Process for the preparation of modified zeolites
Assignee: Shell Internationale Research Maatschappij BV
•
Filing: 1988-04-12
•
Granted: —
•
Expires: 2008-04-12
Abstract
Abstract Process for the preparation of a modified zeolite of the Y-type by treatment with a solution of a metal salt and a calcination which comprises treating a zeolite of the Y-type having an alkali oxide/aluminium oxide molar ratio of at most 0.13 with a solution of a multi-valent metal salt having a cationic radius between 0.6 and 1.0 Å and converting the thus treated zeolite by calcination into a product having a unit cell size between 24.21 and 24.65 Å.
Inventors
- 👤 Aan Hendrik Klazinga
Bibliographic Details
Application Number
—
Jurisdiction
EP
Data Source
google_patents
Last Synchronized
2026-11-08 05:20
CPC Classifications
B; B01; B01J; B01J29/00; B01J29/04; B01J29/06; B01J29/08; B01J29/084; C; C10; C10G; C10G47/00; C10G47/02; C10G47/10; C10G47/12; C10G47/16
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
80 words
Process for the preparation of a modified zeolite of the Y-type by treatment with a solution of a metal salt and a calcination which comprises treating a zeolite of the Y-type having an alkali oxide/aluminium oxide molar ratio of at most 0.13 with a solution of a multi-valent metal salt having a cationic radius between 0.6 and 1.0 Å and converting the thus treated zeolite by calcination into a product having a unit cell size between 24.21 and 24.65 Å.
Claim 2
Dependent Claim
80 words
Process for the preparation of a modified zeolite of the Y-type by treatment with a solution of a metal salt and a calcination which comprises treating a zeolite of the Y-type having an alkali oxide/aluminium oxide molar ratio of at most 0.13 with a solution of a multi-valent metal salt having a cationic radius between 0.6 and 1.0 Å and converting the thus treated zeolite by calcination into a product having a unit cell size between 24.21 and 24.65 Å.
Claim 3
Dependent Claim
24 words
Process according to claim 1, wherein a solution of a multi-valent metal ion is used having a cationic radius between 0.60 and 0.80 Å.
Claim 4
Dependent Claim
22 words
Process according to claim 2, wherein use is made of one or more salts of gallium, iron, copper, magnesium, cobalt and nickel.
Claim 5
Dependent Claim
29 words
Process according to any one of claims 1 to 3, wherein use is made of a solution of a multi-valent metal salt having a molarity between 0.005 and 2.
Claim 6
Dependent Claim
27 words
Process according to any one of claims 1 to 4, wherein the treated zeolite is subjected to a drying treatment at a temperature up to 200 °C.
Claim 7
Dependent Claim
28 words
Process according to any one of claims 1 to 5, wherein the treated zeolite is subjected to a final calcination at a temperature between 350 and 800 °C.
Claim 8
Dependent Claim
23 words
(Catalytically active) compositions comprising a zeolite prepared in accordance with a process according to any one of the preceding claims and a binder.
Claim 9
Dependent Claim
28 words
Compositions according to claim 7 comprising also at least one hydrogenation component of a Group 6 metal and/or at least one hydrogenation component of a Group 8 metal.
Claim 10
Dependent Claim
32 words
Compositions according to claim 8 comprising one or more components of nickel and/or cobalt and one or more components of molybdenum and/or tungsten or one or more components of platinum and/or palladium.
Claim 11
Dependent Claim
22 words
Process for the hydroconversion of hydrocarbons which comprises using a catalyst composition according to one or more of claims 7 to 9.