A car stabilizer and a manufacturing method therefor
Assignee: NHK Spring Co Ltd
•
Filing: 1983-04-22
•
Granted: —
•
Expires: 2003-04-22
Abstract
Abstract A car stabilizer and a manufacturing method therefor are disclosed. In this method, a straight material of carbon steel with a carbon content of 0.10 % to 0.35 % is first directly quenched (2) by quick heating, and then bent (3) into a predetermined shape. Thereafter, the material is annealed at a low temperature of 100°C to 400°C, shot-peened (5) as required, and then coated (6). Thus, a stabilizer is obtained as a final product. The coating may be executed between the steps of quenching and bending.
Inventors
- 👤 Akira Ohno
- 👤 Kanji Inoue
Bibliographic Details
Application Number
—
Jurisdiction
EP
Data Source
google_patents
Last Synchronized
2026-10-28 19:52
CPC Classifications
C; C21; C21D; C21D9/00; C21D9/02; B; B23; B23P; B23P15/00; B60; B60G; B60G21/00; B60G21/02; B60G21/04; B60G21/05; B60G21/055; B60G21/0551; C21D1/00; C21D1/18; B23P2700/00; B23P2700/14; B60G2202/00; B60G2202/10; B60G2202/13; B60G2202/135; B60G2204/00; B60G2204/10; B60G2204/12; B60G2204/122; B60G2204/1222; B60G2204/1224; B60G2204/40; B60G2204/44; B60G2204/45; B60G2206/00; B60G2206/01; B60G2206/012; B60G2206/40; B60G2206/42; B60G2206/427; B60G2206/80
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
52 words
A method for manufacturing a car stabilizer using a straight material formed of carbon steel with a carbon content of 0.10 % to 0.35 %, comprising the steps of: (a) quenching the material by quick heating; (b) bending the material into a predetermined shape; and (c) annealing the material at low temperature.
Claim 2
Independent Claim
52 words
A method for manufacturing a car stabilizer using a straight material formed of carbon steel with a carbon content of 0.10 % to 0.35 %, comprising the steps of: (a) quenching the material by quick heating; (b) bending the material into a predetermined shape; and (c) annealing the material at low temperature.
Claim 3
Dependent Claim
17 words
The method according to claim 1, characterized in that said quick-heating quenching employs the induction hardening method.
Claim 4
Dependent Claim
24 words
The method according to claim 1 or 2, characterized in that said low-temperature annealing is executed at a processing temperature of 100°C to 400°C.
Claim 5
Dependent Claim
20 words
The method according to claim 1, characterized in that the surface of said material is coated after said low-temperature annealing.
Claim 6
Dependent Claim
23 words
The method according to claim 1, characterized in that the surface of said material is coated between said steps of quenching and bending.
Claim 7
Dependent Claim
17 words
The method according to claim 1, characterized in that said material is shot-peened after said low-temperature annealing.
Claim 8
Dependent Claim
15 words
The method according to claim 1, characterized in that said material is a pipe material.
Claim 9
Dependent Claim
19 words
A stabilizer of a manufacture prepared in accordance with the method of any one of claims 1 to 7.
References Cited (Backward Citations)
No citation records indexed.
USPTO Annuity & Maintenance Windows
Maintenance schedule is calculated for granted US utility patents.