Increasing the yield of cast plastic lenses
Assignee: BMC Industries Inc
•
Filing: 1974-02-11
•
Granted: 1976-03-16
•
Expires: 1994-02-11
Abstract
Abstract A terpolymer plastic lens having equal or greater light transmission, greater hardness and scratch resistance equal to the monomers used in prior art plastic lenses is obtained by the co-polymerization of diethylene glycol bis (allyl carbonate), methyl methacrylate and methacrylic acid or acrylic acid.
Inventors
- 👤 Herbert M. Bond
- 👤 Daniel L. Torgersen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 16:53
CPC Classifications
G; G02; G02B; G02B1/00; G02B1/04; G02B1/041; B; B29; B29D; B29D11/00; B29D11/00009; C; C08; C08F; C08F18/00; C08F18/02; C08F18/04; C08F18/08
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
162 words
In the process of preparing a polymerized lens in a glass mold by preparing a reactant mixture of methyl methacrylate, diethylene glycol bis (allyl carbonate) and an acid selected from the group consisting of acrylic acid and methacrylic acid, which method comprises: preparing a monomer mixture of methyl methacrylate and diethylene glycol bis (allyl carbonate) wherein the methyl methacrylate monomer ranges from about 10 to about 50% by weight of the monomer mixture, balance diethylene glycol bis (allyl carbonate); adding to said monomer mixture a lubricant and a catalyst of benzoyl peroxide ranging from between about 1 to 1.5% by weight of the monomer mixture; exposing said reactant mixture to a thermal treating zone to polymerize said reactant mixture and form a terpolymer therefrom with the improvement comprising adding to said monomer mixture an acid selected from the group consisting of acrylic acid and methacrylic acid, with said acid ranging from between about 1/2 to 5% by weight of said monomer mixutre.
Claim 2
Dependent Claim
162 words
In the process of preparing a polymerized lens in a glass mold by preparing a reactant mixture of methyl methacrylate, diethylene glycol bis (allyl carbonate) and an acid selected from the group consisting of acrylic acid and methacrylic acid, which method comprises: preparing a monomer mixture of methyl methacrylate and diethylene glycol bis (allyl carbonate) wherein the methyl methacrylate monomer ranges from about 10 to about 50% by weight of the monomer mixture, balance diethylene glycol bis (allyl carbonate); adding to said monomer mixture a lubricant and a catalyst of benzoyl peroxide ranging from between about 1 to 1.5% by weight of the monomer mixture; exposing said reactant mixture to a thermal treating zone to polymerize said reactant mixture and form a terpolymer therefrom with the improvement comprising adding to said monomer mixture an acid selected from the group consisting of acrylic acid and methacrylic acid, with said acid ranging from between about 1/2 to 5% by weight of said monomer mixutre.
Claim 3
Dependent Claim
73 words
The process as set forth in claim 1 being particularly characterized in that a lubricant is added to said reactant mixture prior to polymerization thereof, and wherein said lubricant is selected from the group consisting of mono and dialkyl phosphates having from between about 16 and 18 carbon atoms in the alkyl radical, and stearic acid, said lubricant being present in said reactant mixture in a quantity of less than about 20 ppm.
Claim 4
Dependent Claim
28 words
The process as set forth in claim 1 wherein said treating zone increases the temperature of said reactant mixture slowly until a temperature of about 100°C. is reached.
Claim 5
Dependent Claim
38 words
The process as set forth in claim 1 being particularly characterized in that said acid is methacrylic acid, and is present in said reactant mixture in an amount greater than 1/2 % by weight of the reactant mixture.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-03-16 | 1979-09-15 | 1980-03-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-03-16 | 1983-09-15 | 1984-03-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-03-16 | 1987-09-15 | 1988-03-16 | $7700.00 | Window Closed / Lapsed |