Methods of producing chemically hardening coatings
Assignee: Kaman Sciences Corp
•
Filing: 1970-02-02
•
Granted: 1976-03-16
•
Expires: 1990-02-02
Abstract
Abstract A new ceramic treatment process and product and, more particularly, a process for forming and treating and shaping and treating of porous skeletal bodies to produce hardened dimensionally stable end products of relatively low temperatures and the resulting materials produced thereby which comprises the steps of treating a porous skeletal body by impregnating the interstices of the porous body with a compound of a metal capable of being converted to an oxide in situ at relatively low temperatures, heating the body so impregnated at temperatures well below normal vitrification to a temperature of at least 600°F. and for a period of time sufficient to convert the compound impregnated therein to an oxide and repeating the impregnation and heating steps until the desired degree of hardness is obtained. The invention further contemplates the forming of the porous body from relatively finely divided materials which may be relatively pure powders, mixtures of powders or impure powders, including additives in the form of discrete particles, fibers, fillers and the like, which powders are molded and bound together or bound together and molded with a binder which may comprise the impregnating compound or other suitable binder prior to treatment.
Inventors
- 👤 Peter K. Church
- 👤 Oliver J. Knutson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 18:53
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/45; C04B41/50; C04B41/5025; C04B41/5033; C04B41/80; C04B41/81; C04B41/85; C04B41/87; F; F02; F02B; F02B75/00; F02B75/02; F02B2075/022; F02B2075/027
Claims Analysis
Total Claims: 32
Claim 1
Independent Claim
102 words
A method of producing a chemically hardened refractory coating on a substrate having a porous coating thereon of a refractory oxide having a vitrification temperature in excess of 600°F. which comprises: impregnating the porous oxide coating with a solution of a chromium compound which is capable of being converted to an oxide on being heated; drying and curing said impregnated coating by heating same to a temperature below the vitrification temperature of the oxide but sufficient to convert the chromium compound in situ to an oxide; and, repeating the impregnation and curing steps at least once to harden and densify the coating.
Claim 2
Independent Claim
102 words
A method of producing a chemically hardened refractory coating on a substrate having a porous coating thereon of a refractory oxide having a vitrification temperature in excess of 600°F. which comprises: impregnating the porous oxide coating with a solution of a chromium compound which is capable of being converted to an oxide on being heated; drying and curing said impregnated coating by heating same to a temperature below the vitrification temperature of the oxide but sufficient to convert the chromium compound in situ to an oxide; and, repeating the impregnation and curing steps at least once to harden and densify the coating.
Claim 3
Dependent Claim
49 words
The method of claim 1 wherein the oxide refractory is selected from the group consisting of oxides of aluminum, barium, beryllium, calcium, cerium, chromium, cobalt, copper, gallium, hafnium, iron, lanthanum, magnesium, manganese, molybdenum, nickel niobium, silicon tantalum, thorium, tin, titanium, tungsten, uranium, vanadium, yttrium, zinc, zirconium and mixtures thereof.
Claim 4
Dependent Claim
11 words
The method of claim 1 wherein the solution is chromic acid.
Claim 5
Dependent Claim
54 words
The method of claim 1 which includes as a last step the impregnation of the hardened refractory body with phosphoric acid and heating and curing said body by raising the temperature of said body to at least about 600°F. in increments over a period of time sufficient to completely dry and harden the body.
Claim 6
Dependent Claim
20 words
The method of claim 1 wherein the drying and curing is carried out at a temperature of at least 600°F.
Claim 7
Dependent Claim
23 words
The method of claim 1 wherein the porous refractory oxide coating is sprayed onto the substrate in a porous state prior to impregnation.
Claim 8
Dependent Claim
15 words
The method of claim 6 where the coating is plasma sprayed on to the substrate.
Claim 9
Dependent Claim
17 words
The method of claim 6 where the coating is formed on the substrate by a detonation process.
Claim 10
Independent Claim
101 words
A method of producing a chemically hardened coating on a substrate which comprises: forming a porous refractory oxide coating having a vitrification temperature in excess of 600°F. on the substrate; impregnating the porous oxide coating with a solution of a chromium compound which is capable of being converted to an oxide on being heated; drying and curing said impregnated coating by heating same to a temperature below the vitrification temperature of the oxide coating but sufficient to convert the chromium compound in situ to an oxide; repeating the impregnation and curing steps at least once to harden and densify the coating.
Claim 11
Independent Claim
101 words
A method of producing a chemically hardened coating on a substrate which comprises: forming a porous refractory oxide coating having a vitrification temperature in excess of 600°F. on the substrate; impregnating the porous oxide coating with a solution of a chromium compound which is capable of being converted to an oxide on being heated; drying and curing said impregnated coating by heating same to a temperature below the vitrification temperature of the oxide coating but sufficient to convert the chromium compound in situ to an oxide; repeating the impregnation and curing steps at least once to harden and densify the coating.
Claim 12
Dependent Claim
22 words
The method of claim 9 wherein the refractory oxide coating is formed and applied to the substrate by means of flame spraying.
Claim 13
Dependent Claim
22 words
THe method of claim 9 wherein the refractory oxide coating is formed and applied to the substrate by means of plasma spraying.
