Phenolic resin-isocyanate trimerization product and friction material containing the same
Assignee: Federal Mogul Bremsbelag GmbH
•
Filing: 1970-05-18
•
Granted: 1973-04-03
•
Expires: 1990-05-18
Abstract
Abstract At least one isocyanurate derivative is added to polymer or polymer mixtures as a stabilizing agent, preferably prior to molding and setting the blend. The isocyanurate derivative may be added in the form of an emulsion or dispersion in a liquid vehicle. An improved friction material contains an isocyanate derivative and a trimerization catalyst acting to react said isocyanate to said isocyanurate, in admixture with an organic binding agent comprising a phenolic resin and inorganic or organic fillers and, if desired, a natural or synthetic rubber.
Inventors
- 👤 F Popp
- 👤 W Reinbek
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 13:45
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/70; C08G18/72; C08G18/77; C08G18/78; C08G18/79; C08G18/791; C08G18/794; C08G18/28; C08G18/40; C08G18/54; C08G18/542; C08K; C08K5/00; C08K5/16; C08K5/34; C08K5/3467; C08K5/3477
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
11 words
A polymer as claimed in claim 1, in which R is
Claim 2
Dependent Claim
26 words
A stabilized polymer consisting essentially of a cured blend of a phenolic resin polymer and acrylonitrile-butadiene-copolymer and a cross-linked polyisocyanurate compound characterized by the repeating group
Claim 3
Dependent Claim
39 words
A friction material consisting essentially of a phenolic resin binder through which are dispersed fillers which impart thereto wear resistance and a desired coefficient of friction, and a dispersion of a cross-linked polyisocyanurate compound characterized by the repeating group
Claim 4
Dependent Claim
84 words
A friction material consisting essentially of, in approximate percentage by weight: phenol-Novolak polymeric resin 4.47 cresol-resol polymeric resin 6.93 4,4''-diphenylmethane- diisocyanate trimerizedwith a mixture of tertiary phenolic amines 3.32 a member selected from the group consisting of zinc oxide, aluminum silicate, calcium carbonate, barium sulphate and a mixture thereof 36.56 asbestos, short fibers 16.62 asbestos, impregnated with a said polymeric resin 13.11 a member selected from the group consisting of graphite and molybdenum disulphide 3.31 premixture of 20% acrylo- nitrile-butadiene-copolymer and inorganic filler 15.68
Claim 5
Dependent Claim
49 words
A friction material consisting essentially of, in approximate percentage by weight: phenol-Novolak 2 cresol-resol 5.5 4,4''-diphenylmethane- diisocyanate trimerized with a mixture of tertiary phenolic amines 2.5 asbestos, short fibers 10 asbestos, long fibers 10 KNO3 1.5 Ca(OH)2 1.5 premixture of 20% acrylo-nitrile-butadiene-copolymer and inorganic filler 50 inorganic filler 17
Claim 6
Dependent Claim
41 words
A friction material consisting essentially of, in approximate percentage by weight: phenol-Novolak 6.58 cresol-resol 6.79 4,4''-diphenylmethane- diisocyanate trimerized with a mixture of tertiary phenolic amines 6.63 asbestos, short fibers 20 asbestos, long fibers 20 KNO3 2.5 Ca(OH)2 2 inorganic filler 35.5.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1976-04-02 | 1976-10-02 | 1977-04-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1980-04-02 | 1980-10-02 | 1981-04-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1984-04-02 | 1984-10-02 | 1985-04-03 | $7700.00 | Window Closed / Lapsed |