Fiber-reinforced calcium silicate hydrate insulation
Assignee: Johns Manville Corp
•
Filing: 1973-08-06
•
Granted: 1974-12-24
•
Expires: 1993-08-06
Abstract
Abstract An improved process is described for the ''''preautoclaved'''' production of calcium silicate hydrate thermal insulation. The improvement comprises the incorporation into the slurry of calcium silicate hydrate crystals 1-10 weight percent of poly(ethylene terephthalate) fibers of defined size. An improved insulation product containing these fibers is also described. In a preferred form, the slurry and product also contain glass fiber.
Inventors
- 👤 S Benner
- 👤 K Greene
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 20:37
CPC Classifications
C; C04; C04B; C04B16/00; C04B16/04; C04B16/06; C04B16/0675; C04B16/0683; C04B28/00; C04B28/18; Y; Y02; Y02P; Y02P40/00; Y02P40/60
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
104 words
IN A PROCESS FOR REACTING LIME AND A SILICEOUS MATERIAL UNDER HYDROTHERMAL CONDITIONS IN AQUEOUS SOLUTION TO PRODUCE AN AQUEOUS SLURRY OF CALCIUM SILICATE HYDRATE CRYSTALS, WITH SUBSEQUENT MOLDING OF THE CRYSTALS TO A DESIRED SHAPE AND DRYING OF THE SHAPE-MOLDED PRODUCT TO FORM A SHAPED OBJECT OF LIGHT WEIGHT CALCIUM SILICATE HYDRATE SUITABLE FOR USE AS THERMAL INSULATION, THE IMPROVEMENT WHICH COMPRISES INCORPORATING INTO SAID AQUEOUS SLURRY OF CALCIUM SILICATE HYDRATE CRYSTALS 1 TO 10% BY WEIGHT BASED ON SOLIDS OF POLY(ETHYLENE TEREPHTHALATE) FIBERS, SAID FIBERS HAVING A LENGTH OF FROM 1/8 TO 1 INCH AND A DENIER OF FROM 0.5 TO 5.
Claim 2
Dependent Claim
104 words
IN A PROCESS FOR REACTING LIME AND A SILICEOUS MATERIAL UNDER HYDROTHERMAL CONDITIONS IN AQUEOUS SOLUTION TO PRODUCE AN AQUEOUS SLURRY OF CALCIUM SILICATE HYDRATE CRYSTALS, WITH SUBSEQUENT MOLDING OF THE CRYSTALS TO A DESIRED SHAPE AND DRYING OF THE SHAPE-MOLDED PRODUCT TO FORM A SHAPED OBJECT OF LIGHT WEIGHT CALCIUM SILICATE HYDRATE SUITABLE FOR USE AS THERMAL INSULATION, THE IMPROVEMENT WHICH COMPRISES INCORPORATING INTO SAID AQUEOUS SLURRY OF CALCIUM SILICATE HYDRATE CRYSTALS 1 TO 10% BY WEIGHT BASED ON SOLIDS OF POLY(ETHYLENE TEREPHTHALATE) FIBERS, SAID FIBERS HAVING A LENGTH OF FROM 1/8 TO 1 INCH AND A DENIER OF FROM 0.5 TO 5.
Claim 3
Dependent Claim
26 words
The improved process of claim 1 wherein said fibers are incorporated into said slurry in an amount of 1.5 to 6 weight percent based on solids.
Claim 4
Dependent Claim
28 words
The improved process of claim 1 wherein said fibers are of a length of from 1/4 to 1/2 inch and of a denier of from 1 to 3.
Claim 5
Dependent Claim
59 words
The improved process of claim 1 wherein the improvement further comprises incorporating into said slurry glass fibers in an amount of up to 7 percent by weight based on solids, with said poly(ethylene terephthalate) fibers being incorporated in an amount such that the total fiber content of said slurry is 1 to 10 percent by weight based on solids.
Claim 6
Dependent Claim
30 words
The improved process of claim 4 wherein said glass fibers have a length in the range of 1/8 to 1 inch and a diameter of from 5 to 15 microns.
Claim 7
Dependent Claim
24 words
The improved process of claim 4 wherein said glass fibers are present as 2 to 7 weight percent of the slurry based on solids.
Claim 8
Dependent Claim
52 words
In a shaped object comprising calcium silicate hydrate and suitable as a thermal insulation, the improvement which comprises the inclusion in said object of 1 to 10 weight percent of poly(ethylene terephthalate) fibers, said fibers having a length of from 1/8 to 1 inch and a denier of from 0.5 to 5.
Claim 9
Dependent Claim
52 words
In a shaped object comprising calcium silicate hydrate and suitable as a thermal insulation, the improvement which comprises the inclusion in said object of 1 to 10 weight percent of poly(ethylene terephthalate) fibers, said fibers having a length of from 1/8 to 1 inch and a denier of from 0.5 to 5.
Claim 10
Dependent Claim
57 words
In the improved product of claim 7 wherein the improvement further comprises the inclusion in said object of up to 7 weight percent of glass fiber, and said poly(ethylene terephthalate) fiber being present in an amount such that the total fiber content of said object is in the range of from 1 to 10 percent by weight.
Claim 11
Dependent Claim
25 words
In the improved object of claim 8, the improvement further comprising said glass fiber being present as 2 to 7 weight percent of said object.
References Cited (Backward Citations)
US3501323A
Cited
US3679446A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1977-12-23 | 1978-06-24 | 1978-12-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1981-12-23 | 1982-06-24 | 1982-12-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1985-12-23 | 1986-06-24 | 1986-12-24 | $7700.00 | Window Closed / Lapsed |