Method for preparing solid films
Assignee: United States Department of the Navy
•
Filing: 1970-04-15
•
Granted: 1972-05-02
•
Expires: 1990-04-15
Abstract
Abstract The electrical discontinuity which appears in the temperature response of certain materials when they are in crystalline form and are at characteristic transitional temperatures is suppressed by depositing the material on a substrate which is maintained at a temperature low enough to cause the resulting film to be amorphous. Also, by utilizing temperatures on either side of the transitional temperature, for example, new and different resistivity versus temperature responses may be realized which do not inhibit the semiconductor-metal transition.
Inventors
- 👤 John D Mackenzie
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 03:45
CPC Classifications
H; H01; H01C; H01C7/00; H01C7/04; H01C7/041; C; C23; C23C; C23C14/00; C23C14/06; C23C14/08; C23C14/083; C23C14/22; C23C14/54; C23C14/541; H01B; H01B1/00; H01B1/06; H01B1/08
Claims Analysis
Total Claims: 3
Claim 1
Independent Claim
21 words
In a method as defined in claim 1, wherein said material is V2O4 and the transitional temperature is approximately 66* C.
Claim 2
Dependent Claim
21 words
In a method as defined in claim 1, whereIn said material is V2O3 and the transitional temperature is approximately -120* C.
Claim 3
Dependent Claim
52 words
A solid amorphous film of V2O4 prepared by vapor depositing said V2O4 on a substrate maintained at a temperature below approximately 66* C. during the film forming process whereby the resistivity versus temperature response of said amorphous film is linear over a temperature range which includes the crystalline transitional temperature of V2O4.
References Cited (Backward Citations)
US3483110A
Cited
US3491000A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1975-05-02 | 1975-11-01 | 1976-05-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1979-05-02 | 1979-11-01 | 1980-05-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1983-05-02 | 1983-11-01 | 1984-05-02 | $7700.00 | Window Closed / Lapsed |