Cook-in shrink film

Claim 2

A three layer plastic film comprising: a) a core layer of between about 60 and 90 wt. % hydrolyzed ethylene-vinyl acetate copolymer containing between about 28 and 40 wt. % ethylene and blended with between about 10 and 40 wt. % amide polymer having a melting point below about 420°F, said core layer providing an oxygen transmission rate through the film below about 90 cc/m²/mil thickness/24 hrs/Atm; b) a first outer layer directly adhered to one side of said core layer comprising a blend of ethylene-vinyl acetate containing between about 7 and 15 wt. % vinyl acetate and between about 10 and 25 wt. % linear low density polyethylene being a copolymer of C6 to C8 olefin and ethylene; and c) a second outer layer directly adhered to the other side of said core layer and comprising ethylene vinyl acetate containing between about 7 and 15 wt. % vinyl acetate; d) said film having been irradiated at a level of between about 1 and 5 MR.

Claim 3

A film according to claim 1 wherein the second outer layer is a blend of said ethylene vinyl acetate and up to about 10 wt. % linear low density polyethylene being a copolymer of C6 to C8 olefin and ethylene.

Claim 4

A film according to claim 1 wherein said amide polymer in the core layer is a Nylon 6 copolymer.

Claim 5

A film according to claim 3 wherein said Nylon 6 copolymer is Nylon 6, 66.

Claim 6

A film according to claim 3 wherein said Nylon 6 copolymer is Nylon 6, 12.

Claim 7

A film according to claim 1 wherein the core layer comprises between about 25 and 85 wt. % hydrolyzed ethylene-vinyl acetate copolymer blended with between about 15 and 25 wt. % amide polymer.

Claim 8

A film according to claim 1 wherein said hydrolyzed ethylene-vinyl acetate copolymer contains between about 32 and 38 wt. % ethylene.

Claim 9

A film according to claim 1 wherein hexene-1 is the C6 to C8 olefin in said first outer layer.

Claim 10

A film according to claim 1 wherein the oxygen transmission rate of said core layer is below about 75 cc/M²/mil thickness/24 hrs/Atm.

Claim 11

A film according to claim 1 wherein the total thickness of the three layers is between about 2.0 and 3.5 mils.

Claim 12

A film according to claim 10 wherein the thickness of said core layer is up to about 0.3 mils.

Claim 13

A film according to claim 1 wherein the ethylene-vinyl acetate of said first outer layer contains between about 9 and 12 wt. % vinyl acetate.

Claim 14

A film according to claim 1 wherein said first outer layer contains between about 15 and 20 wt. % linear low density polyethylene.

Claim 15

A film according to claim 2 wherein hexene-1 is the C6 to C8 olefin in said second outer layer.

Claim 16

A film according to claim 10 wherein the thickness of said first outer layer is between about 1.2 and 2.6 mils.

Claim 17

A film according to claim 1 wherein said second outer layer is a blend of said ethylene-­vinyl acetate and up to about 5 wt. % linear low density polyethylene being a copolymer of hexene-1 and ethylene.

Claim 18

A film according to claim 1 wherein the ethylene vinyl acetate of said second outer layer contains between about 9 and 12 wt. % vinyl acetate.

Claim 19

A film according to claim 10 wherein the thickness of said second outer layer is between about 0.3 and 1.0 mils.

Claim 20

A film according to claim 1 which is irradiated at a level of between about 2 and 4 MR.

Claim 21

A three layer plastic film comprising: a) a core layer of between about 75 and 85 wt. % hydrolyzed ethylene-vinyl acetate copolymer containing between about 32 and 38 wt. % ethylene and blended with between about 15 and 25 wt. % Nylon 6,66 copolymer, said core layer having an oxygen transmission rate below about 75 cc/M²/mil thickness/24 hrs/Atm and thickness of between about 0.05 and 0.2 mils; b) a first outer layer of thickness between about 1.2 and 2.6 mils directly adhered to one side of said core layer comprising a blend of ethylene vinyl acetate containing between about 9 and 12 wt. % vinyl acetate, and between about 15 and 20 wt. % linear low density polyethylene being a copolymer of hexene-1 and ethylene; and c) a second outer layer of thickness between about 0.3 and 1.0 mils directly adhered to the other side of said core layer and comprising a blend of ethylene-vinyl acetate containing between about 9 and 12 wt. % vinyl acetate, and up to about 5 wt. % linear low density polyethylene being a copolymer of butene-1 and ethylene; d) said film having a total thickness of between about 2.0 and 3.5 mils and having been irradiated at a level of between about 2 and 4 MR.

Claim 22

A three layer plastic film comprising: a) a core layer of between about 75 and 85 wt. % hydrolyzed ethylene-vinyl acetate copolymer containing between about 32 and 38 wt. % ethylene and blended with between about 15 and 25 wt. % Nylon 6,66 copolymer, said core layer having an oxygen transmission rate below about 75 cc/M²/mil thickness/24 hrs/Atm and thickness of between about 0.05 and 0.2 mils; b) a first outer layer of thickness between about 1.2 and 2.6 mils directly adhered to one side of said core layer comprising a blend of ethylene vinyl acetate containing between about 9 and 12 wt. % vinyl acetate, and between about 15 and 20 wt. % linear low density polyethylene being a copolymer of hexene-1 and ethylene; and c) a second outer layer of thickness between about 0.3 and 1.0 mils directly adhered to the other side of said core layer and comprising a blend of ethylene-vinyl acetate containing between about 9 and 12 wt. % vinyl acetate, and up to about 5 wt. % linear low density polyethylene being a copolymer of butene-1 and ethylene; d) said film having a total thickness of between about 2.0 and 3.5 mils and having been irradiated at a level of between about 2 and 4 MR.