 29 wherein component (a) is a poly(1,4-butylene terephthalate) resin.
Claim 34
Dependent Claim
31 words
The composition as defined in claim 29 wherein the linear aliphatic polyester resin component (b) is poly(betapropiolactone), poly (gammabutyrolactone), poly(deltavalerolactone, poly(epsiloncaprolactone) or a mixture of at least two of the foregoing.
Claim 35
Dependent Claim
27 words
The composition as defined in claim 22 wherein the polyester resin contains units providing branching sites and derived from compounds containing at least three ester forming groups.
Claim 36
Dependent Claim
26 words
A composition as defined in claim 22 wherein said reinforcing filler is selected from the group consisting of reinforcing metals, ceramics, silicas, quartz, glass and carbons.
Claim 37
Dependent Claim
40 words
A composition as defined in claim 33 wherein said reinforcing filler is filamentous glass, in an amount of from about 1 to about 50 percent by weight based on the combined weight of components (a) and (b) and the glass.
Claim 38
Dependent Claim
14 words
The composition as defined in claim 22 wherein the hydroxybenzotriazole is 2-(2'-hydroxy-3',5'-di-tert-amyl phenyl) benzotriazole.
References Cited (Backward Citations)
US3213058A
Cited
US3766205A
Cited
US3413379A
Cited
US3632552A
Cited
US3742087A
Cited
US3723572A
Cited
US3751396A
Cited
US3671487A
Cited
US3833535A
Cited
US3781242A
Cited
US3833685A
Cited
US3835089A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-04-13 | 1979-10-13 | 1980-04-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-04-13 | 1983-10-13 | 1984-04-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-04-13 | 1987-10-13 | 1988-04-13 | $7700.00 | Window Closed / Lapsed |