Controlled environment superplastic forming of metals
Assignee: Boeing North American Inc
•
Filing: 1974-07-08
•
Granted: 1976-01-27
•
Expires: 1994-07-08
Abstract
Abstract Metals such as titanium alloy blanks which are subject to contamination by air at elevated temperatures are precision formed into desired shapes in a controlled environment. The metal worksheet and a shaping member are located within an enclosure. An inert gas environment is provided in the enclosed area. The metal worksheet is heated to a suitable forming temperature and stretched substantially in excess of its original surface area under tensile stress from a fluid pressure loading and formed into the desired shape by interaction with the shaping member. Novel sealing arrangements for the enclosed area of the forming apparatus are provided.
Inventors
- 👤 Charles Howard Hamilton
- 👤 Fred B. Koeller
- 👤 Roger S. Raymond
- 👤 Martin Goldberg
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 20:40
CPC Classifications
B; B21; B21D; B21D26/00; B21D26/02; B21D26/053; B21D26/055; Y; Y10; Y10S; Y10S72/00; Y10S72/709
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
189 words
A method of making metallic forms in a controlled environment comprising: providing at least one shaping member having a surface formed complimentary to the shape desired to be formed; providing a metal blank having an effective strain rate sensitivity and two opposed principal surfaces; enclosing an area around said metal blank and said at least one shaping member, said enclosed area being divided into first and second chambers by said metal blank, said metal blank being positioned as a diaphram between said chambers, said at least one shaping member being located in said first chamber; providing an inert gas environment in said chambers; heating said metal blank to a temperature suitable for superplastic forming; and controlling the fluid pressure of said inert gas within said chambers to induce a pressure loading across the principal surfaces of said metal blank wherein the fluid pressure of said inert gas within said second chamber is greater than the fluid pressure of said inert gas within said first chamber, thereby causing said metal blank to deform into said first chamber and against, and into intimate contact with, said at least one shaping member.
Claim 2
Independent Claim
189 words
A method of making metallic forms in a controlled environment comprising: providing at least one shaping member having a surface formed complimentary to the shape desired to be formed; providing a metal blank having an effective strain rate sensitivity and two opposed principal surfaces; enclosing an area around said metal blank and said at least one shaping member, said enclosed area being divided into first and second chambers by said metal blank, said metal blank being positioned as a diaphram between said chambers, said at least one shaping member being located in said first chamber; providing an inert gas environment in said chambers; heating said metal blank to a temperature suitable for superplastic forming; and controlling the fluid pressure of said inert gas within said chambers to induce a pressure loading across the principal surfaces of said metal blank wherein the fluid pressure of said inert gas within said second chamber is greater than the fluid pressure of said inert gas within said first chamber, thereby causing said metal blank to deform into said first chamber and against, and into intimate contact with, said at least one shaping member.
Claim 3
Dependent Claim
30 words
A method as defined in claim 1 wherein said metal blank is positioned with its principal opposed surfaces in operative projection with respect to said at least one shaping member.
Claim 4
Dependent Claim
44 words
The method as defined in claim 2 wherein said pressure loading across said principal surfaces is applied for a substantial period of time inversely related to the induced tensile stress and said metal blank is stretched substantially in excess of its original surface area.
Claim 5
Dependent Claim
34 words
The method as defined in claim 3 wherein said first chamber is vented to allow for efflux of inert gas as said metal blank deforms and thereby reduces the size of said first chamber.
Claim 6
Dependent Claim
31 words
The method as defined in claim 3 wherein said pressure loading comprises application of vacuum to said first chamber while maintaining a constant pressure of inert gas in said second chamber.
Claim 7
Dependent Claim
29 words
The method as defined in claim 3 wherein said pressure loading comprises application of vacuum to said first chamber and increased pressure of inert gas in said second chamber.
Claim 8
Dependent Claim
19 words
The method of claim 3 wherein said inert gas is argon and said metal blank is titanium alloy sheet.
