Abstract A relatively inexpensive injection molding-grade thermoplastic polyurethane is based on a modified polyether diol. This elastomer has improved toughness, abrasion resistance and good mechanical properties. Its temperature insensitivity and low temperature flexability are exceptional. It is flexible to impact at -50°F and stiff enough at 250°F to allow painting without distortion. Of special interest is the fact that this grafted PPG-based polymer is injection moldable and possesses properties adequate for exterior automobile trim components and the like. The modified polyether polyol is a poly (oxypropylene) diol reacted with a 50/50 styrene/acrylonitrile monomer mixture using a free radical catalyst. While a one shot method of preparation can be used, the capped polyol is preferably reacted with an aromatic diisocyanate to form a prepolymer in a known manner. The prepolymer is thereafter reacted with a C 2 to C 6 alkane diol, pan cast, cured and aged, followed by grinding to give the molding composition.
An injection molding-grade thermoplastic polyurethane having good low temperature properties made by reacting the following:Grafted polyol, PBW 100Aromatic Polyisocyanate, to FNCO of 7 to 15C 2 -C 6 alkane diol, PBW 5 to 30 wherein: said grafted polyol is a 2000 to 5000 molecular weight copolymer of: a. 70 to 90 weight percent of a 1000 to 4000 molecular weight poly (oxy C 1 -C 4 alkene) diol, reacted by free radical polymerization with b. 10 to 30 weight percent of a monomer mixture of 1 part by weight of a vinylaromatic and 0.1 to 9 parts of an olefinic C 2 -C 6 nitrile.
Claim 2
Dependent Claim
105 words
An injection molding-grade thermoplastic polyurethane having good low temperature properties made by reacting the following:Grafted polyol, PBW 100Aromatic Polyisocyanate, to FNCO of 7 to 15C 2 -C 6 alkane diol, PBW 5 to 30 wherein: said grafted polyol is a 2000 to 5000 molecular weight copolymer of: a. 70 to 90 weight percent of a 1000 to 4000 molecular weight poly (oxy C 1 -C 4 alkene) diol, reacted by free radical polymerization with b. 10 to 30 weight percent of a monomer mixture of 1 part by weight of a vinylaromatic and 0.1 to 9 parts of an olefinic C 2 -C 6 nitrile.
Claim 3
Dependent Claim
41 words
The polyurethane of claim 1 wherein said grafted polyol and aromatic polyisocyanate are first reacted to form a prepolymer having a free NCO in the range of 8 to 12, followed by addition of said C 2 -C 6 alkane diol.
Claim 4
Dependent Claim
51 words
The polyurethane of claim 2 wherein: said grafted polyol is composed of a 2400 to 3200 molecular weight poly (oxypropylene-ethylene) diol and a 50/50 styrene/acrylonitrile monomer mixture reacted therewith by a free radical polymerization. said aromatic polyisocyanate is MDI, and said C 2 -C 6 alkane diol is 1, 4 butanediol.
Claim 5
Dependent Claim
30 words
The polyurethane of claim 3 wherein the mixture is cast as a slab at a termperature above 210°F, cured for a few days and ground to size for injection molding.
Claim 6
Dependent Claim
12 words
An automobile exterior trim component made from the polyurethane of claim 1.