Calcium phophate-coated composite material and process for production thereof
Assignee: De Nora Permelec Ltd
•
Filing: 1987-10-16
•
Granted: —
•
Expires: 2007-10-16
Abstract
Abstract A calcium phosphate-coated composite material is disclosed, comprising a metallic substrate, an oxide layer on the metallic substrate, said oxide layer consisting essentially of the oxide of one or more metals selected from the group consisting of titanium, zirconium, hafnium, niobium, tantalum, tin, cobalt, aluminum, chromium, molybdenum and tungsten, and a coating layer of calcium phosphate provided on the oxide layer. A process for production of the calcium phosphate-coated composite material is also disclosed.
Inventors
- 👤 Takayuki Shimamune
- 👤 Masashi Hosonuma
Bibliographic Details
Application Number
—
Jurisdiction
EP
Data Source
google_patents
Last Synchronized
2026-11-08 23:43
CPC Classifications
C; C23; C23C; C23C28/00; C23C28/04; A; A61; A61F; A61F2/00; A61F2/02; A61F2/28; A61L; A61L27/00; A61L27/28; A61L27/30; A61L27/32; C23C28/044; A61F2310/00; A61F2310/00389; A61F2310/00592; A61F2310/00796; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12535; Y10T428/12583; Y10T428/1259; Y10T428/12736; Y10T428/12771; Y10T428/12806
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
60 words
A calcium phosphate-coated composite material comprising a metallic substrate, an oxide layer on the metallic substrate, said oxide layer consisting essentially of an oxide of one or more metals selected from the group consisting of titanium, zirconium, hafnium, vanadium, niobium, tantalum, tin, cobalt, aluminum, chromium, molybdenum and tungsten, and a coating layer of calcium phosphate provided on the oxide layer.
Claim 2
Dependent Claim
60 words
A calcium phosphate-coated composite material comprising a metallic substrate, an oxide layer on the metallic substrate, said oxide layer consisting essentially of an oxide of one or more metals selected from the group consisting of titanium, zirconium, hafnium, vanadium, niobium, tantalum, tin, cobalt, aluminum, chromium, molybdenum and tungsten, and a coating layer of calcium phosphate provided on the oxide layer.
Claim 3
Dependent Claim
28 words
The composite material as claimed in Claim 1, wherein the metallic substrate is made of titanium and the oxide layer consists essentially of titanium oxide and tantalum oxide.
Claim 4
Dependent Claim
30 words
The composite material as claimed in Claim 1, wherein the metallic substrate is made of titanium and the oxide layer consists essentially of a composite oxide of titanium and niobium.
Claim 5
Dependent Claim
32 words
The composite material as claimed in Claim 1, wherein the metallic substrate is made of a corrosion resistant iron alloy and the oxide layer consists essentially of titanium oxide and niobium oxide.
Claim 6
Dependent Claim
82 words
A process for producing a calcium phosphate coated-composite material which comprises coating a coating solution containing one or more metals selected from the group consisting of titanium, zirconium, hafnium, vanadium, niobium, tantalum, tin, cobalt, aluminum, chromium, molybdenum and tugsten on the surface of a metallic substrate, converting the one or more metals into a corresponding oxide by heating in a oxidizing atmosphere to form an oxide layer, and then forming a coating of calcium phosphate on the surface of the oxide layer.
Claim 7
Dependent Claim
82 words
A process for producing a calcium phosphate coated-composite material which comprises coating a coating solution containing one or more metals selected from the group consisting of titanium, zirconium, hafnium, vanadium, niobium, tantalum, tin, cobalt, aluminum, chromium, molybdenum and tugsten on the surface of a metallic substrate, converting the one or more metals into a corresponding oxide by heating in a oxidizing atmosphere to form an oxide layer, and then forming a coating of calcium phosphate on the surface of the oxide layer.
Claim 8
Dependent Claim
19 words
The process as claimed in Claim 5, wherein the metallic substrate is made of titanium or a titanium alloy.
Claim 9
Dependent Claim
33 words
The process as claimed in Claim 5, wherein the metallic substrate is made of a corrosion resistant iron alloy and the coating solution is a solution containing neither halogen ions nor halogen compounds.
Claim 10
Dependent Claim
29 words
The process as claimed in Claim 5, wherein the formation of the oxide layer by heat treatment is carried out by calcinating at a temperature not less than 300°C.
Claim 11
Dependent Claim
29 words
The process as claimed in Claim 6, wherein the formation of the oxide layer by heat treatment is carried out by calcinating at a temperature not less than 300°C.
Claim 12
Dependent Claim
29 words
The process as claimed in Claim 7, wherein the formation of the oxide layer by heat treatment is carried out by calcinating at a temperature not less than 300°C.
Claim 13
Dependent Claim
33 words
The process as claimed in Claim 5, 6, 7, 8, 9 or 10, wherein the coating of calcium phosphate is carried out by plasma spray coating of calcium phosphate and/or apatite hydroxide power.
Claim 14
Dependent Claim
56 words
The process as claimed in Claim 5, 6, 7, 8, 9 or 10, wherein the coating of calcium phosphate is carried out by coating a nitric acid aqueous solution of apatite hydroxide as a coating solution on the surface of the oxide layer, and then calcining the coating solution at a temperature not less than 300°C.