Method and converter for refining pig-iron into steel
Assignee: Kloeckner CRA Patent GmbH
•
Filing: 1972-12-15
•
Granted: 1976-01-13
•
Expires: 1992-12-15
Abstract
Abstract Pig-iron is refined into steel by blowing oxygen and a protective screen of an encasing gas through injecting means located at or near the bottom of a converter containing a melt of molten metal. The encasing gas while protecting the injecting means, allows it to be consumed at substantially the same rate as the bottom of the converter so that the injecting means is not left projecting from the bottom of the converter. The encasing gas can be one which is inert to the melt or the metal of the injecting means or both, or it can be a gas which reacts sluggishly with the melt or the material of the oxygen feed pipe or both. Desirably, the oxygen jet is circular in cross-section and the encasing gas is in the form of a concentric jet. A converter for carrying out the method is made up of a pear-shaped sheet-steel casing having a refractory lining and an inserted bottom provided with nozzles in the form of metal tubes for the oxygen and encasing gas. Preferably, a substantial portion (for example about half) of the converter bottom is free of nozzles. The nozzles can be arranged in groups and there can be rows running parallel with the tilting axis of the converter. The nozzles may also be arranged to cause circulation of the molten metal in the converter. The nozzles can be constructed to provide for swirling movement of the encasing gas. Examples of encasing gas which may be used are hydrogen, nitrogen, noble-gases, carbon monoxide, carbon dioxide, ammonia, hydrogen-fluoride, furnace-mouth gas, coke-oven gas, natural gas and other gases containing hydrocarbons.
Inventors
- 👤 Helmut Knuppel
- 👤 Karl Brotzmann
- 👤 Hans-Georg Fassbinder
- 👤 Guy Savard
- 👤 Robert Lee
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 22:44
CPC Classifications
C; C21; C21C; C21C5/00; C21C5/28; C21C5/30; C21C5/34
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
167 words
A process for refining steel comprising: a. adding to a refractory lined steelmaking vessel a charge comprising a mixture of hot metal and solid steel scrap, said scrap being in an amount of at least about 20% by weight of charged metal; b. introducing into said charge at least one stream of oxygen through at least one chromium steel injector, said injector extending through the refractory lining and terminating substantially at the surface of the refractory lining and in contact with and below the surface of the liquid metal charge; surrounding each such injector with a protective jacket fluid comprising a hydrocarbon and introducing said fluid into said charge; controlling the amount of said fluid with respect to each said oxygen stream to maintain the wear rate of each such injector substantially equal to the wear rate of the adjacent refractory lining while refining the charge to a desired extent; c. tapping the refined steel; and d. repeating the above steps for at least about 200 times.
Claim 2
Dependent Claim
167 words
A process for refining steel comprising: a. adding to a refractory lined steelmaking vessel a charge comprising a mixture of hot metal and solid steel scrap, said scrap being in an amount of at least about 20% by weight of charged metal; b. introducing into said charge at least one stream of oxygen through at least one chromium steel injector, said injector extending through the refractory lining and terminating substantially at the surface of the refractory lining and in contact with and below the surface of the liquid metal charge; surrounding each such injector with a protective jacket fluid comprising a hydrocarbon and introducing said fluid into said charge; controlling the amount of said fluid with respect to each said oxygen stream to maintain the wear rate of each such injector substantially equal to the wear rate of the adjacent refractory lining while refining the charge to a desired extent; c. tapping the refined steel; and d. repeating the above steps for at least about 200 times.
Claim 3
Dependent Claim
26 words
The process of claim 1 wherein said scrap is in an amount of from at least about 20% to about 35% by weight of charged metal.
Claim 4
Dependent Claim
26 words
The process of claim 1 wherein said scrap is in an amount of from at least about 28% to about 35% by weight of charged metal.
Claim 5
Dependent Claim
26 words
The process of claim 1 wherein said scrap is in an amount of from at least about 30% to about 35% by weight of charged metal.
Claim 6
Dependent Claim
20 words
The process of claim 1 wherein said scrap is in an amount of about 35% by weight of charged metal.
Claim 7
Dependent Claim
30 words
The process of claim 1 wherein said hydrocarbon includes at least one member selected from the group consisting of methane, propane, butane, natural gas, coke oven gas, and light oil.
Claim 8
Dependent Claim
10 words
The process of claim 1 wherein said hydrocarbon includes propane.
Claim 9
Dependent Claim
11 words
The process of claim 1 wherein said hydrocarbon includes natural gas.
