Polyester-ester urethane
Assignee: DSM BV
•
Filing: 1983-08-03
•
Granted: —
•
Expires: 2003-08-03
Abstract
Abstract The invention relates to novel high molecular weight polyester-ester urethanes containing blocks of ester units of a high melting polyester and of blocks of ester units of a low melting polyester which are linked together through ester groups and/or urethane groups. The melting point of the polyester-ester urethanes is at least 150°C and when the blocks of ester units of the low melting polyester form part of less than 50% by weight of the total number of ester units the upper limit of the glass transition range Tg (e) thereof does not exceed +20°C and when said blocks of ester units of the low melting polyester form part of more than 50% by weight of the total number of ester units, the upper limit of the glass transition range Tg (e) is not higher than -5°C. The polyester- ester urethanes are prepared by reacting a high melting polyester and a low melting polyester in the molten phase, after which the resulting polyester-ester is reacted with a low molecular weight polyisocyanate. When the number of end groups of the high melting polyester and the low-melting polyester together amount to more than 700 meq per kg, the transesterification catalyst present in one or in both polyesters or polyester amides is entirely or partly deactivated before and/or during the preparation of the polyester-ester.
Inventors
- 👤 Franciscus Johannes Huntjens
- 👤 Anton Hendrikus Johannes Brouwer
Bibliographic Details
Application Number
—
Jurisdiction
EP
Data Source
google_patents
Last Synchronized
2026-11-08 04:36
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/40; C08G18/42; C08G18/4202; C08G18/4205; C08G18/4208; C08G18/4211; C08G18/4216; C08G18/60; C08G18/606
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
362 words
Polyester-ester urethane built up of polyester-ester units which are linked together by low molecular weight structural units of the formula wherein R 1 represents a polyfunctional organic group having not more than 30 carbon atoms, and p is an integer of 2 or 3, which polyesterester units are built up of blocks comprising a multiple of ester units of the formula and blocks comprising a multiple of ester units which may form a bifunctional polyester or polyester amide having a melting point not higher than 100°C, which two types of polyester units are linked together by ester bonds, with the proviso that: at least 80 mole % of the G groups in the latter formula are tetramethylene- radicals and the remaining proportion thereof are divalent radicals left after removal of hydroxyl groups from a low molecular weight diol having a molecular weight not higher than 250; at least 80 mole % of the R 2 groups are 1,4-phenylene radicals and the remaining proportion thereof are divalent radicals left after removal of carboxyl groups from a low molecular weight dicarboxylic acid having a molecular weight not higher than 300; the sum of the percentages of G groups which are not tetramethylene radicals and of the percentage of R 2 groups which are not 1,4-phenylene radicals does not exceed 20; and the ester units of the formula form 20 to 90% by weight of the polyester-ester, characterized in that the interlinked ester units of the formula and the other ester units interlinked to form a bifunctional polyester or polyester amide are present in an amount such that the melting point of the polyester-ester urethane is at least 150°C and when the blocks of ester units of the low melting polyester form part of less than 50% by weight of the total number of ester units, the upper limit of the glass transition range [Tg (e) ] thereof does not exceed +20°C and when said blocks of ester units of the low melting polyester form part of more than 50% by weight of the total number of ester units, the upper limit of the glass transition range [Tg (e) ] is not higher than -5°C.
Claim 2
Dependent Claim
362 words
Polyester-ester urethane built up of polyester-ester units which are linked together by low molecular weight structural units of the formula wherein R 1 represents a polyfunctional organic group having not more than 30 carbon atoms, and p is an integer of 2 or 3, which polyesterester units are built up of blocks comprising a multiple of ester units of the formula and blocks comprising a multiple of ester units which may form a bifunctional polyester or polyester amide having a melting point not higher than 100°C, which two types of polyester units are linked together by ester bonds, with the proviso that: at least 80 mole % of the G groups in the latter formula are tetramethylene- radicals and the remaining proportion thereof are divalent radicals left after removal of hydroxyl groups from a low molecular weight diol having a molecular weight not higher than 250; at least 80 mole % of the R 2 groups are 1,4-phenylene radicals and the remaining proportion thereof are divalent radicals left after removal of carboxyl groups from a low molecular weight dicarboxylic acid having a molecular weight not higher than 300; the sum of the percentages of G groups which are not tetramethylene radicals and of the percentage of R 2 groups which are not 1,4-phenylene radicals does not exceed 20; and the ester units of the formula form 20 to 90% by weight of the polyester-ester, characterized in that the interlinked ester units of the formula and the other ester units interlinked to form a bifunctional polyester or polyester amide are present in an amount such that the melting point of the polyester-ester urethane is at least 150°C and when the blocks of ester units of the low melting polyester form part of less than 50% by weight of the total number of ester units, the upper limit of the glass transition range [Tg (e) ] thereof does not exceed +20°C and when said blocks of ester units of the low melting polyester form part of more than 50% by weight of the total number of ester units, the upper limit of the glass transition range [Tg (e) ] is not higher than -5°C.
