Abstract A process for preparing fusible, crosslinkable resinous intermediates of polyaddition and polycondensation resins consisting essentially of continuously proportioning and feeding a resin precursor composition in solid and liquid form, in a mixing and kneading machine, intensively mixing the resin precursor composition in both the longitudinal and transversal directions and simultaneously heating said composition, thereby plasticizing and homogenizing the same below the temperature of cross-linking and hardening and at a temperature of 50°-90° C during a brief average dwell time in the mixing chamber of said machine which will prevent excessive stiffening of the mixture in the form of a pasty mass to thereby plug the machine, continuously expelling the plasticized intermediate resin mix at a temperature of 50° to 90° C in the form of a pasty mass through a hollow die with twin conical outlet heated to a temperature of not more than 50° C. The intermediate resin mix which is expelled is cooled, solidified, preformed by a pair of rollers into a strand which is friable and is adapted to be broken by up grinding to form a powdered intermediate.
A process for the preparation of fusible resinous intermediates of fully cross-linkable polyaddition and polycondensation resins, consisting essentially of: continuously proportioning and feeding the resin precursor composition containing one of the precursors as a linear polymer, in solid or liquid form, in a mixing and kneading machine; intensively mixing the resin precursor composition in both the longitudinal and transversal directions and simultaneously heating said composition, thereby plasticizing and homogenizing the same below the temperature of cross-linking and hardening and at a temperature of 50° to 90° C during a brief average dwell time in the mixing chamber of said machine which will prevent stiffening of the mixture whereby the mixture is in the form of a pasty mass at a temperature of about 50° to 90°; continuously expelling the plasticized pasty mass at said temperature of 50° to 90° C through a hollow heated die having an outlet in the form of a twin conical throat with acute edges sloping away smoothly at inlet and outlet sides to a temperature of not more than 50° C; preforming said expelled mass between a pair of rollers to form a strand; cooling and solidifying the expelled strand into a friable state; and, breaking up and grinding said strand into a powder adapted to fuse and cross-link.
Claim 2
Dependent Claim
214 words
A process for the preparation of fusible resinous intermediates of fully cross-linkable polyaddition and polycondensation resins, consisting essentially of: continuously proportioning and feeding the resin precursor composition containing one of the precursors as a linear polymer, in solid or liquid form, in a mixing and kneading machine; intensively mixing the resin precursor composition in both the longitudinal and transversal directions and simultaneously heating said composition, thereby plasticizing and homogenizing the same below the temperature of cross-linking and hardening and at a temperature of 50° to 90° C during a brief average dwell time in the mixing chamber of said machine which will prevent stiffening of the mixture whereby the mixture is in the form of a pasty mass at a temperature of about 50° to 90°; continuously expelling the plasticized pasty mass at said temperature of 50° to 90° C through a hollow heated die having an outlet in the form of a twin conical throat with acute edges sloping away smoothly at inlet and outlet sides to a temperature of not more than 50° C; preforming said expelled mass between a pair of rollers to form a strand; cooling and solidifying the expelled strand into a friable state; and, breaking up and grinding said strand into a powder adapted to fuse and cross-link.