Method of sealing and spacing glass substrates of gaseous discharge display panels used at high altitudes
Assignee: OI Glass Inc
•
Filing: 1975-01-02
•
Granted: 1976-03-30
•
Expires: 1995-01-02
Abstract
Abstract A low melting, transparent glass spacer rod system is disclosed which will soften and seal the two glass substrates in the center of a gaseous discharge panel at or below the temperature used to seal the periphery but above the gas processing temperature thus relieving the stresses developed at the edge seal when the gas within the panel expands at high altitudes. High melting rods near the seal periphery provide the proper gap spacing between substrates.
Inventors
- 👤 Charles W. Salisbury
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 16:08
CPC Classifications
C; C03; C03C; C03C27/00; C03C27/06; C03C27/10; C03B; C03B23/00; C03B23/20; C03C8/00; C03C8/24; C03C8/245; H; H01; H01J; H01J9/00; H01J9/24; H01J9/26; H01J9/261
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
159 words
A method of sealing the two glass substrates of a gaseous discharge display panel while simultaneously maintaining a uniform gas chamber gap therebetween and strengthening the panel for use at high altitudes which comprise the steps of: a. inserting in the center of the viewing area between electrode lines on one of the glass substrates glass rods which soften at or below the softening temperature of the periphery solder glass b. adhering said center glass rods to the substrate by heating c. applying solder glass with a softening temperature not less than that of said center glass rods to the periphery of the panel d. inserting outside the viewing area but adjacent the periphery solder glass of said substrate stop gap glass rods with a softening temperature higher than either the center glass rods or the periphery solder glass e. placing another glass substrate over the first substrate and f. subjecting the entire assembly to a heat sealing cycle.
Claim 2
Independent Claim
159 words
A method of sealing the two glass substrates of a gaseous discharge display panel while simultaneously maintaining a uniform gas chamber gap therebetween and strengthening the panel for use at high altitudes which comprise the steps of: a. inserting in the center of the viewing area between electrode lines on one of the glass substrates glass rods which soften at or below the softening temperature of the periphery solder glass b. adhering said center glass rods to the substrate by heating c. applying solder glass with a softening temperature not less than that of said center glass rods to the periphery of the panel d. inserting outside the viewing area but adjacent the periphery solder glass of said substrate stop gap glass rods with a softening temperature higher than either the center glass rods or the periphery solder glass e. placing another glass substrate over the first substrate and f. subjecting the entire assembly to a heat sealing cycle.
Claim 3
Dependent Claim
26 words
A method as in claim 1 in which a vitreous solder glass is employed for the center rods, the periphery seal and the stop gap rods.
Claim 4
Dependent Claim
29 words
A method as in claim 2 in which the solder glass employed contains on a weight basis 73.3% PbO, 13.4% B 2 O 3 and 13.3% SiO 2 .
Claim 5
Dependent Claim
37 words
A method as in claim 2 in which the solder glass employed contains on a weight basis 72% PbO, 15% B 2 O 3 , 4% SiO 2 , 5% Al 2 O 3 and 4% ZnO.
Claim 6
Dependent Claim
37 words
A method as in claim 2 in which the solder glass employed contains on a weight basis 72% PbO, 15% B 2 O 3 , 2: SIO 2 , 5% Al 2 O 3 and 6% ZnO.
Claim 7
Dependent Claim
59 words
A method as in claim 2 in which the solder glass employed for the stop gap rods contains on a weight basis 1.5% B 2 O 3 , 67.6% SiO 2 , 2.8% Al 2 O 3 , 15.5% Na 2 O, 5.6% CaO, 4.0% MgO, 2.0% BaO, 0.6% K 2 O and 0.4% Fe 2 O 3 .
Claim 8
Dependent Claim
13 words
A method as in claim 1 in which a devitrifiable solder glass employed.
Claim 9
Dependent Claim
50 words
A method as in claim 1 in which the sealing cycle comprises heating the assembly at a constant rate of from 3° to 5°F. per minute to a maximum of 960°F., holding at that temperature for about one hour and then cooling at the same constant rate to room temperature.
Claim 10
Dependent Claim
33 words
A method as in claim 1 in which the center glass rods are about 7 to 12 mils in diameter and the stop gap rods are about 3 to 6 mils in diameter.
Claim 11
Dependent Claim
47 words
A method as in claim 1 in which the periphery solder glass is dispersed in a vehicle comprising equal parts by weight of poly (alpha methyl) styrene and terpineol in a ratio of 6 parts by weight of said glass to vehicle and applied by screen printing.
Claim 12
Dependent Claim
46 words
A method as in claim 10 in which the periphery solder glass is first applied and heated to burn out the vehicle and then the center glass rods are adhered to the substrate with the same vehicle before placing the stop gap rods adjacent the periphery.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-03-30 | 1979-09-29 | 1980-03-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-03-30 | 1983-09-29 | 1984-03-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-03-30 | 1987-09-29 | 1988-03-30 | $7700.00 | Window Closed / Lapsed |