Process for manufacture of flame retardant polyester
Assignee: Akzona Inc
•
Filing: 1972-12-07
•
Granted: 1975-01-07
•
Expires: 1992-12-07
Abstract
Abstract Polyester is made flame retardant by incorporating therein flame retardants, such as cyclophosphazene additives, prior to polycondensation, at ester interchange and in an amount of from about 1 percent to about 20 percent by weight; a preferred range is from 5 to 15 percent.
Inventors
- 👤 Gerald Willard Mcneely
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 16:20
CPC Classifications
C; C08; C08K; C08K5/00; C08K5/49; C08K5/5399
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
86 words
IN THE PROCESS OF PREPARING POLYESTER POLYMER BY ESTER INTERCHANGE AND POLYCONDENSATION, THE IMPROVEMENT WHEREIN FLAME RETARDED POLYESTER POLYMER IS PREPARED BY ADDING FROM 1 TO 20 PERCENT BY WEIGHT OF A THERMALLY AND CHEMICALLY STABLE CYCPHOSPHAZENE DERIVATIVE AT THE BEGINNING OF ESTER INTERCHANGE, SAID DERIVATIVE BEING SELECTED FROM THE GROUP CONSISTING OF CYCLOTRI- AND CYCLOTETRAPHOSPHAZENE HAVING, RESPECTIVELY, 6 OR 8 SUBSTITUENTS THEREON SELECTED FROM THE GROUP CONSISTING OF PHENYL OR PHENOXY SAID CYCLOPHOSPHANZENE DERIVATIVE BEING THERMALLY AND CHEMICALLY STABLE AT TEMPERATURES UP TO ABOUT 300*C.
Claim 2
Dependent Claim
86 words
IN THE PROCESS OF PREPARING POLYESTER POLYMER BY ESTER INTERCHANGE AND POLYCONDENSATION, THE IMPROVEMENT WHEREIN FLAME RETARDED POLYESTER POLYMER IS PREPARED BY ADDING FROM 1 TO 20 PERCENT BY WEIGHT OF A THERMALLY AND CHEMICALLY STABLE CYCPHOSPHAZENE DERIVATIVE AT THE BEGINNING OF ESTER INTERCHANGE, SAID DERIVATIVE BEING SELECTED FROM THE GROUP CONSISTING OF CYCLOTRI- AND CYCLOTETRAPHOSPHAZENE HAVING, RESPECTIVELY, 6 OR 8 SUBSTITUENTS THEREON SELECTED FROM THE GROUP CONSISTING OF PHENYL OR PHENOXY SAID CYCLOPHOSPHANZENE DERIVATIVE BEING THERMALLY AND CHEMICALLY STABLE AT TEMPERATURES UP TO ABOUT 300*C.
Claim 3
Dependent Claim
22 words
Process according to claim 1 wherein said cyclophosphazene is added in an amount of from about 5 to about 15 weight percent.
Claim 4
Dependent Claim
41 words
In the process of preparing polyester polymer by ester interchange and polycondensation, the improvement wherein flame retarded polyester polymer is prepared by adding from 1 to 20 percent by weight hexaphenoxycyclotriphosphazene as flame retardant additive at the beginning of ester interchange.
Claim 5
Dependent Claim
41 words
In the process of preparing polyester polymer by ester interchange and polycondensation, the improvement wherein flame retarded polyester polymer is prepared by adding from 1 to 20 percent by weight hexaphenoxycyclotriphosphazene as flame retardant additive at the beginning of ester interchange.
Claim 6
Dependent Claim
23 words
A process according to claim 3 wherein said hexaphenoxycyclotriphosphazene flame retardant is added in an amount from 5 to 15 percent by weight.
References Cited (Backward Citations)
US2853517A
Cited
US3322859A
Cited
US3392214A
Cited
US3316330A
Cited
US3356769A
Cited
US3446763A
Cited
US3280222A
Cited
US3450799A
Cited
US3505087A
Cited
US3624024A
Cited
US3629365A
Cited
US3792117A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1978-01-06 | 1978-07-08 | 1979-01-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1982-01-06 | 1982-07-08 | 1983-01-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1986-01-06 | 1986-07-08 | 1987-01-07 | $7700.00 | Window Closed / Lapsed |