Biodegradable moldable surgical material
Assignee: United States Surgical Corp
•
Filing: 1996-05-07
•
Granted: —
•
Expires: 2016-05-07
Abstract
Abstract A moldable biodegradable surgical material is made of a bioabsorbable polymer derived from hydroxyacids, lactones, carbonates, etheresters, anhydrides, orthoesters and copolymers, terpolymers and/or blends thereof, the polymer blended with at least one surface active agent selected from the group consisting of fatty acid ester and poly(oxypropylene)/poly(oxyethylene) block copolymer. In one embodiment, a leaching agent is blended with the above-mentioned surgical material. Methods of making moldable biodegradable surgical material are provided. The surgical material may be used as a moldable bone wax in connection with repair of wounds and is an adaptable aid for any appropriate surgical use, e.g., hemostat, anchor, patch etc.
Inventors
- 👤 Walter Skalla
- 👤 Steven L. Bennett
- 👤 Ying Jiang
Bibliographic Details
Application Number
—
Jurisdiction
EP
Data Source
google_patents
Last Synchronized
2026-10-25 21:18
CPC Classifications
A; A61; A61L; A61L31/00; A61L31/04; A61L31/041; A61L24/00; A61L24/001; A61L24/0036; A61L24/04; A61L24/043; A61L24/046; A61L27/00; A61L27/14; A61L27/18; A61L27/26; A61L27/50; A61L27/56; A61L31/06
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
27 words
A moldable biodegradable surgical material comprising a blend of a bioabsorbable polymer and a surface active agent selected from sorbitan fatty acid ester and poly(oxypropylene/poly(oxyethylene) block copolymer.
Claim 2
Dependent Claim
33 words
A moldable biodegradable surgical material according to claim 1 wherein the bioabsorbable polymer is derived from a member selected from hydroxyacids, lactones, carbonates, etheresters, anhydrides, esteramides, orthoesters, and copolymers, terpolymers and blends thereof.
Claim 3
Dependent Claim
28 words
A moldable biodegradable surgical material according to claim 2 wherein the bioabsorbable polymer is selected from polylactide, polyglycolide, polydioxanone, polycaprolactone, polytrimethylene carbonate and copolymers, terpolymers and blends thereof.
Claim 4
Dependent Claim
21 words
A moldable biodegradable surgical material according to claim 3 wherein the bioabsorbable polymer is a star polymer of glycolide and caprolactone.
Claim 5
Dependent Claim
33 words
A moldable biodegradable surgical material according to claim 4 wherein glycolide is present in an amount of about 9.8 weight percent and caprolactone is present in an amount of about 90.2 weight percent.
Claim 6
Dependent Claim
35 words
A moldable biodegradable surgical material according to any one of the preceding claims wherein the sorbitan fatty acid ester is present in an amount ranging from about 10 weight percent to about 90 weight percent.
Claim 7
Dependent Claim
25 words
A moldable biodegradable surgical material according to any one of the preceding claims wherein the sorbitan fatty acid ester is polyoxyethylene sorbitan fatty acid ester.
Claim 8
Dependent Claim
20 words
A moldable biodegradable surgical material according to claim 7 wherein the polyoxyethylene sorbitan fatty acid ester is polyoxyethylene sorbitan monopalmitate.
Claim 9
Dependent Claim
35 words
A moldable biodegradable surgical material according to any one of the preceding claims wherein the bioabsorbable polymer is a star polymer of glycolide and caprolactone and the sorbitan fatty acid ester is polyoxyethylene sorbitan monopalmitate.
Claim 10
Dependent Claim
34 words
A moldable biodegradable surgical material according to any one of the preceding claims wherein the poly(oxypropylene)\poly(oxyethylene) block copolymer is present in an amount ranging from about 2 weight percent to about 55 weight percent.
Claim 11
Dependent Claim
37 words
A moldable biodegradable surgical material according to any one of the preceding claims wherein the bioabsorbable material is a star polymer of glycolide and caprolactone and the poly(oxypropylene)\poly(oxyethylene) block copolymer has a molecular weight of about 7500.
Claim 12
Dependent Claim
18 words
A moldable biodegradable surgical material according to any one of the preceding claims further comprising a leaching agent.
Claim 13
Dependent Claim
24 words
A moldable biodegradable surgical material according to claim 12 wherein the leaching agent is selected from calcium triphosphate, calcium carbonate, calcium chloride and hydroxyapalite.
Claim 14
Dependent Claim
17 words
A moldable biodegradable surgical material according to any one of the preceding claims further comprising calcium triphosphate.