Process for the preparation of polymer latex
Assignee: SINTEF AS
•
Filing: 1979-11-05
•
Granted: —
•
Expires: 1999-11-05
Abstract
Abstract The invention provides a process for the preparation of polymer latex. The process involves emulsification of an initiator or initiator mixture and optionally a solvent in the presence of an emulsifier in water in a first step and adding a monomer and polymerizing in a second step. The process is carried out by emulsifying an essentially water-insoluble initiator or initiator mixture in the first step at a temperature above the melting point of the initiator or initiator mixture if no solvent is used, and below its decomposition temperature, optionally together with an essentially water-insoluble liquid solvent, which forms a liquid solution together with the initiator or the initiator mixture at the emulsification temperature, then, in a second step adding the desired monomer, optionally additional emulsifier and water to a desired amount and initiating polymerization.
Inventors
- 👤 John Ugelstadt
Bibliographic Details
Application Number
—
Jurisdiction
EP
Data Source
google_patents
Last Synchronized
2026-10-27 21:43
CPC Classifications
C; C08; C08F; C08F2/00; C08F2/12; C08F2/16; C08F2/22; C08F2/24
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
159 words
A process for the preparation of a polymer latex which comprises (a) forming a pre-emulsion either by emulsifying an initiator or initiator mixture having a water-solubility of <10 -2 g/l with water in the presence of an emulsifier at a temperature above the melting point and below the decomposition temperature of the initiator or initiator mixture, or, if a liquid solvent is additionally employed having a water-solubility of<10 -2 g/1 and a molecular weight <5000 in an amount effective to form a liquid solution with the initiator or initiator mixture emulsifying said solution with water in the presence of an emulsifier at a temperature below the decomposition temperature of the initiator or initiator mixture; (b) adding to said pre-emulsion a monomer corresponding to the desired polymer, optionally additional emulsifier and water to a desired amount whereby a major portion of the monomer is absorbed by drops in the pre-emulsion containing the initiator or initiator mixture; (c) and initiating polymerisation.
Claim 2
Dependent Claim
159 words
A process for the preparation of a polymer latex which comprises (a) forming a pre-emulsion either by emulsifying an initiator or initiator mixture having a water-solubility of <10 -2 g/l with water in the presence of an emulsifier at a temperature above the melting point and below the decomposition temperature of the initiator or initiator mixture, or, if a liquid solvent is additionally employed having a water-solubility of<10 -2 g/1 and a molecular weight <5000 in an amount effective to form a liquid solution with the initiator or initiator mixture emulsifying said solution with water in the presence of an emulsifier at a temperature below the decomposition temperature of the initiator or initiator mixture; (b) adding to said pre-emulsion a monomer corresponding to the desired polymer, optionally additional emulsifier and water to a desired amount whereby a major portion of the monomer is absorbed by drops in the pre-emulsion containing the initiator or initiator mixture; (c) and initiating polymerisation.
Claim 3
Dependent Claim
21 words
A process as claimed in claim 1 wherein the initiator or initiator mixture has a water solubility of <10 -4 g/litre.
Claim 4
Dependent Claim
22 words
A process as claimed in claim 1 or claim 2 wherein the liquid solvent has a water solubility of <10 -4 g/litre.
Claim 5
Dependent Claim
43 words
A process as claimed in claim 1 or claim 2 wherein in the absence of said liquid solvent, the initiator is oil-soluble and an amount of initiator from 0.5:1000 to 2:100 based on the total amount of water in the latex is used.
Claim 6
Dependent Claim
48 words
A process as claimed in any of claims 1 to 3 wherein said liquid solvent is employed in an amount in proportion to water in the latex of 0.5:1000 to 5:100 and is present in an amount in proportion to initiator of from 0.05:1 to 10:1 by weight.
Claim 7
Dependent Claim
38 words
A process as claimed in any of claims 1 to 5 wherein an anionic,cationic or non-ionic emulsifier is employed in a total amount of from 1:1000 to 5:100 based on the total amount of water in the latex.
Claim 8
Dependent Claim
32 words
A process as claimed in any of claims 1 to 6 wherein the amount of monomer employed is from 0.5:1 to 2:1 based on the total amount of water in the latex.
Claim 9
Dependent Claim
19 words
A process as claimed in any of claims 1 to 7 wherein the monomer is vinyl chloride or styrene.
Claim 10
Dependent Claim
31 words
A process as claimed in any of claims 1 to 8 wherein said pre-emulsion is mixed with a seed of polymer particles or other emulsion prior to addition of the monomer.
References Cited (Backward Citations)
GB1492028A
Cited
FR2316252A1
Cited
FR2316251A1
Cited
BE851556A
Cited
BE857919R
Cited
US4113687A
Cited
USPTO Annuity & Maintenance Windows
Maintenance schedule is calculated for granted US utility patents.