US3940254A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Nickel clad steel coinage blank
Assignee: Viridian Inc Canada
•
Filing: 1974-10-21
•
Granted: 1976-02-24
•
Expires: 1994-10-21
Abstract
Abstract A two-component blank suitable for minting into a coin is described. The blank consists of a low-carbon steel core completely encased in nickel. The blank has magnetic properties sufficiently similar to a solid nickel coin of the same size that the minted blank is accepted by magnetic property testing coin discriminating devices which accept pure nickel coins.
Inventors
- 👤 Arthur G. McMullen
- 👤 Michael J. H. Ruscoe
- 👤 Maurice A. Clegg
- 👤 Ronald L. Prowse
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 08:33
CPC Classifications
B; B32; B32B; B32B15/00; B32B15/01; B32B15/013; B32B15/015; Y; Y10; Y10S; Y10S428/00; Y10S428/922; Y10S428/923; Y10S428/924; Y10S428/926; Y10S428/9265; Y10S428/928; Y10T; Y10T428/00; Y10T428/12; Y10T428/12486; Y10T428/12493; Y10T428/12771; Y10T428/12861; Y10T428/12937; Y10T428/12951; Y10T428/12972
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
152 words
A coin blank comprising a core formed of low carbon steel having a carbon content below about 0.03 wt. %, a continuous cladding of nickel completely encasing said core, said cladding having a thickness of at least 0.05 mm on each of the opposed faces of the blank and a thickness, measured radially, of 2 to 4 times the face thickness at the edge thereof, a layer of interdiffused nickel and iron metallurgically bonding said cladding to said core, said blank having a hardness value of less than 65 on the Rockwell 30T hardness scale and said blank having an induced magnetism value B in a field of 150 oersteds of less than about 4000 gauss measured on an axis through the centre of and normal to the faces of the blank whereby said blank, after minting, possesses magnetic properties substantially similar to a pure nickel coin of similar size and shape.
Claim 2
Dependent Claim
152 words
A coin blank comprising a core formed of low carbon steel having a carbon content below about 0.03 wt. %, a continuous cladding of nickel completely encasing said core, said cladding having a thickness of at least 0.05 mm on each of the opposed faces of the blank and a thickness, measured radially, of 2 to 4 times the face thickness at the edge thereof, a layer of interdiffused nickel and iron metallurgically bonding said cladding to said core, said blank having a hardness value of less than 65 on the Rockwell 30T hardness scale and said blank having an induced magnetism value B in a field of 150 oersteds of less than about 4000 gauss measured on an axis through the centre of and normal to the faces of the blank whereby said blank, after minting, possesses magnetic properties substantially similar to a pure nickel coin of similar size and shape.
Claim 3
Dependent Claim
19 words
The blank as claimed in claim 1 wherein said mild steel core contains less than 0.01% by weight carbon.
Claim 4
Dependent Claim
22 words
The blank as claimed in claim 1 wherein the hardness value is less than about 45 on the Rockwell 30T hardness scale.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-02-23 | 1979-08-25 | 1980-02-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-02-23 | 1983-08-25 | 1984-02-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-02-23 | 1987-08-25 | 1988-02-24 | $7700.00 | Window Closed / Lapsed |