Process for graft polymerization onto organic macromolecular materials
Assignee: Furukawa Electric Co Ltd
•
Filing: 1969-09-10
•
Granted: 1973-02-13
•
Expires: 1989-09-10
Abstract
Abstract A process for graft polymerization of monomers onto organic macromolecular solid materials which comprises activating a macromolecular shaped article having a specific surface area of less than 3800 cm2/g with ozone under a condition of any point of the area defined by straight lines connecting p1, c1, c10, p10 in the attached FIG. 1, and further bringing said ozone activated material into contact with one or more radical polymerizable monomers in the presence of one or more members selected from the group consisting of trimethylamine, propylamine, ethylenediamine, piperidine, piperazine, morpholine, ethanolamine, hydroxyethyl ethylenediamine, pyridine, formamide and dimethyl formamide.
Inventors
- 👤 K Hosoda
- 👤 N Hoshino
- 👤 Y Kadowaki
- 👤 E Oda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 12:23
CPC Classifications
C; C08; C08F; C08F291/00; C08F291/18; C08F291/185
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
111 words
A process for graft polymerization of monomers onto organic macromolecular solid materials, which consists essentially of activating a macromolecular solid material having a specific surface area of less than 3800 cm2/g with ozone under a condition of any point of the area defined by the straight lines connecting p1, c1, c10, p10 in FIG. 1 to produce ozone activated solid materials, and further bringing said ozone activated solid materials into contact with a material consisting essentially of one or more radical polymerizable monomers in the presence of one or more members selected from the group consisting of trimethylamine, propylamine, ethylenediamine, piperidine, piperazine, morpholine, ethanolamine, hydroxy-ethyl ethylenediamine, pyridine, formamide and dimethyl formamide.
Claim 2
Dependent Claim
111 words
A process for graft polymerization of monomers onto organic macromolecular solid materials, which consists essentially of activating a macromolecular solid material having a specific surface area of less than 3800 cm2/g with ozone under a condition of any point of the area defined by the straight lines connecting p1, c1, c10, p10 in FIG. 1 to produce ozone activated solid materials, and further bringing said ozone activated solid materials into contact with a material consisting essentially of one or more radical polymerizable monomers in the presence of one or more members selected from the group consisting of trimethylamine, propylamine, ethylenediamine, piperidine, piperazine, morpholine, ethanolamine, hydroxy-ethyl ethylenediamine, pyridine, formamide and dimethyl formamide.
Claim 3
Dependent Claim
16 words
A process as claimed in claim 1 wherein the ozone is present in the gas phase.
Claim 4
Dependent Claim
16 words
A process as claimed in claim 1 wherein the ozone is present in a liquid medium.
Claim 5
Dependent Claim
20 words
A process as claimed in claim 1 wherein the ozone is preheated to a temperature of between 60* and 200*C.
Claim 6
Dependent Claim
20 words
A process as claimed in claim 1 wherein the concentration of the ozone is 0.1 to 10 percent by volume.
Claim 7
Dependent Claim
47 words
A process as claimed in claim 1 wherein the organic macromolecular shaped article is brought into contact with the monomer and simultaneously with one or more members selected from the group consisting of trimethylamine, propylamine, ethylenediamine, piperidine, piperazine, morpholine, ethanolamine, hydroxy-ethyl ethylenediamine, pyridine, formamide and dimethyl formamide.
Claim 8
Dependent Claim
42 words
A process as claimed in claim 1 wherein the radical polymerizable monomer and one or more members selected from the group consisting of trimethylamine, propylamine, ethylenediamine, piperidine, piperazine, morpholine, ethanolamine, hydroxy-ethyl ethylenediamine, pyridine, formamide and dimethyl formamide are in the gaseous state.
Claim 9
Dependent Claim
42 words
A process as claimed in claim 1 wherein the radical polymerizable monomer and one or more members selected from the group consisting of trimethylamine, propylamine, ethylenediamine, piperidine, piperazine, morpholine, ethanolamine, hydroxy-ethyl ethylenediamine, pyridine, formamide and dimethyl formamide are in the liquid state.
Claim 10
Dependent Claim
49 words
A process as claimed in claim 1 wherein any one or more members selected from the group consisting of trimethylamine, propylamine, ethylenediamine, piperidine, piperazine, morpholine, ethanolamine, hydroxy-ethyl ethylenediamine, pyridine, formamide and dimethyl formamide are brought into contact with the organic macromolecular solid material prior to contact with said monomer.
Claim 11
Dependent Claim
32 words
A process as claimed in claim 1 wherein the organic macromolecular solid material is preheated so as to heat the surface of the article to a temperature of between 60* and 200*C.
Claim 12
Dependent Claim
45 words
A process as claimed in claim 1 wherein the radical polymerizable monomers are one or more members selected from the group consisting of styrene, vinyl chloride, vinylidene chloride, acrylonitrile, methacrylonitrile, acrylic acid, methacrylic acid, methyl methacrylate, acrylamide, vinylpyridine, methyl vinylpyridine, vinylpyrollidone, ethylene, butadiene and isoprene.
Claim 13
Dependent Claim
53 words
A process as claimed in claim 1 wherein the organic macromolecular solid material is made of low density polyethylene and said low density polyethylene is brought into contact with ozone under a condition selected from any point within the area defined by the straight lines connecting p2, c2, c6, p6 in FIG. 1.
Claim 14
Dependent Claim
53 words
A process as claimed in claim 1 wherein the organic macromolecular solid material is made of high density polyethylene and said high density polyethylene is brought into contact with ozone under a condition selected from any point within the area defined by the straight lines connecting p4, c4, c7, p7 in FIG. 1.
Claim 15
Dependent Claim
49 words
A process as claimed in claim 1 wherein the organic macromolecular solid material is made of polypropylene and said polypropylene is brought into contact with ozone under a condition selected from any point within the area defined by the straight lines connecting p5, c5, c9, p9 in FIG. 1.
Claim 16
Dependent Claim
51 words
A process as claimed in claim 1 wherEin the organic macromolecular solid material is made of polyvinyl chloride and said polyvinyl chloride is brought into contact with ozone under a condition selected from any point within the area defined by the straight lines connecting p3, c3, c8, p8 in FIG. 1.
Claim 17
Dependent Claim
20 words
A process as claimed in claim 1 wherein the organic macromolecular solid material is made of a synthetic addition polymer.
Claim 18
Dependent Claim
25 words
A process as claimed in claim 16 wherein the synthetic addition polymer is selected from the group consisting of polyethylene, polypropylene, polyvinyl chloride and polytetrafluoroethylene.
Claim 19
Dependent Claim
20 words
A process as claimed in claim 1 wherein the organic macromolecular solid material is made of a synthetic condensation polymer.
Claim 20
Dependent Claim
26 words
A process as claimed in claim 18 wherein the condensation polymer is selected from the group consisting of polyethylene terephthalate, polyhexamethylene adipamide and poly- epsilon -caprolactam.
Claim 21
Dependent Claim
18 words
A process as claimed in claim 1 wherein the radical polymerizable monomers are mixed with radical copolymerizable monomers.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1976-02-13 | 1976-08-14 | 1977-02-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1980-02-13 | 1980-08-14 | 1981-02-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1984-02-13 | 1984-08-14 | 1985-02-13 | $7700.00 | Window Closed / Lapsed |