Method for producing poly{60 -olefins

Assignee: JNC Corp
•
Filing: 1970-09-04
•
Granted: 1972-06-13
•
Expires: 1990-09-04
📄 Original PDF 🌐 Google Patents 🔄 Sync Now

Abstract

Abstract Polypropylene or copolymer of propylene with another Alpha olefin is produced by polymerizing propylene or propylene together with another Alpha -olefin, at a temperature below 80* C, in the presence of a three component catalyst system consisting of TiCl3 or TiCl3.1/3AlCl3, a trialkylaluminum or dialkylaluminum halide, and polyethyleneglycol dialkylether or polyethylenethioglycol dialkylthioether, and substantially in the absence of any solvent, whereby a number of advantages can be obtained such as not only the exemption from usual drawbacks of solvent polymerization, for example, solvent loss, increase of cost necessary for solvent recovery, etc.; but also the fact that the product can be used directly to molding without removing amorphous polypropylene (APP); increase in polymerization rate; no formation of appreciable atactic polymer is the copolymerization of propylene; higher bulk density of the product; easy removal of catalyst; etc.

Inventors

  • 👤 Shiro Konotsune
  • 👤 Atsuyuki Kachi
  • 👤 Takao Tonoike
  • 👤 Kinya Mori

Bibliographic Details

Application Number —
Jurisdiction US
Data Source google_patents
Last Synchronized 2026-10-29 11:54
CPC Classifications
C; C08; C08F; C08F10/00; Y; Y10; Y10S; Y10S526/00; Y10S526/902

Claims Analysis

Total Claims: 9
Claim 1
Independent Claim 24 words
A method for producing polypropylene according to claim 1 wherein said dialkylaluminum is selected from the group consisting of diethylaluminum chloride and diisobutylaluminum chloride.
Claim 2
Dependent Claim 34 words
A method for producing polypropylene according to claim 1 wherein said ether is selected from the group consisting of diethyleneglycol dimethylether, triethyleneglycol dimethylether, tetraethyleneglycol dimethylether, tetraethyleneglycol diethylether, diethylenethioglycol dimethylthioether, triethylenethioglycol dimethylthioether, and tetraethylenethioglycol diethylthioether.
Claim 3
Dependent Claim 21 words
The method of claim 1 wherein the mole ratio of said ether to said titanium member is from 0.001:1 to 0.3:1.
Claim 4
Dependent Claim 16 words
The method of claim 1 which is carried out in the absence of an inert diluent.
Claim 5
Independent Claim 164 words
A method for producing predominantly crystalline copolymers of propylene with another Alpha -olefin which comprises polymerizing propylene together with another Alpha -olefin in the liquid phase at a temperature below 80* C., in the presence of a three component catalyst system which consists of TiCl3. 1/3 AlCl3, dialkylaluminum halides wherein said alkyl has one to four carbon atoms and said halide is selected from chloride and bromide, and an ether selected from the group consisting of polyethyleneglycol dialkylethers and polyethylenethioglycol dialkylthioethers wherein said polyethyleneglycol or polyethylenethioglycol has two to five ethylene units and said alkyl has one to four carbon atoms, wherein the mole ratio of said dialkylaluminum halides to said TiCl3. 1/3 AlCl3 is at least 1:1, and the mole ratio of said ether to said TiCl3. 1/3 AlCl3 is up to 0.5:1; and in the absence of an inert diluent or in the presence of only as much inert diluent as is required for the preparation of a slurry of the catalyst.
Claim 6
Dependent Claim 31 words
A method for producing copolymers of propylene with another Alpha -olefin according to claim 6 wherein said dialkylaluminum halide is selected from the group consisting of diethylaluminum chloride and diisobutylaluminum chloride.
Claim 7
Dependent Claim 36 words
A method for producing copolymers of propylene according to claim 6 wherein said ether is selected from the group consisting of diethyleneglycol dimethylether, triethyleneglycol dimethylether, tetraethyleneglycol dimethylether, tetraethyleneglycol diethylether, diethylenethioglycol dimethylthioether, triethylenethioglycol dimethylthioether and tetraethylenethioglycol diethylthioether.
Claim 8
Dependent Claim 21 words
The method of claim 6 wherein the mole ratio of said ether to said titanium member is from 0.001:1 to 0.3:1.
Claim 9
Dependent Claim 16 words
The method of claim 6 which is carried out in the absence of an inert diluent.

References Cited (Backward Citations)

GB1020873A Cited
US3300457A Cited
US3182049A Cited
US3367927A Cited
US3219648A Cited

USPTO Annuity & Maintenance Windows

Annuity Stage Window Opens Payment Deadline Surcharge Period Until Estimated Fee Status
3.5 Years (Year 4) 1975-06-13 1975-12-13 1976-06-13 $2000.00 Window Closed / Lapsed
7.5 Years (Year 8) 1979-06-13 1979-12-13 1980-06-13 $3760.00 Window Closed / Lapsed
11.5 Years (Year 12) 1983-06-13 1983-12-13 1984-06-13 $7700.00 Window Closed / Lapsed

Assigned Categories & Tags

No categories assigned to this patent yet.

Assign Category Tag