Mold release method for polyurethane integral-skin foam
Assignee: Aerojet Rocketdyne Holdings Inc
•
Filing: 1974-09-09
•
Granted: 1976-01-06
•
Expires: 1994-09-09
Abstract
Abstract In molding polyurethane integral-skin foam the foam tends to stick to the mold surface. Conventional mold release agents have not been found effective; they fail to provide full release of the molded product, are not durable enough to withstand more than one molding cycle, interfere with development of the integral skin, or plate onto the integral-skin thus necessitating solvent washing of the molded foam product. This invention is a method of preparing a mold to release flexible polyurethane integral-skin foam, free from skin damage and other defects, that is durable, i.e., that will permit many molding cycles before requiring replacement, and that permits the molded foam to be merely water washed to remove all traces of the mold release agent.
Inventors
- 👤 Charles D. Lindberg
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 17:25
CPC Classifications
B; B29; B29C; B29C44/00; B29C44/02; B29C44/04; B29C33/00; B29C33/56; B29C33/60; B29K; B29K2075/00; B29K2105/00; B29K2105/04; B29K2105/043; Y; Y10; Y10S; Y10S264/00; Y10S264/14
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
118 words
A method of preparing a mold to release flexible polyurethane integral skin foam comprising: a. applying a continuous coating of a fused polytetrafluoroethylene polymer to the mold surfaces; b. applying a thin film of a liquid mixture comprising (by weight) from 1 to 10 parts of a hydrocarbon wax having a melting point of from about 200° to 220°F., an acid number of about zero, and a saponification number of about zero, from 7 to 26 parts of sodium di(2-ethylhexyl) sulfosuccinate, and from 330 to 300 parts of a solvent for said wax and said sodium di(2-ethylhexyl) sulfosuccinate over said coating; and, c. drying said film prior to injecting the mixture of foam reactants into the said mold.
Claim 2
Independent Claim
118 words
A method of preparing a mold to release flexible polyurethane integral skin foam comprising: a. applying a continuous coating of a fused polytetrafluoroethylene polymer to the mold surfaces; b. applying a thin film of a liquid mixture comprising (by weight) from 1 to 10 parts of a hydrocarbon wax having a melting point of from about 200° to 220°F., an acid number of about zero, and a saponification number of about zero, from 7 to 26 parts of sodium di(2-ethylhexyl) sulfosuccinate, and from 330 to 300 parts of a solvent for said wax and said sodium di(2-ethylhexyl) sulfosuccinate over said coating; and, c. drying said film prior to injecting the mixture of foam reactants into the said mold.
Claim 3
Dependent Claim
14 words
The method of claim 1 wherein said melting point of said wax is 210°F.
Claim 4
Independent Claim
160 words
A method of molding flexible polyurethane integral-skin foam, free of surface pinholes and ruptures, comprising: a. applying a continuous coating of a fused polytetrafluoroethylene polymer to the mold surfaces; b. applying a thin film of a liquid mixture comprising (by weight) from 1 to 10 parts of a hydrocarbon wax having a melting point of from about 200° to 220°F., an acid number of about zero, and a saponification number of about zero, from 7 to 26 parts of sodium di(2-ethylhexyl) sulfosuccinate, and from 330 to 300 parts of a solvent for said wax and said sodium di(2-ethylhexyl) sulfosuccinate over said coating; c. drying said film, d. injecting a mixture of flexible polyurethane foam reactants into said mold containing said dried film to react and produce an integral skin foam; e. curing said integral-skin foam in said mold; f. removing said cured integral-skin foam from said mold; and, g. washing said foam with water to remove traces of said mixture.
Claim 5
Independent Claim
160 words
A method of molding flexible polyurethane integral-skin foam, free of surface pinholes and ruptures, comprising: a. applying a continuous coating of a fused polytetrafluoroethylene polymer to the mold surfaces; b. applying a thin film of a liquid mixture comprising (by weight) from 1 to 10 parts of a hydrocarbon wax having a melting point of from about 200° to 220°F., an acid number of about zero, and a saponification number of about zero, from 7 to 26 parts of sodium di(2-ethylhexyl) sulfosuccinate, and from 330 to 300 parts of a solvent for said wax and said sodium di(2-ethylhexyl) sulfosuccinate over said coating; c. drying said film, d. injecting a mixture of flexible polyurethane foam reactants into said mold containing said dried film to react and produce an integral skin foam; e. curing said integral-skin foam in said mold; f. removing said cured integral-skin foam from said mold; and, g. washing said foam with water to remove traces of said mixture.
References Cited (Backward Citations)
US2902376A
Cited
US3046177A
Cited
US3165567A
Cited
US3101244A
Cited
US3210448A
Cited
US3413390A
Cited
US3523918A
Cited
US3341646A
Cited
US3492394A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-01-05 | 1979-07-07 | 1980-01-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-01-05 | 1983-07-07 | 1984-01-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-01-05 | 1987-07-07 | 1988-01-06 | $7700.00 | Window Closed / Lapsed |