Claim 3
Dependent Claim
39 words
Polyester-ester urethane according to claim 1, characterized in that the proportion of low-molecular weight structural units of the formula calculated as diphenylmethane-4,4'-diisocyanate (MDI) and based on the polyester-ester urethane is in the range of 0,5 to 25% by weight.
Claim 4
Dependent Claim
27 words
Polyester-ester urethane according to claim 2, characterized in that the proportion of low-molecular weight structural units of the formula is in the range of 1 to 15.
Claim 7
Dependent Claim
24 words
Polyester-ester urethane according to one or more of the preceding claims, characterized in that the ester units of the formula are butylene terephthalate units.
Claim 8
Dependent Claim
41 words
Polyester-ester urethane according to one or more of the preceding claims, characterized in that the ester units which may form a bifunctional polyester or polyester amide having a melting point not exceeding 100°C are entirely or substantially derived from polybutylene adipate.
Claim 9
Dependent Claim
40 words
Polyester-ester urethane according to one or more of the claims 1-4, characterized in that the ester units which may form a bifunctional polyester or polyester amide having a melting point not exceeding 100°C are entirely or substantially derived from polycaprolactone.
Claim 10
Dependent Claim
176 words
A process for the preparation of a polyester-ester urethane according to one or more of the preceding claims, in which process a bifunctional polyester having a molecular weight of at least 1000 and built up of ester units of the formula wherein both G and R 2 have the same meaning as indicated in claim 1, is reacted, while in the molten phase, with a bifunctional polyester or polyester amide having a molecular weight of at least 1000 and a melting point not higher than 100°C, after which the resulting polyester-ester is reacted with a low molecular weight coupling agent of the formula wherein R 1 and p have the meaning as indicated in claim 1, in an amount, such that the ratio of the number of -NCO groups to the number of functional groups of the polyester-ester is at least 1,0 and not higher than 5, characterized in that before and/or during the preparation of the polyester-ester the transesterification catalyst present in one or in both polyesters or polyester amides is entirely or partly deactivated.
Claim 11
Dependent Claim
55 words
A process for the preparation of a polyester-ester urethane according to claim 7, characterized in that it is started from a low-melting bifunctional polyester or polyester amide having a molecular weight of 1500 to 2500 and a high-melting polyester of the formula having a molecular weight in the range of 10 000 to 25 000.
Claim 12
Dependent Claim
28 words
A process according to claim 8, characterized in that the high-melting polyester is polybutylene terephthalate having a molecular weight in the range of 15 000 to 19 000.
Claim 13
Dependent Claim
31 words
A process according to one or more of the claims 7-9, characterized in that the deactivaticn is carried out by incorporating a complexing phosphorus compound into one polyester or both polyesters.
Claim 14
Dependent Claim
32 words
A process according to claim 10, characterized in that the amount of phosphorus compound used for the deactivation corresponds to at least 0,5 phosphorus atoms per metal atom of the transesterification catalyst.
Claim 15
Dependent Claim
34 words
A process according to claim 10, characterized in that the amount of phosphorus compound used for the deactivation corresponds to at least 1 to 5 phosphorus atoms per metal atom of the transesterification catalyst.
Claim 16
Dependent Claim
22 words
A process according to one or more of the claims 10-12, characterized in that the phosphorus compound used is diethyl carbethoxymethyl phosphonate.
Claim 17
Dependent Claim
20 words
A process according to one or more of the claims 10-12, characterized in that the phosphorus compound used is tris(triethyleneglycol)phosphate.
Claim 18
Dependent Claim
32 words
A process according to one or more of the claims 10-14, characterized in that the polyester-ester is prepared at a temperature between the melting point of the highest melting component and 290°C.
Claim 19
Dependent Claim
173 words
A process for the preparation of a polyester-ester urethane according to one or more of the claims 1-6, in which process a bifunctional polyester having a molecular weight of at least 1000 and built up of ester units of the formula wherein both G and R 2 have the same meaning as indicated in claim 1, is reacted, while in the molten phase, with a bifunctional polyester or polyester amide having a molecular weight of at least 100 0 and a melting point not higher than 100°C, after which the resulting polyester-ester is reacted with a low molecular weight coupling agent of the formula wherein R, and p have the meaning given in claim 1, in an amount, such that the ratio of the number of -NCO groups to the number of functional groups of the polyester-ester is at least 1,0 and not higher than 5, characterized in that the number of end groups of the high-melting polyester and the low-melting polyester together do not amount to more than 700 meq per kg.
Claim 20
Dependent Claim
41 words
A process according to claim 16, characterized in that the number of end groups both of the high-melting polyester and of the low-melting polyester or polyester amide is in the range of 110 to 170 meq per kg in either case.
References Cited (Backward Citations)
FR2380308A1
Cited
EP0013461A1
Cited
USPTO Annuity & Maintenance Windows
Maintenance schedule is calculated for granted US utility patents.