Process for preparing of creep resistant pressure-sensitive resins
Assignee: Monsanto Co
•
Filing: 1973-02-20
•
Granted: 1975-09-02
•
Expires: 1993-02-20
Abstract
Abstract A process comprising solution interpolymerizing a pressuresensitive resin containing an acid-epoxy monomer system, formulating the interpolymer solution with the 1,3bis(dimethylamino)-2-hydroxypropane and coating the solution on a substrate to obtain a film of pressure-sensitive resin thereon. The pressure-sensitive film possesses cohesive strength and exhibits low release values from silicone coated release paper.
Inventors
- 👤 Donald M Gardner
- 👤 Lawrence W Mckenna
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 13:11
CPC Classifications
C; C09; C09J; C09J163/00; C08; C08G; C08G59/00; C08G59/18; C08G59/40; C08G59/62; C08G59/64; C08K; C08K5/00; C08K5/16; C09J133/00; C09J133/04; C09J133/06; C09J133/062; C09J133/068; C09J7/00; C09J7/20; C09J7/21; C09J7/30; C09J7/38; C08L; C08L2666/00; C08L2666/28; C08L2666/36; Y; Y10; Y10T; Y10T428/00; Y10T428/28; Y10T428/2852; Y10T428/287; Y10T428/2878; Y10T428/2891; Y10T428/31504; Y10T428/31511; Y10T428/31652; Y10T428/31663; Y10T428/31855; Y10T428/31931
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
36 words
A PROCESS OF MANUFACTURE OF A PRESSURE-SENSITIVE ADHESIVE COATED ARTICLE WHICH IS READILY RELEASED FROM SILICONE RELEASE SURFACES AND WHICH PROVIDES BONDS OF HIGH COHESIVE STRENGTH, COMPRISING: A.POLYMERIZING IN AN ORGANIC SOLVENT MEDIUM AN INTERPOLYMER CONTAINING:
Claim 2
Dependent Claim
36 words
A PROCESS OF MANUFACTURE OF A PRESSURE-SENSITIVE ADHESIVE COATED ARTICLE WHICH IS READILY RELEASED FROM SILICONE RELEASE SURFACES AND WHICH PROVIDES BONDS OF HIGH COHESIVE STRENGTH, COMPRISING: A.POLYMERIZING IN AN ORGANIC SOLVENT MEDIUM AN INTERPOLYMER CONTAINING:
Claim 3
Dependent Claim
14 words
BETWEEN 0.1 AND 15 WEIGHT PER CENT OF AN A,B-ETHYLEICALLY UNSATURATED ALIPHATIC CARBOXYLIC ACID,
Claim 4
Dependent Claim
14 words
BETWEEN 0.1 AND 15 WEIGHT PER CENT OF AN A,B-ETHYLEICALLY UNSATURATED ALIPHATIC CARBOXYLIC ACID,
Claim 5
Dependent Claim
25 words
BETWEEN 0.1 AND 2 WEIGHT PER CENT OF A GLYCIDYL MONOMER SELECTED FROM THE GROUP CONSISTING OF GLYCIDYL ACRYLATE, GLYCIDYL METHACRYLATE AND ALLYL GLYCIDYL ETHER,
Claim 6
Dependent Claim
25 words
BETWEEN 0.1 AND 2 WEIGHT PER CENT OF A GLYCIDYL MONOMER SELECTED FROM THE GROUP CONSISTING OF GLYCIDYL ACRYLATE, GLYCIDYL METHACRYLATE AND ALLYL GLYCIDYL ETHER,
Claim 7
Dependent Claim
64 words
The process of claim 1 wherein the Alpha , Beta -ethylenically unsaturated aliphatic carboxylic acid is selected from the group consisting of acrylic acid, methacrylic acid, crotonic acid, isocrotonic acid, maleic acid, fumaric acid, citraconic acid, itaconic acid, and the alkyl monoesters of maleic acid, fumaric acid, citraconic acid and itaconic acid in which the alkyl group contains from 1 to 4 carbon atoms.
Claim 8
Dependent Claim
25 words
between 0.1 and 2 weight per cent of a glycidyl monomer selected from the group consisting of glycidyl acrylate, glycidyl methacrylate and allyl glycidyl ether,
Claim 9
Dependent Claim
25 words
between 0.1 and 2 weight per cent of a glycidyl monomer selected from the group consisting of glycidyl acrylate, glycidyl methacrylate and allyl glycidyl ether,
Claim 10
Dependent Claim
31 words
between 35 to 84.9 weight per cent of a monomer selected from the group consisting of esters of acrylic acid and methacrylic acid containing from 6 to 20 carbon atoms, and
Claim 11
Dependent Claim
31 words
between 35 to 84.9 weight per cent of a monomer selected from the group consisting of esters of acrylic acid and methacrylic acid containing from 6 to 20 carbon atoms, and
Claim 12
Dependent Claim
21 words
The process of claim 1 wherein the Alpha , Beta -ethylenically unsaturated aliphatic carboxylic acid is acrylic acid or methacrylic acid.