Claim 10
Dependent Claim
16 words
The process of claim 1 wherein said oxygen is under a pressure of about 5-10 atmospheres.
Claim 11
Dependent Claim
20 words
The process of claim 1 wherein said steel injectors have a chromium content of from about 15 to about 25%.
Claim 12
Dependent Claim
21 words
The process of claim 1 wherein said steel injectors have a chromium content of from about 15 to about 18% chromium.
Claim 13
Dependent Claim
193 words
The process of claim 1 wherein at least one of the repetitions of the steel refining includes: a. adding to a refractory lined steelmaking vessel a charge comprising a mixture of hot metal and solid steel scrap, said scrap being in an amount of at least about 20% by weight of charged metal; b. introducing into said charge at least one stream of oxygen through at least one chromium steel injector, said injector extending through the refractory lining and terminating substantially at the surface of the refractory lining and in contact with and below the surface of the liquid metal charge; surrounding each such injector with a protective jacket fluid comprising a hydrocarbon and introducing said fluid into said charge; controlling the amount of said fluid with respect to each said oxygen stream to maintain the wear rate of each such injector substantially equal to the wear rate of the adjacent refractory lining while refining the charge to a desired extent; c. thereafter introducing into the charge through said injectors a scavenger gas for reducing the hydrogen content of said charge during the terminal portion of refining; and d. tapping the refined steel.
Claim 14
Dependent Claim
13 words
The process of claim 12 wherein said scavenger gas includes nitrogen or argon.
Claim 15
Dependent Claim
11 words
The process of claim 12 wherein said scavenger gas is nitrogen.
Claim 16
Dependent Claim
11 words
The process of claim 12 wherein said scavenger gas is argon.
Claim 17
Dependent Claim
22 words
The process of claim 1 wherein at least one said injector extends through the side wall of said refractory lined steelmaking vessel.
Claim 18
Dependent Claim
209 words
A process for refining steel comprising: a. adding to a refractory lined steelmaking vessel a charge comprising a mixture of hot metal and solid steel scrap, said scrap being in an amount of from at least about 20% to about 35% by weight of charged metal; b. introducing into said charge at least one stream of oxygen through at least one chromium steel injector, said injector extending through the refractory lining and terminating substantially at the surface of the refractory lining and in contact with and below the surface of the liquid metal charge, said steel injectors having a chromium content of from about 15 to about 25%; surrounding each such injector with a protective jacket fluid comprising a hydrocarbon and introducing said fluid into said charge wherein said hydrocarbon includes at least one member selected from the group consisting of methane, propane, butane, natural gas, coke oven gas and light oil; controlling the amount of said fluid with respect to each said oxygen stream to maintain the wear rate of each such injector substantially equal to the wear rate of the adjacent refractory lining while refining the charge to a desired extent; c. tapping the refined steel; and d. repeating the above steps up to about 200 times.
Claim 19
Dependent Claim
209 words
A process for refining steel comprising: a. adding to a refractory lined steelmaking vessel a charge comprising a mixture of hot metal and solid steel scrap, said scrap being in an amount of from at least about 20% to about 35% by weight of charged metal; b. introducing into said charge at least one stream of oxygen through at least one chromium steel injector, said injector extending through the refractory lining and terminating substantially at the surface of the refractory lining and in contact with and below the surface of the liquid metal charge, said steel injectors having a chromium content of from about 15 to about 25%; surrounding each such injector with a protective jacket fluid comprising a hydrocarbon and introducing said fluid into said charge wherein said hydrocarbon includes at least one member selected from the group consisting of methane, propane, butane, natural gas, coke oven gas and light oil; controlling the amount of said fluid with respect to each said oxygen stream to maintain the wear rate of each such injector substantially equal to the wear rate of the adjacent refractory lining while refining the charge to a desired extent; c. tapping the refined steel; and d. repeating the above steps up to about 200 times.
Claim 20
Dependent Claim
41 words
The process for refining steel of claim 17 including during at least one of the repetitions of step (d): introducing through said injectors a scavenger gas for reducing the hydrogen content of said charge during the terminal portion of said refining.
Claim 21
Dependent Claim
13 words
The process of claim 1 wherein said charge comprises a pig iron-chromium alloy.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-01-12 | 1979-07-14 | 1980-01-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-01-12 | 1983-07-14 | 1984-01-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-01-12 | 1987-07-14 | 1988-01-13 | $7700.00 | Window Closed / Lapsed |