Abstract Method of hardening powdered titania (titanium dioxide) so as to make it attrition-resistant and to enhance its properties as a catalyst carrier. The method involves thoroughly dispersing powdered titanium dioxide in water, removing the excess water, drying and then calcining the product at a temperature between 650°C and 900°C. Preferably a large excess of water is used, at least 37% to effect dispersion; and dispersion may be aided by use of a surfactant, a water soluble organic compound or a highly polar inorganic compound. The excess water may be removed by filtration or the use of flocculants. The resultant powdered material is particularly useful as a carrier for oxidising ortho-xylene to phthalic anhydride.
A method of hardening powdered titania comprising thoroughly dispersing a composition consisting essentially of commercial pigment grade anatase or rutile in a large excess of water, removing excess water to form a paste of said titania and water, drying said paste and then calcining the titania at a temperature of 650°C to 900°C.
Claim 2
Independent Claim
53 words
A method of hardening powdered titania comprising thoroughly dispersing a composition consisting essentially of commercial pigment grade anatase or rutile in a large excess of water, removing excess water to form a paste of said titania and water, drying said paste and then calcining the titania at a temperature of 650°C to 900°C.
Claim 3
Dependent Claim
19 words
A method according to claim 1 and in which the removal of the excess water is achieved by filtration.
Claim 4
Dependent Claim
14 words
A method according to claim 1 and in which the powdered titania is anatase.
Claim 5
Dependent Claim
18 words
A method according to claim 3 and in which the anatase is British Titan Products AHR grade anatase.
Claim 6
Dependent Claim
17 words
A method according to claim 1 and in which the calcination temperature is between 800°C and 850°C.
Claim 7
Dependent Claim
25 words
A method according to claim 1 in which the amount of water, as a percentage of the water plus titanium dioxide, is at least 37%.
Claim 8
Dependent Claim
21 words
A carrier for oxidising ortho-xylene to phthalic anhydride which consists of titania prepared in accordance with the method of claim 1.