Abstract Improved flameproof moulding compositions, which are based on polyolefins and made from a pulverulent blend comprising a polyolefin as its essential ingredient and a plurality of flame-retardant ingredients. The flame-retardant ingredients comprise red phosphorus and at least one organic nitrogen compound which carbonizes after inflammation. The moulding compositions contain the flame-retardant ingredients in a total proportion of at most about 30 weight %. Red phosphorus and organic nitrogen compound are used in a quantitative ratio between 99:1 and 1:99. The improved moulding compositions contain as a stabilizer A. between about 1 and 10 weight % of amidosulfonic acid or ammonium bisulfate, based on the total quantity of the flame-retardant ingredients, or B. between about 5 and 15 weight % of a paraffin oil having a density between about 0.83 and 0.88 g/cc and a viscosity between about 15 and 380 centipoises, or of a mineral oil boiling within the range 170° and 350°C, or of a silicon oil, based on the quantity of red phosphorus, or C. between about 20 and 50 weight % of pentaerythritol, based on the quantity of organic nitrogen compound.
Improved flameproof moulding composition, comprising a pulverulent blend of a polyolefin and a plurality of flame retardants consisting of, in addition to red phosphorus, at least one organic nitrogen compound, selected from the group consisting of melamine and polyacrylonitrile, the amount of flame retardants being about 10-3o weight % of said composition, the quantitative ratio of red phosphorus and the organic nitrogen compound being 3o:7o - 7o:3o, the improved moulding composition containing as a stabilizer a. between about 1 and 1o weight % of amidosulfonic acid or ammonium bisulfate, based on the total quantity of the flame-retardant, or b. between about 5 and 15 weight % of a paraffin oil having a density between about o.83 and o.88 g/cc and a viscosity between about 15 and 38o centipoises, or of a mineral oil boiling within the range 17o and 35°C, or of a silicon oil, based on the quantity of red phosphorus, or c. between about 2o and 5o weight % of pentaerythritol, based on the quantity of organic nitrogen compound, or d. mixtures of (a) and (b).
Claim 2
Dependent Claim
178 words
Improved flameproof moulding composition, comprising a pulverulent blend of a polyolefin and a plurality of flame retardants consisting of, in addition to red phosphorus, at least one organic nitrogen compound, selected from the group consisting of melamine and polyacrylonitrile, the amount of flame retardants being about 10-3o weight % of said composition, the quantitative ratio of red phosphorus and the organic nitrogen compound being 3o:7o - 7o:3o, the improved moulding composition containing as a stabilizer a. between about 1 and 1o weight % of amidosulfonic acid or ammonium bisulfate, based on the total quantity of the flame-retardant, or b. between about 5 and 15 weight % of a paraffin oil having a density between about o.83 and o.88 g/cc and a viscosity between about 15 and 38o centipoises, or of a mineral oil boiling within the range 17o and 35°C, or of a silicon oil, based on the quantity of red phosphorus, or c. between about 2o and 5o weight % of pentaerythritol, based on the quantity of organic nitrogen compound, or d. mixtures of (a) and (b).
Claim 3
Dependent Claim
22 words
The moulding composition as claimed in claim 1, containing a mixture of the (a) and (b) stabilizers in a ratio of 2:5.