Antistatic coating composition, manufacturing process thereof and antistatic and non-glare picture displaying screen utilizing the coating composition
Assignee: Samsung SDI Co Ltd
•
Filing: 1990-05-17
•
Granted: —
•
Expires: 2010-05-17
Abstract
Abstract An antistatic coating composition, a manufacturing process thereof, and an antistatic and non-glare picture displaying screen are disclosed. The manufacturing process for the antistatic coating composition comprises steps of forming a silicate solution by partially hydrolysing a silicate substance; forming a conductive solution containing a conductive material which is formed by doping a soluble inorganic compound and a different inorganic compound into molecular water-containing oxides or hydroxides of a soluble inorganic compound which is soluble in an organic compound and water; and mixing the silicate solution and the conductive solution, and subjecting the mixture to a hydrolysis and to a polycondensation. According to the present invention, the antistatic and non-glare effects are greatly promoted.
Inventors
- 👤 Chang-Min Sohn
- 👤 Heon-Su Kim
Bibliographic Details
Application Number
—
Jurisdiction
EP
Data Source
google_patents
Last Synchronized
2026-11-04 02:09
CPC Classifications
C; C09; C09D; C09D183/00; C09D183/14; C09K; C09K3/00; C09K3/16; C09D183/02; C09D4/00; C09D5/00; C09D5/24; C09K11/00; C09K11/08; H; H01; H01J; H01J2229/00; H01J2229/863; H01J2229/8631; H01J2229/8632
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
68 words
An antistatic coating composition comprising: a silicate solution obtained by partially hydrolysing a silicate substance; and a conductive solution containing a conductive material which is formed by doping a compound of different kind from the inorganic compound into the molecular water-containing oxides or hydroxides of the soluble inorganic compound. said silicate solution and said conductive solution being mixed to be subjected to a hydrolysis and to a polycondensation.
Claim 2
Dependent Claim
24 words
The antistatic coating composition as claimed in claim 1, wherein said hydrolysed silicate consists of alkyl silicate, a polycondensate thereof, or a mixture thereof.
Claim 3
Dependent Claim
23 words
The antistatic coating composition as claimed in claim 1, wherein said organic solvent consists of alcohol, a polarized solvent, or a mixture thereof.
Claim 4
Dependent Claim
30 words
The antistatic coating composition as claimed in claim 1, wherein said soluble inorganic compound consists of Zr, Li, Sn or In, or a combination of two or more of them.
Claim 5
Dependent Claim
37 words
The antistatic coating composition as claimed in claim 1 or 4, wherein said different inorganic compound which is different from said soluble inorganic compound consists of an Sn compound or an Sb compound, or a mixture thereof.
Claim 6
Dependent Claim
33 words
The antistatic coating composition as claimed in claim 1, wherein said hydrolysed silicate substance is contained by the amount of 1 - 20 wt% based on the total amount of said coating composition.
Claim 7
Dependent Claim
36 words
The antistatic coating composition as claimed in claim 1, wherein said conductive material in said conductive solution is contained by the amount of 0.03 - 7 w% based on the total amount of said coating composition.
Claim 8
Dependent Claim
99 words
A process for preparation of a transparent conductive solution, comprising: forming a hydroxide solution containing hydroxides of a soluble inorganic compound which is hydrated by adding a small amount of water and/or base, and by dissolving a soluble inorganic compound or a hydrate thereof; forming an opaque solution which is formed by doping said soluble inorganic compound or a different metallic compound into said molecular water-containing oxides or hydroxides of said inorganic compound, and by agitating them after adding them; and poptizing said opaque solution by adding sufficient amounts of water and acid, and by heating and agitating them.
Claim 9
Dependent Claim
21 words
The process as claimed in claim 8, wherein said soluble inorganic compound is dissolved in an organic solvant or in water.
Claim 10
Dependent Claim
31 words
The process as claimed in claim 9, wherein said soluble inorganic compound consists of a compound of Zr, Li, Sn or In, or a combination of two or more compounds thereof.
Claim 11
Dependent Claim
37 words
The process as claimed in any one of claims 8 to 10, wherein said different inorganic compound which is different from said soluble inorganic compound consists of a compound of Sn, or Sb, or a mixture thereof.
Claim 12
Dependent Claim
31 words
The process as claimed in claim 8, wherein said conductive solution is contained by the amount of 0.02 - 6 wt% based on the total amount of said transparent conductive solution.
Claim 13
Dependent Claim
119 words
An antistatic and non-glare picture displaying screen comprising: a silicate solution formed by carrying out a partial hydrolysis on a silicate material: a conductive solution including a conductive material which is formed by doping a different inorganic compound into molecular water-containing oxides or hydroxides of a soluble inorganic compound; said silicate solution and said conductive solution being mixed together, and the mixture being subjected to a hydrolysis and to a polycondensation to form an antistatic composition solution before spreading of it on the surface of the transparent panel of a picture displaying screen; and said spread composition solution being subjected to a baking at temperature of 80 - 500° C, thereby finally obtaining an antistatic and non-glare coating layer.
Claim 14
Dependent Claim
19 words
The antistatic and non-glare picture displaying screen as claimed in claim 13, wherein said transparent panel consists of glass.
Claim 15
Dependent Claim
30 words
The antistatic and non-glare picture displaying screen as claimed in claim 13, wherein said transparent panel consists of a synthetic resin, and said baking temperature is 80 - 150° C.
Claim 16
Dependent Claim
33 words
The antistatic and non-glare picture displaying screen as claimed in any one of claims 13 to 15, wherein the time period of the baking for said coating layer is 5 to 60 minutes.
Claim 17
Dependent Claim
21 words
The antistatic and non-glare picture displaying screen as claimed in claim 13, wherein said antistatic and non-glare coating layer is grounded.
Claim 18
Dependent Claim
38 words
The antistatic and non-glare picture displaying screen as claimed in claim 13, wherein the spreading of said antistatic coating composition is carried out by applying a spin coating, a dipping, or a spray coating, or a combination thereof.