Continuous heat treating process for low carbon structural steels in bar form
Assignee: Baustahlgewebe GmbH
•
Filing: 1972-05-11
•
Granted: 1976-01-20
•
Expires: 1992-05-11
Abstract
Abstract An improvement in a process for preparing a structural steel having a maximum carbon content of 0.26 weight percent, the balance comprising iron, wherein the steel is continuously heated with the use of rapid heating, followed by quenching, the improvement comprising heating the steel only in its shell to a temperature between Acl and 1,300 DEG C such that the core heats up at an average rate of at least 100 DEG C/sec. up to a temperature between incipient pearlite transformation (Acl) and 900 DEG C, and thereafter, but prior to the attainment of equilibrium with respect to the carbon content, quenching said steel.
Inventors
- 👤 Ludwig Ettenreich
- 👤 Otto Reimann
- 👤 Klaus Greulich
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 12:39
CPC Classifications
C; C21; C21D; C21D1/00; C21D1/18; Y; Y10; Y10S; Y10S148/00; Y10S148/902
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
147 words
In a process for preparing a structural steel in which the steel is rapidly heated and thereafter quenched, said steel having a maximum carbon content of 0.26 weight percent, the balance comprising iron, the improvement which comprises heating said steel only in its shell to a temperature between its incipient pearlite transformation and 1300°C such that its core heats up at an average rate of at least 100°C/sec. to a temperature between the incipient pearlite transformation and 900°C and commencing quenching in less than 5 seconds from passing the incipient pearlite transformation point, and performing the quenching operation prior to the attainment of equilibrium with respect to the carbon content and effecting said quenching prior to reduction of the shell surface temperature to a value below 650°C, so that the more carbon rich portions are transformed to a substantially martensite free structure throughout the transverse cross-section thereof.
Claim 2
Dependent Claim
147 words
In a process for preparing a structural steel in which the steel is rapidly heated and thereafter quenched, said steel having a maximum carbon content of 0.26 weight percent, the balance comprising iron, the improvement which comprises heating said steel only in its shell to a temperature between its incipient pearlite transformation and 1300°C such that its core heats up at an average rate of at least 100°C/sec. to a temperature between the incipient pearlite transformation and 900°C and commencing quenching in less than 5 seconds from passing the incipient pearlite transformation point, and performing the quenching operation prior to the attainment of equilibrium with respect to the carbon content and effecting said quenching prior to reduction of the shell surface temperature to a value below 650°C, so that the more carbon rich portions are transformed to a substantially martensite free structure throughout the transverse cross-section thereof.
Claim 3
Dependent Claim
25 words
A process according to claim 1 wherein said steel is heated such that its core heats up at an average rate of at least 300°C/sec.
Claim 4
Dependent Claim
28 words
A process according to claim 2 wherein the quenching is initiated at the moment in which the rising core temperature is equal to the falling shell surface temperature.
Claim 5
Dependent Claim
37 words
A process according to claim 2 wherein the time of stay from the first passing of the incipient pearlite transformation point in the core to the beginning of the quenching amounts to no more than 1.5 seconds.
Claim 6
Dependent Claim
29 words
A process according to claim 1 wherein the quenching is performed by projecting or spraying water onto said steel, said water under a pressure of at least 2 atmospheres.
Claim 7
Dependent Claim
49 words
A process according to claim 1 wherein a temperature is produced in the core of said steel of at least the incipient pearlite transformation point at a shell surface temperature of up to 1,000°C and thereafter the steel is quenched at an average cooling rate of at least 800°C/sec.
Claim 8
Dependent Claim
13 words
A process according to claim 1 wherein the steel is straightened after quenching.
Claim 9
Dependent Claim
39 words
A process according to claim 1 wherein after quenching the steel is subjected to a heat treatment performed at temperatures between 100° and 380° C for a period of time sufficient to increase the elastic limit of the steel.
Claim 10
Dependent Claim
31 words
A process according to claim 8 wherein the temperature is about 340° C and the steel is maintained at such temperature for a period of time between 20 and 30 minutes.
Claim 11
Dependent Claim
23 words
A process according to claim 1 wherein the steel is in the form of a bar consisting of at least 50% pre-eutectic ferrite.
Claim 12
Dependent Claim
28 words
A process according to claim 1 wherein the steel is an unalloyed steel having a carbon content between 0.06 and 0.20 and containing quantities of manganese and silicon.
Claim 13
Dependent Claim
21 words
A process according to claim 11 wherein the unalloyed steel contains carbon in an amount between o.12 and o.22 weight percent.
Claim 14
Dependent Claim
21 words
A process according to claim 1 wherein the steel contains manganese present in an amount not greater than 1.8 weight percent.
Claim 15
Dependent Claim
17 words
A process according to claim 1 wherein the steel treated is in the form of a bar.
Claim 16
Dependent Claim
18 words
A process according to claim 14 wherein the bar has a diameter of between 4 and 36 millimeters.
Claim 17
Dependent Claim
17 words
A process according to claim 15 wherein the bar has a diameter between 6 and 16 millimeters.
Claim 18
Dependent Claim
19 words
A process according to claim 1 wherein the steel comprises between 20 and 70 % cold shaped bar material.
Claim 19
Dependent Claim
20 words
A process according to claim 17 wherein the amount of cold shaped bar material is between 30 and 50 %.
Claim 20
Dependent Claim
16 words
A process according to claim 1, wherein the more carbon rich portions are transformed into troostite.
Claim 21
Dependent Claim
16 words
A process as claimed in claim 3, wherein the temperature is selected between 750° and 850°C.
References Cited (Backward Citations)
US1946876A
Cited
US3756870A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-01-19 | 1979-07-21 | 1980-01-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-01-19 | 1983-07-21 | 1984-01-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-01-19 | 1987-07-21 | 1988-01-20 | $7700.00 | Window Closed / Lapsed |