Integrated fluidized reduction and melting of iron ores

Claim 3

The process of claim 1 wherein the carbonaceous fuel is coke.

Claim 4

The process of claim 1 wherein the reducing gas is transferred to the bottom of the reducing zone to fludiize coke mixed with iron ore so as to maintain the temperature in the reducing zone in the range of about 1400°F. to about 1600°F. and wherein the partially reduced ore transferred to the refining zone is from about 30 percent to about 50 percent metallized.

Claim 5

The process of claim 1 wherein the transferred reducing gas is admixed with a recycle gas from the reducing zone therby providing a reducing gas for fluidization of the iron ore which will maintain the temperature in the reducing zone in the range of about 1400°F. to about 1600°F and wherein the partially reduced ore transferred to the refining zone is from about 65 percent to about 85 percent metallized.

Claim 6

The process of claim 1 wherein the amount of carbonaceous fuel also is controlled to provide a molten iron-containing material having a carbon content in the range of from about 0.05 percent to about 4.3 percent.

Claim 7

A process for making iron-containing materials for finely divided iuron ore by combining separate reducing and refining steps and comprising the steps of: a. fluidizing the iron ore in the reduction zone with a reducing gas to effect a partial reduction of the iron ore at temperatures below about 1900°F. to a metallization in the range from about 30 percent to about 85 percent; b. transferring the partially reduced iron ore from the reduction zone to a refining zone for melting and processing; c. introducing the iron ore transfer from the reducing zone to the melting zone below the molten metal in the melting zone; d. introducing carbonaceous fuel and oxygen into the refining zone to generate sufficient heat for melting, and finally reducing the partially reduced ore and to liberate a hot CO rich reducing gas at a temperature range of about 2600°F. to 3000°F. and having a CO/CO 2 mole ratio of about 4:1 to about 9:1; e. transferring said reducing gas from a refining zone to the reduction zone to fluidize and partially reduce the iron therein; and f. recovering a molten iron-containing material.

Claim 8

A process for making iron-containing materials for finely divided iuron ore by combining separate reducing and refining steps and comprising the steps of: a. fluidizing the iron ore in the reduction zone with a reducing gas to effect a partial reduction of the iron ore at temperatures below about 1900°F. to a metallization in the range from about 30 percent to about 85 percent; b. transferring the partially reduced iron ore from the reduction zone to a refining zone for melting and processing; c. introducing the iron ore transfer from the reducing zone to the melting zone below the molten metal in the melting zone; d. introducing carbonaceous fuel and oxygen into the refining zone to generate sufficient heat for melting, and finally reducing the partially reduced ore and to liberate a hot CO rich reducing gas at a temperature range of about 2600°F. to 3000°F. and having a CO/CO 2 mole ratio of about 4:1 to about 9:1; e. transferring said reducing gas from a refining zone to the reduction zone to fluidize and partially reduce the iron therein; and f. recovering a molten iron-containing material.

Claim 9

The process of claim 6 wherein a carbonaceous fuel and oxygen introduced in the refining zone in Step (d) is adjusted to provide a reducing gas with a CO/CO 2 mole ratio of from about 4:1 to about 9:1 at a temperature of about 2600° to 3000°F.

Claim 10

The process of claim 7 further characterized by admixing the transferred reducing gas of step (e) with coke and iron ore in the bottom of the reducing zone whereby the temperature in the reducing zone is maintained in the range of about 1400°F. to about 1600°F. and in which transferred ore of step (b) is about 30 percent to about 50 percent metallized.

Claim 11

The process of claim 7 wherein the reducing gas transferred from the refining zone to the reducing zone is mixed before introduction in the reducing zone with a recycle gas from said zone to provide a reducing gas mixture having a temperature sufficient to maintain the temperature in the reducing zone in the range of about 1,400°F. to about 1600°F. and wherein the ore transferred in step (b) is about 65 percent to about 85 percent metallized.

Claim 12

The process of claim 6 including the steps of controlling the carbon content in the refining zone to provide a molten iron containing material having a carbon content of from about 0.05 wt. percent to about 4.3 wt. percent.

Claim 13

The process of claim 6 including the steps of providing lime and process additives in the refining zone to obtain a molten iron-containing material and slag.