Claim 13
Dependent Claim
31 words
BETWEEN 35 TO 84.9 WEIGHT PER CENT OF A MONOMER SELECTED FROM THE GROUP CONSISTING OF ESTERS OF ACRYLIC ACID AND METHACRYLIC ACID CONTAINING FROM 6 TO 20 CARBON ATOMS, AND
Claim 14
Dependent Claim
31 words
BETWEEN 35 TO 84.9 WEIGHT PER CENT OF A MONOMER SELECTED FROM THE GROUP CONSISTING OF ESTERS OF ACRYLIC ACID AND METHACRYLIC ACID CONTAINING FROM 6 TO 20 CARBON ATOMS, AND
Claim 15
Dependent Claim
97 words
OPTIONALLY, A MONOMER SELECTED FROM THE GROUP CONSISTING OF A-OLEFINS CONTAINING FROM 2 TO 10 CARBON TOMS, VINYL ESTERS OF ALKANOIC ACIDS CONTAINING FROM 3 TO 10 CARBON ATOMS, ETHYL AND MTHYL ESTERS OF ACRYLIC AND METHACRYLIC ACIDS, ACRYLONITRILE, METHACRYLONITRILE, STYRENE AND VINYL CHLORIDE, WHEREIN THE INTERPOLYMER HAS A WEIGHT AVERAGE MOLECULAR WEIGHT IN THE RANGE OF 10.000 TO 500,000 AND A GLASS TRANSITION TEMPERATURE IN THE RANGE OF -15* TO -75*C., AND B. ADDING BETWEEN 0.01 AND 1.0 PARTS OF THE 1,3-BIS(DIMETHYLAMINO)-2-HYDROXYPROPANE PER 100 PARTS OF INTERPOLYMER, AND C. COATING THE INTERPOLYMER SOLUTION ON THE ARTICLE.
Claim 16
Dependent Claim
97 words
OPTIONALLY, A MONOMER SELECTED FROM THE GROUP CONSISTING OF A-OLEFINS CONTAINING FROM 2 TO 10 CARBON TOMS, VINYL ESTERS OF ALKANOIC ACIDS CONTAINING FROM 3 TO 10 CARBON ATOMS, ETHYL AND MTHYL ESTERS OF ACRYLIC AND METHACRYLIC ACIDS, ACRYLONITRILE, METHACRYLONITRILE, STYRENE AND VINYL CHLORIDE, WHEREIN THE INTERPOLYMER HAS A WEIGHT AVERAGE MOLECULAR WEIGHT IN THE RANGE OF 10.000 TO 500,000 AND A GLASS TRANSITION TEMPERATURE IN THE RANGE OF -15* TO -75*C., AND B. ADDING BETWEEN 0.01 AND 1.0 PARTS OF THE 1,3-BIS(DIMETHYLAMINO)-2-HYDROXYPROPANE PER 100 PARTS OF INTERPOLYMER, AND C. COATING THE INTERPOLYMER SOLUTION ON THE ARTICLE.
Claim 17
Dependent Claim
12 words
The process of claim 1 wherein the glycidyl monomer is glycidyl methacrylate.
Claim 18
Dependent Claim
98 words
optionally, a monomer selected from the group consisting of Alpha -olefins containing from 2 to 10 carbon atoms, vinyl esters of alkanoic acids containing from 3 to 10 carbon atoms, ethyl and methyl esters of acrylic and methacrylic acids, acrylonitrile, methacrylonitrile, styrene and vinyl chloride, wherein the interpolymer has a weight average molecular weight in the range of 10,000 to 500,000 and a glass transition temperature in the range of -15* to -75*C.; and B. adding between 0.01 and 1.0 parts of the 1,3-bis(dimethylamino)-2-hydroxypropane per 100 parts of interpolymer; and C. coating the interpolymer solution on the article.
Claim 19
Dependent Claim
98 words
optionally, a monomer selected from the group consisting of Alpha -olefins containing from 2 to 10 carbon atoms, vinyl esters of alkanoic acids containing from 3 to 10 carbon atoms, ethyl and methyl esters of acrylic and methacrylic acids, acrylonitrile, methacrylonitrile, styrene and vinyl chloride, wherein the interpolymer has a weight average molecular weight in the range of 10,000 to 500,000 and a glass transition temperature in the range of -15* to -75*C.; and B. adding between 0.01 and 1.0 parts of the 1,3-bis(dimethylamino)-2-hydroxypropane per 100 parts of interpolymer; and C. coating the interpolymer solution on the article.
Claim 20
Dependent Claim
13 words
The process of claim 1 wherein the article is silicone coated release paper.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1978-09-01 | 1979-03-03 | 1979-09-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1982-09-01 | 1983-03-03 | 1983-09-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1986-09-01 | 1987-03-03 | 1987-09-02 | $7700.00 | Window Closed / Lapsed |