Claim 9
Dependent Claim
22 words
The method as defined in claim 7 also including sealing said enclosed area to prevent influx of air into said enclosed area.
Claim 10
Dependent Claim
155 words
Apparatus for making metallic forms from metal blank having an effective strain rate sensitivity in a controlled environment comprising: at least one shaping member having a surface formed complimentary to the shape desired to be formed; an enclosure around said metal blank and said at least one shaping member, said metal blank being positioned within said enclosure such that said enclosure is divided into first and second separate chambers, said at least one shaping member being located in said first chamber; means for heating said metal blank to a suitable forming temperature; and an environmental control means for providing an inert gas environment with said chambers during heating and forming of said metal blank and for regulating the inert gas pressure in said first and second chambers to induce a pressure loading across said metal blank to cause said metal blank to deform against, and into intimate contact with, said at least one shaping member.
Claim 11
Dependent Claim
155 words
Apparatus for making metallic forms from metal blank having an effective strain rate sensitivity in a controlled environment comprising: at least one shaping member having a surface formed complimentary to the shape desired to be formed; an enclosure around said metal blank and said at least one shaping member, said metal blank being positioned within said enclosure such that said enclosure is divided into first and second separate chambers, said at least one shaping member being located in said first chamber; means for heating said metal blank to a suitable forming temperature; and an environmental control means for providing an inert gas environment with said chambers during heating and forming of said metal blank and for regulating the inert gas pressure in said first and second chambers to induce a pressure loading across said metal blank to cause said metal blank to deform against, and into intimate contact with, said at least one shaping member.
Claim 12
Dependent Claim
54 words
Apparatus as set out in claim 9 wherein said environmental control means includes a vent in said first chamber to allow for efflux of inert gas when the pressure in said second chamber is greater than said first chamber thereby causing said metal blank to deform and reduce the size of said first chamber.
Claim 13
Dependent Claim
23 words
Apparatus as set out in claim 9 wherein said environmental control means includes a means for application of vacuum to said first chamber.
Claim 14
Dependent Claim
39 words
Apparatus as set out in claim 9 also including sealing means for said enclosure to ensure that the portion of said metal blank to be formed is only exposed to the environment within said enclosure during heating and forming.
Claim 15
Dependent Claim
14 words
Apparatus as set out in claim 12 wherein said sealing means includes a press.
Claim 16
Dependent Claim
60 words
Apparatus as set out in claim 13 wherein said enclosure comprises upper and lower frame members; said metal blank is positioned between said frame members; and said seal means includes a metal O-ring and a high temperature sealant mounted between said metal blank and said lower frame member and in contact with a single continuous edge of said metal blank.
Claim 17
Dependent Claim
47 words
Apparatus as set out in claim 13 wherein said enclosure includes upper and lower frame members; said metal blank is positioned between said frame members; and said sealing means includes a projection on said lower frame member in contact with a continuous edge of said metal blank.
Claim 18
Dependent Claim
68 words
Apparatus as set out in claim 13 wherein said enclosure includes upper and lower frame members; said metal blank is mounted between said frame members; and said sealing means includes a pair of projections on said lower frame member in contact with a continuous edge of said metal blank, a cavity in said lower frame member between said projections, and means for providing inert gas to said cavity.
Claim 19
Dependent Claim
21 words
Apparatus as set out in claim 12 wherein said inert gas is argon and said metal blank is titanium alloy sheet.
References Cited (Backward Citations)
US3440858A
Cited
US3339387A
Cited
US3535766A
Cited
US3595060A
Cited
US3646653A
Cited
GB1231428A
Cited
US3572073A
Cited
US3698219A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-01-26 | 1979-07-28 | 1980-01-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-01-26 | 1983-07-28 | 1984-01-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-01-26 | 1987-07-28 | 1988-01-27 | $7700.00 | Window Closed / Lapsed |