EP0172269A2
Expired / Lapsed
EP
⏱️ 0.0 years remaining
Thermoplastic resin film laminate and production thereof
Assignee: Toyobo Co Ltd
•
Filing: 1984-10-25
•
Granted: —
•
Expires: 2004-10-25
Abstract
Abstract A thermoplastic resin film laminate which comprises a thermoplastic resin film, particularly, a polyester film and a layer of a polyester resin composition provided on at least one surface of the film, said composition comprising (A) a water insoluble polyester copolymer composed of a mixed dicarboxylic acid component containing a dicarboxylic acid having metal sulfonate group in an amount of 0.5 to 15 mol % based on all the dicarboxylic acid component and a glycol component; and (B) inert particles; the weight ratio of (A)/(B)= 100 , 0 0 0 /0.5-3,0 0 0. Optionally, the composition can contain one or more ingredients selected from the group consisting of a water soluble silicone, a polyfunctional reactive compound, a polyethylene glycol and its derivative and an antistatic agent. The thermoplastic resin film laminate is preferably produced by so-called in-line coating.
Inventors
- 👤 Katsuhiko Nose
- 👤 Hajime Suzuki
- 👤 Osamu Makimura
Bibliographic Details
Application Number
—
Jurisdiction
EP
Data Source
google_patents
Last Synchronized
2026-10-26 22:31
CPC Classifications
G; G03; G03C; G03C1/00; G03C1/76; G03C1/795; G03C1/7954; C; C08; C08J; C08J7/00; C08J7/04; C08J7/0427; C08J7/043; C08J7/044; C08J7/056; C08J2467/00; Y; Y10; Y10T; Y10T428/00; Y10T428/26; Y10T428/31504; Y10T428/31786; Y10T428/31797
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
81 words
A thermoplastic resin film laminate which comprises a thermoplastic resin film and a layer of a polyester resin composition provided on at least one surface of the film, said composition comprising (A) a water insoluble polyester copolymer composed of a mixed dicarboxylic acid component containing a dicarboxylic acid having metal sulfonate group in an amount of 0.5 to 15 mol % based on the entire dicarboxylic acid component and a glycol component; and (B) inert particles; the weight ratio of (A)/(B)=100,000/0.5-3,000.
Claim 2
Dependent Claim
81 words
A thermoplastic resin film laminate which comprises a thermoplastic resin film and a layer of a polyester resin composition provided on at least one surface of the film, said composition comprising (A) a water insoluble polyester copolymer composed of a mixed dicarboxylic acid component containing a dicarboxylic acid having metal sulfonate group in an amount of 0.5 to 15 mol % based on the entire dicarboxylic acid component and a glycol component; and (B) inert particles; the weight ratio of (A)/(B)=100,000/0.5-3,000.
Claim 3
Dependent Claim
32 words
A thermoplastic resin film laminate according to claim 1, wherein the inert particles are those of an inorganic or organic compounds and have an average particle size of 0.01 to 10 microns.
Claim 4
Dependent Claim
45 words
A thermoplastic resin film laminate according to claim 1, wherein the composition further includes one or more ingredients selected from the group consisting of (E) a water soluble silicone, (F) a polyfunctional reactive compound, (G) polyethylene glycol and its derivative and (H) an antistatic agent.
Claim 5
Dependent Claim
28 words
A thermoplastic resin film laminate according to claim 3, wherein the composition contains (E) a water soluble silicone and the weight ratio of (A)/(E) is 100/0.05 to 10.
Claim 6
Dependent Claim
116 words
A thermoplastic resin film laminate according to claim 4, wherein the water soluble silicone is represented by the following formula (I) or (II) or a mixture thereof, the ratio of ethylene oxide and propylene oxide has the relation of the equation (III) and the molecular weight thereof is 500 to 20,000. or wherein R is hydrogen or lower alkyl having 1 to 4 carbon atoms, R' is lower alkyl having 1 to 4 carbon atoms, R" is hydrogen or lower alkyl, R"' is lower alkylene having 1 to 4 carbon atoms, x and a are each 0 or an integer of 1 or more and y and b are each an integer of 1 or more.
Claim 7
Dependent Claim
28 words
A thermoplastic resin film laminate according to claim 3, wherein the composition contains ,(F) a polyfunctional reactive compound and the weight ratio of (A)/(F) is 100/1 to 40.
Claim 8
Dependent Claim
29 words
A thermoplastic resin film laminate according to claim 3, wherein the composition contains (G) polyethylene glycol or its derivative and the weight ratio of (A)/(G) is 100/1 to 20.
Claim 9
Dependent Claim
27 words
A thermoplastic resin film laminate according to claim 3, wnerein the composition contains (H) an antistatic agent and the weight ratio of (A)/(G) is 100/0.1 to 15.
Claim 10
Dependent Claim
33 words
A thermoplastic resin film laminate according to claim 1, wherein the thermoplastic resin film is a melt extruded, unoriented or uniaxially oriented film and the resulting laminate is further uiaxially or biaxially oriented.
Claim 11
Dependent Claim
29 words
A thermoplastic resin film laminate according to claim 9 wherein the melt extruded, unoriented or uniaxially oriented film contains a lubricant in an amount of 300 ppm or less.
Claim 12
Dependent Claim
18 words
A thermoplastic resin film laminate according to claim 1, wherein the thermoplastic resin film is a polyester film.
Claim 13
Dependent Claim
19 words
A thermoplastic resin film laminate according to claim 11, wherein the thermoplastic resin film is a polyethylen terephthalate film.
Claim 14
Dependent Claim
156 words
A process for the production of a thermoplastic resin film laminate which comprises applying an aqueous dispersion of a polyester resin comprising (A) a water insoluble polyester copolymer composed of a mixed dicarboxylic acid component containing a dicarboxylic acid having metal sulfonate group in an amount of 0.5 to 15 mol % based on all the dicarboxylic acid component and a glycol component; (B) inert particles; (C) a water soluble organic compound having an boiling point of 60 - 200°C; (D) water; and, optionally, one or more ingredients selected from the group consisting of (E) a water soluble silicone, (F) a polyfunctional reactive compound, (G) a polyethylene glycol and its derivative and (H) an antistatic agent, the weight ratios of (A)/(B) = 100,000/0.5 - 3,000, (A)/(C) = 100/20 - 5,000 and (C)/(D) = 100/50 - 1,000, on at least one surface of a thermoplastic resin film to form a layer of a polyester resin composition thereon.
Claim 15
Dependent Claim
156 words
A process for the production of a thermoplastic resin film laminate which comprises applying an aqueous dispersion of a polyester resin comprising (A) a water insoluble polyester copolymer composed of a mixed dicarboxylic acid component containing a dicarboxylic acid having metal sulfonate group in an amount of 0.5 to 15 mol % based on all the dicarboxylic acid component and a glycol component; (B) inert particles; (C) a water soluble organic compound having an boiling point of 60 - 200°C; (D) water; and, optionally, one or more ingredients selected from the group consisting of (E) a water soluble silicone, (F) a polyfunctional reactive compound, (G) a polyethylene glycol and its derivative and (H) an antistatic agent, the weight ratios of (A)/(B) = 100,000/0.5 - 3,000, (A)/(C) = 100/20 - 5,000 and (C)/(D) = 100/50 - 1,000, on at least one surface of a thermoplastic resin film to form a layer of a polyester resin composition thereon.