Dental alloy
Assignee: Dentsply Research and Development Corp
•
Filing: 1974-05-23
•
Granted: 1975-10-28
•
Expires: 1994-05-23
Abstract
Abstract A base metal alloy is described comprised primarily of nickel and chromium with minor amounts of niobium, tin, molybdenum, boron, and silicon, which has outstanding physical properties with the melting temperature being low enough for the alloy to be used advantageously as a substitute for precious metals and metal alloys, generally and specifically, in the fabrication of a wide variety of dental prosthetic appliances.
Inventors
- 👤 Charles R Manning
- 👤 Mitchell W Haller
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 11:25
CPC Classifications
C; C22; C22C; C22C19/00; C22C19/03; C22C19/05; C22C19/051; C22C19/055; A; A61; A61K; A61K6/00; A61K6/80; A61K6/84; A61L; A61L27/00; A61L27/02; A61L27/04; A61L27/047
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
8 words
A dental alloy consisting essentially of (by weight):
Claim 2
Dependent Claim
8 words
A dental alloy consisting essentially of (by weight):
Claim 3
Dependent Claim
13 words
The alloy of claim 1 containing additionally between about 0.5 to 5.0% aluminum.
Claim 4
Dependent Claim
99 words
A nickel-chromium alloy having a melting point in the range of from about 2,100*F to 2,500*F, an ultimate strength of over about 80,000 psi, a yield strength of at least 50,000 psi, and a coefficient of thermal expansion in the range of from about 13.0 X 10-6 in/in/*C to about 15.0 X 10-6 in/in/*C and consisting essentially of (by weight): from about 8 to 25% chromium, from about 0.5 to 3.5% silicon, from about 0.1 to 1.0% boron and further comprising from about 0.5 to about 5% each of tin and molybdenum, with or without 0.5% to 5.0* niobium.
Claim 5
Dependent Claim
99 words
A nickel-chromium alloy having a melting point in the range of from about 2,100*F to 2,500*F, an ultimate strength of over about 80,000 psi, a yield strength of at least 50,000 psi, and a coefficient of thermal expansion in the range of from about 13.0 X 10-6 in/in/*C to about 15.0 X 10-6 in/in/*C and consisting essentially of (by weight): from about 8 to 25% chromium, from about 0.5 to 3.5% silicon, from about 0.1 to 1.0% boron and further comprising from about 0.5 to about 5% each of tin and molybdenum, with or without 0.5% to 5.0* niobium.
Claim 6
Dependent Claim
42 words
The alloy of claim 3 comprising from about 10 to 16% chromium, from about 73 to 85% nickel, from about 0.5 to 3.0% silicon, from about 0.1 to 1.0% boron and from about 0.5 to 5% each of tin, molybdenum and niobium.
Claim 7
Dependent Claim
13 words
The alloy of claim 4 containing additionally between about 0.5 and 3.0% aluminum.
Claim 8
Dependent Claim
10 words
The alloy of claim 4 containing additionally about 1.0% aluminum.
Claim 9
Dependent Claim
37 words
An alloy suitable for use in the fabrication of dental prosthetics consisting of essentially (by weight) at least 76.6% nickel, 12% chromium, 3% tin, 3% molybdenum, 2% silicon, 3% niobium, 0.3% boron and less than 0.1% carbon.
Claim 10
Dependent Claim
37 words
An alloy suitable for use in the fabrication of dental prosthetics consisting of essentially (by weight) at least 76.6% nickel, 12% chromium, 3% tin, 3% molybdenum, 2% silicon, 3% niobium, 0.3% boron and less than 0.1% carbon.
Claim 11
Dependent Claim
49 words
DENTAL WORK CONTAINING DENTAL PORCELAIN FUSED TO A METAL CASTING, SAID CASTING CONSISTING ESSENTIALLY OF (BY WEIGHT): AN ALLOY OF 65 - 85% NICKEL, 10 - 25% CHROMIUM, 0.5 - 5.0% TIN, 1.0 - 8.0% MOLYBDENUM, 0.5 - 3.5%, SILICON, 1.0 - 5.0% NIOBIUM AND 0.1 - 1.0% BORON.
Claim 12
Dependent Claim
49 words
DENTAL WORK CONTAINING DENTAL PORCELAIN FUSED TO A METAL CASTING, SAID CASTING CONSISTING ESSENTIALLY OF (BY WEIGHT): AN ALLOY OF 65 - 85% NICKEL, 10 - 25% CHROMIUM, 0.5 - 5.0% TIN, 1.0 - 8.0% MOLYBDENUM, 0.5 - 3.5%, SILICON, 1.0 - 5.0% NIOBIUM AND 0.1 - 1.0% BORON.
Claim 13
Dependent Claim
17 words
The dental work of claim 8 wherein said alloy contains additionally between about 0.5 to 5.0% aluminum.
References Cited (Backward Citations)
US2936229A
Cited
US3437480A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1978-10-27 | 1979-04-28 | 1979-10-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1982-10-27 | 1983-04-28 | 1983-10-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1986-10-27 | 1987-04-28 | 1987-10-28 | $7700.00 | Window Closed / Lapsed |