Claim 14
Dependent Claim
23 words
The method of claim 9 wherein the refractory oxide coating is formed and applied to the substrate by means of a detonation process.
Claim 15
Dependent Claim
50 words
The method of claim 9 wherein the refractory oxide coating is selected from the group consisting of oxides of aluminum, barium, beryllium, calcium, cerium, chromium, cobalt, copper, gallium, hafnium, iron, lanthanum, magnesium, manganese, molybdenum, nickel, niobium, silicon, tantalum, thorium, tin, titanium, tungsten, uranium, vanodium, yttrium, zinc, zirconium and mixtures thereof.
Claim 16
Dependent Claim
11 words
The method of claim 9 wherein the solution is chromic acid.
Claim 17
Dependent Claim
54 words
The method of claim 9 which includes as a last step the impregnation of the hardened refractory body with phosphoric acid and heating and curing said body by raising the temperature of said body to at least about 600°F. in increments over a period of time sufficient to completely dry and harden the body.
Claim 18
Dependent Claim
22 words
The method of claim 9 where the substrate is metal and the oxide coating is formed by oxidation of the metal substrates.
Claim 19
Dependent Claim
14 words
The method of claim 9 where the coating is flame sprayed onto the substrate.
Claim 20
Dependent Claim
20 words
The method of claim 9 wherein the drying and curing is carried out at a temperature of at least 600°F.
Claim 21
Dependent Claim
43 words
The method of claim 9 wherein the refractory oxide coating is formed by applying a slurry of finely divided particles of at least one refractory oxide suspended in a fluid to the substrate and driving out the fluid to produce a porous coating.
Claim 22
Dependent Claim
11 words
The method of claim 19 wherein the fluid is chromic acid.
Claim 23
Dependent Claim
15 words
The method of claim 19 wherein the fluid is a solution of a chromium compound.
Claim 24
Independent Claim
109 words
A method of producing a chemically hardened coating on a substrate which comprises: applying a slurry of finely divided particles of a metal in a fluid to a substrate and driving out the fluid to produce a porous coating; impregnating the porous coating with a solution of a chromium compound which is capable of being converted to an oxide on being heated; drying and curing said impregnated coating by heating same to a temperature below the vitrification temperaturre of said coating but sufficient to convert the chromium compound in situ to an oxide; and, repeating the impregnation and curing steps at least once to harden and densify the coating.
Claim 25
Independent Claim
109 words
A method of producing a chemically hardened coating on a substrate which comprises: applying a slurry of finely divided particles of a metal in a fluid to a substrate and driving out the fluid to produce a porous coating; impregnating the porous coating with a solution of a chromium compound which is capable of being converted to an oxide on being heated; drying and curing said impregnated coating by heating same to a temperature below the vitrification temperaturre of said coating but sufficient to convert the chromium compound in situ to an oxide; and, repeating the impregnation and curing steps at least once to harden and densify the coating.
Claim 26
Dependent Claim
11 words
The method of claim 22 wherein the fluid is chromic acid.
Claim 27
Dependent Claim
15 words
The method of claim 22 wherein the fluid is a solution of a chromium compound.
Claim 28
Dependent Claim
27 words
The method of claim 22 wherein the metal particles are selected from the group consisting of stainless steel, molybdenum, titanium, aluminum, iron, nickel, chromium, tungsten and copper.
Claim 29
Independent Claim
119 words
The method of producing a chemically hardened coating on a substrate which comprises: applying a slurry of finely divided particles of a carbide selected from the group consisting of boron and silicon carbides in a fluid to a substrate and driving out the fluid to produce a porous coating; impregnating the porous coating with a solution of a chromium compound which is capable of being converted to an oxide on being heated; drying and curing said impregnated coating by heating same to a temperature below the vitrification temperature of said coating but sufficient to convert the chromium compound in situ to an oxide; and, repeating the impregnation and curing steps at least once to harden and densify the coating.
Claim 30
Independent Claim
119 words
The method of producing a chemically hardened coating on a substrate which comprises: applying a slurry of finely divided particles of a carbide selected from the group consisting of boron and silicon carbides in a fluid to a substrate and driving out the fluid to produce a porous coating; impregnating the porous coating with a solution of a chromium compound which is capable of being converted to an oxide on being heated; drying and curing said impregnated coating by heating same to a temperature below the vitrification temperature of said coating but sufficient to convert the chromium compound in situ to an oxide; and, repeating the impregnation and curing steps at least once to harden and densify the coating.
Claim 31
Dependent Claim
11 words
The method of claim 26 wherein the fluid is chromic acid.
Claim 32
Dependent Claim
15 words
The method of claim 26 wherein the fluid is a solution of a chromium compound.
References Cited (Backward Citations)
US2118795A
Cited
US2325553A
Cited
US2354876A
Cited
US2714563A
Cited
US2874071A
Cited
US2805174A
Cited
US2987417A
Cited
US3219730A
Cited
GB1003118A
Cited
US3248251A
Cited
US3300331A
Cited
US3483111A
Cited
US3380849A
Cited
US3505101A
Cited
US3481780A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-03-16 | 1979-09-15 | 1980-03-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-03-16 | 1983-09-15 | 1984-03-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-03-16 | 1987-09-15 | 1988-03-16 | $7700.00 | Window Closed / Lapsed |