Method of producing colored anodic coating on aluminum and its alloys
Assignee: Fujisash Co Ltd
•
Filing: 1974-12-05
•
Granted: 1976-03-23
•
Expires: 1994-12-05
Abstract
Abstract Colored anodic coating of aluminum and its alloys can be obtained by immersing the aluminum or its alloys as an anode in an aqueous electrolyte solution containing aromatic sulfonic acid and at least one of formic acid and formate salts, which solution preferably contains at least one of sulfuric acid and water soluble sulfate or bisulfate salts and by passing electric current through the electrolyte solution for a predetermined time.
Inventors
- 👤 Masanori Osuga
- 👤 Hayao Adachi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 18:48
CPC Classifications
C; C25; C25D; C25D11/00; C25D11/02; C25D11/04; C25D11/14
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
122 words
A method of producing colored anodic coating on aluminum and its alloys comprising: providing at least one cathode; immersing the aluminum or its alloys as an anode into an aqueous electrolyte comprising an aromatic sulfonic acid; passing a direct current through the electrolyte solution between the anode and cathode to obtain a colored anodic coating on the aluminum; wherein, an improvement comprises employing, as said aqueous electrolyte, an aqueous electrolyte solution containing (a) aromatic sulfonic acid in an amount of 10 to 500 g/liter and (b) at least one member selected from the group consisting of formic acid and formate salts in an amount of 5 to 200 g, in terms of the weight of formic acid, per liter of the electrolyte.
Claim 2
Independent Claim
122 words
A method of producing colored anodic coating on aluminum and its alloys comprising: providing at least one cathode; immersing the aluminum or its alloys as an anode into an aqueous electrolyte comprising an aromatic sulfonic acid; passing a direct current through the electrolyte solution between the anode and cathode to obtain a colored anodic coating on the aluminum; wherein, an improvement comprises employing, as said aqueous electrolyte, an aqueous electrolyte solution containing (a) aromatic sulfonic acid in an amount of 10 to 500 g/liter and (b) at least one member selected from the group consisting of formic acid and formate salts in an amount of 5 to 200 g, in terms of the weight of formic acid, per liter of the electrolyte.
Claim 3
Dependent Claim
65 words
A method according to claim 1 wherein said aromatic sulfonic acid is selected from the group consisting of sulfothalic acid and sulfosalicylic acid, and said direct current is passed at a current density of from 0.5 to 5 ampere/square decimeter over the period of 1 to 150 minutes and a voltage of from 20 to 120 volts is applied between the anode and the cathode.
Claim 4
Dependent Claim
57 words
A method according to claim 2, wherein said direct current is passed at a current density of 1 to 3 ampere/square decimeter over the period of from 5 to 20 minutes and a voltage of from 25 to 80 volts is applied, thereby obtaining a colored anodic coating having a thickness ranging from 2 to 20 microns.
Claim 5
Dependent Claim
26 words
A method according to claim 1, wherein said aromatic sulfonic acid is at least one selected from the group consisting of sulfophthalic acid and sulfosalicylic acid.
Claim 6
Dependent Claim
16 words
A method according to claim 1, wherein said formate salts are nickel formate and ammonium formate.
Claim 7
Dependent Claim
14 words
A method according to claim 1, wherein said aromatic sulfonic acid is sulfophthalic acid.
Claim 8
Dependent Claim
14 words
A method according to claim 1, wherein said aromatic sulfonic acid is sulfosalicylic acid.
Claim 9
Independent Claim
166 words
A method of producing colored anodic coating on aluminum and its alloys comprising: providing at least one cathode; immersing the aluminum or its alloys as an anode into an aqueous electrolyte comprising aromatic sulfonic acid; passing a direct current through the electrolyte solution between the anode and cathode to obtain a colored anodic coating on the aluminum anode; wherein an improvement comprises employing, as said aqueous electrolyte, an aqueous electrolyte solution containing (a) aromatic sulfonic acid in an amount of from 10 to 500 g/liter (b) at least one first member selected from the group consisting of formic acid and formate salts in an amount of from 5 to 200 g, in terms of the weight of formic acid, per liter of the electrolyte and (c) at least one second member selected from the group consisting of sulfuric acid and water soluble sulfate or bisulfate salts in an amount not higher than 5g, in terms of the weight of sulfuric acid, per litre of the electrolyte.
Claim 10
Independent Claim
166 words
A method of producing colored anodic coating on aluminum and its alloys comprising: providing at least one cathode; immersing the aluminum or its alloys as an anode into an aqueous electrolyte comprising aromatic sulfonic acid; passing a direct current through the electrolyte solution between the anode and cathode to obtain a colored anodic coating on the aluminum anode; wherein an improvement comprises employing, as said aqueous electrolyte, an aqueous electrolyte solution containing (a) aromatic sulfonic acid in an amount of from 10 to 500 g/liter (b) at least one first member selected from the group consisting of formic acid and formate salts in an amount of from 5 to 200 g, in terms of the weight of formic acid, per liter of the electrolyte and (c) at least one second member selected from the group consisting of sulfuric acid and water soluble sulfate or bisulfate salts in an amount not higher than 5g, in terms of the weight of sulfuric acid, per litre of the electrolyte.
Claim 11
Dependent Claim
67 words
A method according to claim 6 wherein said aromatic sulfonic acid (a) is selected from the group consisting of sulfophthalic acid and sulfosalicylic acid, and, further said direct current is passed at a current density of from 0.5 to 5 ampere/square decimeter over a period of 1 to 150 minutes and a voltage of from 20 to 100 volts is applied between the anode and the cathode.
Claim 12
Dependent Claim
29 words
A method according to claim 9, wherein said second member is contained in the electrolyte in an amount of from 0.5 to 2 g per liter of the electrolyte.
Claim 13
Dependent Claim
26 words
A method according to claim 8, wherein said aromatic sulfonic acid is at least one selected from the group consisting of sulfophthalic acid and sulfosalicylic acid.
Claim 14
Dependent Claim
13 words
A method according to claim 8, wherein said first member is formic acid.
Claim 15
Dependent Claim
13 words
A method according to claim 8, wherein said second member is sulfuric acid.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-03-23 | 1979-09-22 | 1980-03-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-03-23 | 1983-09-22 | 1984-03-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-03-23 | 1987-09-22 | 1988-03-23 | $7700.00 | Window Closed / Lapsed |