EP0189163A2
Expired / Lapsed
EP
⏱️ 0.0 years remaining
Method of producing a water absorbent crosslinked polymer
Assignee: Maruha Nichiro Corp
•
Filing: 1986-01-20
•
Granted: —
•
Expires: 2006-01-20
Abstract
Abstract A water absorbent crosslinked polymer having at least 70% by weight of acrylic acid monomeric units, 60 to 90% of the carboxyl groups of which are in the form of an alkali metal salt, produced by a method in which a mixture comprised of acrylic acid, 60 to 90% of the carboxyl groups of which are in the form of an alkali metal salt, and a fibrous cellulosic material is heated in the presence of a radical initiator. The polymerization temperature can be effectively controlled by smooth evaporation of water. The crosslinked polymer can absorb such a large amount of water as several hundred times the weight of the polymer in an excellent absorption rate, and finds applications as, for example, a disposable diaper and a sanitary napkin.
Inventors
- 👤 Kazuo Saotome
Bibliographic Details
Application Number
—
Jurisdiction
EP
Data Source
google_patents
Last Synchronized
2026-10-25 07:23
CPC Classifications
D; D06; D06M; D06M14/00; D06M14/02; D06M14/04
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
225 words
A water absorbent crosslinked polymer having at least 70 % by weight, based on the total weight of said polymer, of acrylic acid monomeric units, 60 to 90 % of the carboxyl groups of said acrylic acid monomeric units being in the form of an alkali metal salt, produced by a method comprising the steps of: 1) providing an aqueous solution comprising water, at least 30 % by weight, based on the total weight of said aqueous solution, of acrylic acid as a monomeric component, 60 to 90 % of the carboxyl groups of said acrylic acid being in the form of an alkali metal salt, and a radical initiator; 2) mixing the aqueous solution with a fibrous cellulosic material to obtain an aqueous mixture, thereby enabling the water of said mixture to smoothly evaporate at heating so that when said mixture is heated in the following step 3), the maximum temperature of said mixture is controlled as a result of a balance between the heat generation due to the polymerization reaction and the heat radiation by smooth water evaporation due to the fibrous cellulosic material; 3) heating the obtained mixture to effect polymerization of said monomeric component, thereby obtaining a reaction product containing a crosslinked polymer together with the fibrous cellulosic material; and 4) subjecting said reaction product to heat drying, followed by pulverization.
Claim 2
Dependent Claim
225 words
A water absorbent crosslinked polymer having at least 70 % by weight, based on the total weight of said polymer, of acrylic acid monomeric units, 60 to 90 % of the carboxyl groups of said acrylic acid monomeric units being in the form of an alkali metal salt, produced by a method comprising the steps of: 1) providing an aqueous solution comprising water, at least 30 % by weight, based on the total weight of said aqueous solution, of acrylic acid as a monomeric component, 60 to 90 % of the carboxyl groups of said acrylic acid being in the form of an alkali metal salt, and a radical initiator; 2) mixing the aqueous solution with a fibrous cellulosic material to obtain an aqueous mixture, thereby enabling the water of said mixture to smoothly evaporate at heating so that when said mixture is heated in the following step 3), the maximum temperature of said mixture is controlled as a result of a balance between the heat generation due to the polymerization reaction and the heat radiation by smooth water evaporation due to the fibrous cellulosic material; 3) heating the obtained mixture to effect polymerization of said monomeric component, thereby obtaining a reaction product containing a crosslinked polymer together with the fibrous cellulosic material; and 4) subjecting said reaction product to heat drying, followed by pulverization.
Claim 3
Dependent Claim
28 words
A polymer according to claim 1, wherein 60 to 80 % of the carboxyl groups of said acrylic acid is in the form of an alkali metal salt.
Claim 4
Dependent Claim
24 words
A polymer according to claim 1, wherein in step 3), the mixture is heated at a temperature of about 60 to about 110 °C.
Claim 5
Dependent Claim
22 words
A polymer according to claim 3, wherein the mixture is heated at a temperature of about 80 ° to about 100 °C.
Claim 6
Dependent Claim
29 words
A polymer according to claim 1, wherein said radical initiator is employed in an amount of 0.001 to 1.0 %, based on the total weight of the aqueous solution.
