US3864149A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of coating workpieces with thermoplastic synthetic resins
Assignee: GEA Group AG
•
Filing: 1973-06-29
•
Granted: 1975-02-04
•
Expires: 1993-06-29
Abstract
Abstract A process for coating a workpiece with a synthetic resin comprising the steps of adhering particles of a thermally fusible synthetic resin to the workpiece to form a layer thereon and thereafter smoothing the layer and fusing the particles into a continuum by treating the workpiece with a high-molecular-weight sulfuric acid-treated and/or bleaching-earth-treated liquid hydrocarbon nonreactive with the synthetic resin and at a temperature above the melting point of the synthetic resin; the liquid hydrocarbon has a viscosity at 100*C greater than 10 cSt.
Inventors
- 👤 Werner Scheiber
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 16:54
CPC Classifications
B; B05; B05D; B05D3/00; B05D3/02; B05D3/0254; B05D3/007; B05D1/00; B05D1/18; B05D1/22; B05D1/24
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
131 words
A PROCESS FOR COATING A WORKPIECE WITH A THERMALLYFUSIBLE SYNTHETIC RESIN COMPRISING THE STEPS OF: A. HEATING A WORKPIECE TO AT LEAST THE SOFTENING TEMPERATURE OF SAID RESIN; B. ADHERING PARTICLES OF SAID SYNTHETIC RESIN TO THE WORKPIECE BY CONTACTING THE HEATED WORKPIECE WITH SAID PARTICLES TO FORM A ROUGH FRITTED LAYER OF SAID PARTICLES ON SAID WORKPIECE; C. THEREAFTER COALESCING AND SMOOTHING SAID LAYER AND FUSING SAID PARTICLES INTO A CONTINUUM BY TREATING THE WORKPIECE WITH SAID LAYER ADHERENT THERETO WITH A HIGH-MOLECULARWEIGHT LIQUID HYDROCARBON IN WHICH SAID SYNTHETIC RESIN IS INSOLUBLE AT A TEMPERATURE ABOVE THE SOFTENING POINT OF SAID SYNTHETIC RESIN, SAID LIQUID HYDROCARBON HAVING A VISCOSITY AT 100*C GREATER THAN 10 CST; AND D. THEREAFTER COOLING THE SYNTHETIC-RESIN LAYER BY TREATING IT WITH WATER FOLLOWING STEP (C).
Claim 2
Dependent Claim
131 words
A PROCESS FOR COATING A WORKPIECE WITH A THERMALLYFUSIBLE SYNTHETIC RESIN COMPRISING THE STEPS OF: A. HEATING A WORKPIECE TO AT LEAST THE SOFTENING TEMPERATURE OF SAID RESIN; B. ADHERING PARTICLES OF SAID SYNTHETIC RESIN TO THE WORKPIECE BY CONTACTING THE HEATED WORKPIECE WITH SAID PARTICLES TO FORM A ROUGH FRITTED LAYER OF SAID PARTICLES ON SAID WORKPIECE; C. THEREAFTER COALESCING AND SMOOTHING SAID LAYER AND FUSING SAID PARTICLES INTO A CONTINUUM BY TREATING THE WORKPIECE WITH SAID LAYER ADHERENT THERETO WITH A HIGH-MOLECULARWEIGHT LIQUID HYDROCARBON IN WHICH SAID SYNTHETIC RESIN IS INSOLUBLE AT A TEMPERATURE ABOVE THE SOFTENING POINT OF SAID SYNTHETIC RESIN, SAID LIQUID HYDROCARBON HAVING A VISCOSITY AT 100*C GREATER THAN 10 CST; AND D. THEREAFTER COOLING THE SYNTHETIC-RESIN LAYER BY TREATING IT WITH WATER FOLLOWING STEP (C).
Claim 3
Dependent Claim
27 words
The process defined in claim 1 wherein said synthetic resin is selected from the group which consists of polyesters, polyvinylchlorides, vinylchloride-vinylacetate mixed polymers and copolymers, and polyamides.
Claim 4
Dependent Claim
15 words
The process defined in claim 1 wherein said water in step (d) is weakly alkaline.
Claim 5
Dependent Claim
16 words
The process defined in claim 3 wherein said water in step (d) further includes a detergent.
Claim 6
Dependent Claim
55 words
The process defined in claim 4 wherein said hydrocarbon is a naphthene-based or paraffin-based petrolEum cut recovered by vacuum distillation, is treated with concentrated sulfuric acid and bleaching earth, has at 100*C a kinematic viscosity of 15 to 50 cSt, and has a neutralization coefficient prior to treatment of about 0.01 to 0.5 mg KOH/g.
Claim 7
Dependent Claim
45 words
The process defined in claim 5 wherein said hydrocarbon is provided in an upper portion and said water is provided in a lower portion of a column through which said workpiece is caused to fall freely, first contacting said hydrocarbon and then contacting said water.
Claim 8
Dependent Claim
34 words
The process defined in claim 6 wherein said upper portion of said column has a height sufficient to maintain the duration of fall of the workpiece through said hydrocarbon between 10 and 40 seconds.
Claim 9
Dependent Claim
48 words
The process defined in claim 7, further comprising the step of heating said upper portion of said column substantially to a temperature in the melting range of said synthetic resin and cooling said lower portion of said column to maintain the same at a temperature of substantially 20*C.
Claim 10
Dependent Claim
28 words
The process defined in claim 8 wherein said particles are adhered to said workpiece by heating said workpiece and introducing the heated workpiece into gas entraining said particles.
References Cited (Backward Citations)
US2138578A
Cited
US2515489A
Cited
US2684553A
Cited
US2651811A
Cited
US2771378A
Cited
US2783165A
Cited
US3282725A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1978-02-03 | 1978-08-05 | 1979-02-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1982-02-03 | 1982-08-05 | 1983-02-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1986-02-03 | 1986-08-05 | 1987-02-04 | $7700.00 | Window Closed / Lapsed |