Patent EP0575813A2 successfully refreshed from Google Patents.
EP0575813A2
Expired / Lapsed
EP
⏱️ 0.0 years remaining
Multilayer glass ceramic substrate and process for producing the same
Assignee: NEC Corp
•
Filing: 1993-06-08
•
Granted: —
•
Expires: 2013-06-08
Abstract
Abstract A multilayer glass ceramic substrate having a plurality of conductor layers each laminated through a glass ceramic layer. The glass ceramic layer has a composition comprising of alumina, borosilicate magnesium glass and cordierite crystal produced by chemical reaction between alumina and borosilicate magnesium glass. The content of alumina is 12 to 59.6 wt%, the content of borosilicate magnesium glass is 18 to 69.6 wt%, the content of the cordierite crystal is 1 to 50 wt% and the sum of components is 100 wt%. The multilayer glass ceramic substrate shows improved mechanical strength.
Inventors
- 👤 Kazuhiro Ikuina
- 👤 Yuzo Shimada
Bibliographic Details
Application Number
—
Jurisdiction
EP
Data Source
google_patents
Last Synchronized
2026-11-09 09:24
CPC Classifications
C; C03; C03C; C03C17/00; C03C17/34; C03C17/36; C03C17/3602; C03C17/361; C03C14/00; C03C14/004; C03C17/3639; C03C17/3642; C03C3/00; C03C3/04; C03C3/076; C03C3/089; H; H10; H10W; H10W70/00; H10W70/60; H10W70/67; H10W70/69; H10W70/692; C03C2214/00; C03C2214/04; Y; Y10; Y10S; Y10S428/00; Y10S428/901; Y10T; Y10T428/00; Y10T428/24; Y10T428/24802; Y10T428/24851; Y10T428/24917; Y10T428/24926
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
86 words
A multilayer glass ceramic substrate having a plurality of conductor layers each laminated through a glass ceramic layer, characterized in that said glass ceramic layer has a composition comprising of alumina, borosilicate magnesium glass and cordierite crystal produced by chemical reaction between alumina and borosilicate magnesium glass, the content of alumina being 12 to 59.6 wt%, the content of borosilicate magnesium glass being 18 to 69.6 wt% and the content of the cordierite crystal being 1 to 50 wt%, the sum of components being 100 wt%.
Claim 2
Dependent Claim
46 words
The multilayer glass ceramic substrate set forth in claim 1 wherein said composition contain a forth component selected from a group consisting of quart glass, α-quartz and mullite, the content of said forth component being 10 to 30 wt%, the sum of components being 100 wt%.
Claim 3
Dependent Claim
94 words
A process for producing a multilayer glass ceramic substrate by the steps of mixing material powders, preparing green sheets from slurry of the mixed material powders, forming via halls in said green sheets, printing wiring conductors on said green sheets and filling said via halls with conductor, laminating a plurality printed sheets, compressing the laminated sheets under heat and then sintering compressed sheets at a temperature below 1,000°C, characterized in that said mixed material powders consist of 30 to 60 wt% of alumina powder and 70 to 40 wt% of borosilicate magnesium glass powder.
Claim 4
Dependent Claim
35 words
The process set forth in claim 3 wherein alumina powder has the average particle size of 0.5 to 3 µm and borosilicate magnesium glass powder has the average particle size of 1 to 5 µm.
Claim 5
Dependent Claim
65 words
The process set forth in claim 3 wherein a third powder selected from a group consisting of quart glass, α-quartz and mullite is added to said material powders in such proportions as 10 to 50 wt% of alumina powder, 40 to 70 wt% of borosilicate magnesium glass powder and 10 to 50 wt% of said third powder, the sum of all powders being 100 wt%.
Claim 6
Dependent Claim
21 words
The process set forth in claim 3 wherein said third powder has the average particle size of 0.5 to 10 µm.
Claim 7
Dependent Claim
32 words
The process set forth in any one of claims 3 to 6 wherein the content of magnesium in said borosilicate magnesium glass is more than 5 wt% in term of magnesium oxide.