Claim 7
Dependent Claim
65 words
A polymer according to claim 1, wherein the aqueous solution is mixed with the fibrous cellulosic material in an amount ratio of monomeric component to fibrous cellulosic material of 95/5 to 50/50 by weight, so that when the mixture is heated in step 3), the maximum temperature of the mixture is controlled in the range of from just above 100 °C to about 110 °C.
Claim 8
Dependent Claim
38 words
A polymer according to claim 1, wherein said aqueous solution further comprises as a monomeric component at least one member selected from the group consisting of a water soluble crosslinkable polyfunctional monomer and a water soluble copolymerizable monomer.
Claim 9
Dependent Claim
37 words
A polymer according to claim 1, wherein said aqueous solution further comprises at least one member selected from the group consisting of a water soluble post-crosslinking agent, a water soluble starch and a water soluble cellulose derivative.
Claim 10
Dependent Claim
115 words
A polymer according to claim 7, wherein said aqueous solution comprises water, 30 to 60 % by weight, based on the total weight of said aqueous solution, of acrylic acid and a water soluble copolymerizable monomer as monomeric components and a radical initiator, said copolymerizable monomer being selected from the group consisting of methacylic acid, maleic acid, fumaric acid, itaconic acid, acrylamide, methacylamide and mixtures thereof, 60 to 90 % of the carboxyl groups of each of said acrylic acid, methacylic acid, maleic acid, fumaric acid and itaconic acid being in the form of an alkali metal salt, the amount ratio of said acrylic acid to said copolymerizable monomer being at least 70/30 by weight.
Claim 11
Dependent Claim
15 words
A polymer according to claim 1, wherein said cellulosic material is a chemically purified pulp.
Claim 12
Dependent Claim
24 words
A polymer according to claim 10, wherein said chemically purified pulp is a chemically purified wood pulp or a chemically purified cotton linter pulp.
Claim 13
Independent Claim
226 words
A method of producing a water absorbent crosslinked polymer having at least 70 % by weight, based on the total weight of said polymer, of acrylic acid monomeric units, 60 to 90 % of the carboxyl groups of said acrylic acid monomeric units being in the form of an alkali metal salt, which comprises the steps of: 1) providing an aqueous solution comprising water, at least 30 % by weight, based on the total weight of said aqueous solution, of acrylic acid as a monomeric component, 60 to 90 % of the carboxyl groups of said acrylic acid being in the form of an alkali metal salt, and a radical initiator; 2) mixing the aqueous solution with a fibrous cellulosic material to obtain an aqueous mixture, thereby enabling the water of said mixture to smoothly evaporate at heating so that when said mixture is heated in the following step 3), the maximum temperature of said mixture is controlled as a result of a balance between the heat generation due to the polymerization reaction and the heat radiation by smooth water evaporation due to the fibrous cellulosic material; 3) heating the obtained mixture to effect polymerization of said monomeric component, thereby obtaining a reaction product containing a crosslinked polymer together with the fibrous cellulosic material; and 4) subjecting said reaction product to heat drying, followed by pulverization.
Claim 14
Independent Claim
226 words
A method of producing a water absorbent crosslinked polymer having at least 70 % by weight, based on the total weight of said polymer, of acrylic acid monomeric units, 60 to 90 % of the carboxyl groups of said acrylic acid monomeric units being in the form of an alkali metal salt, which comprises the steps of: 1) providing an aqueous solution comprising water, at least 30 % by weight, based on the total weight of said aqueous solution, of acrylic acid as a monomeric component, 60 to 90 % of the carboxyl groups of said acrylic acid being in the form of an alkali metal salt, and a radical initiator; 2) mixing the aqueous solution with a fibrous cellulosic material to obtain an aqueous mixture, thereby enabling the water of said mixture to smoothly evaporate at heating so that when said mixture is heated in the following step 3), the maximum temperature of said mixture is controlled as a result of a balance between the heat generation due to the polymerization reaction and the heat radiation by smooth water evaporation due to the fibrous cellulosic material; 3) heating the obtained mixture to effect polymerization of said monomeric component, thereby obtaining a reaction product containing a crosslinked polymer together with the fibrous cellulosic material; and 4) subjecting said reaction product to heat drying, followed by pulverization.
Claim 15
Dependent Claim
28 words
A method according to claim 12, wherein 60 to 80 % of the carboxyl groups of said acrylic acid is in the form of an alkali metal salt.
References Cited (Backward Citations)
No citation records indexed.
USPTO Annuity & Maintenance Windows
Maintenance schedule is calculated for granted US utility patents.