High surface area catalysts
Assignee: ExxonMobil Technology and Engineering Co
•
Filing: 1979-11-05
•
Granted: 1982-08-17
•
Expires: 1999-11-05
Abstract
Abstract ABSTRACT OF THE DISCLOSURE High surface area metal-containing catalysts are prepared by dispersing a thermally decomposable metal compound in a hydro-carbon oil having a Conradson carbon content of up to about 50 weight percent, the thermally decomposable metal compound being added in an amount sufficient to obtain a specified ratio of atoms of Conradson carbon of the oil chargestock to atoms of metal constituent of the thermally decomposable compound, heating the compound in the presence of a gas comprising either hydrogen or hydrogen sulfide or hydrogen and hydrogen sulfide to form a solid high surface area catalyst within the oil, and recovering the resulting high surface area catalyst. The high surface area solids are suitable as catalysts, catalyst supports or catalyst components for use in hydrocarbon treating processes and in chemical processes.
Inventors
- 👤 Clyde L. Aldridge
- 👤 Roby Bearden, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
CA
Data Source
google_patents
Last Synchronized
2026-11-09 02:18
CPC Classifications
—
Claims Analysis
Total Claims: 32
Claim 1
Independent Claim
160 words
A high surface area catalyst prepared by the steps which comprise: (a) adding to a hydrocarbon oil chargestock having a Conradson carbon content up to about 50 weight percent, a thermally decomposable metal compound in an amount sufficient to provide a ratio of atoms of oil chargestock Conradson Car-bon to atoms of metal constituent of said thermally decompos-able metal compound of less than about 750 to 1, said metal constituent being selected from the group consisting of Group II, Group III, Group IV, Group V, Group VIB, Group VIIB, and Group VIII of the Periodic Table of Elements and mixtures thereof; (b) heating said thermally decomposable metal com-pound within said chargestock at an elevated temperature in the presence of a gas selected from the group consisting of hydrogen-containing gas, a hydrogen sulfied-containing gas, and a gas comprising hydrogen and hydrogen sulfide to pro-duce a solid high surface area catalyst within said charge-stock, and (c) recovering said high surface area catalyst.
Claim 2
Dependent Claim
160 words
A high surface area catalyst prepared by the steps which comprise: (a) adding to a hydrocarbon oil chargestock having a Conradson carbon content up to about 50 weight percent, a thermally decomposable metal compound in an amount sufficient to provide a ratio of atoms of oil chargestock Conradson Car-bon to atoms of metal constituent of said thermally decompos-able metal compound of less than about 750 to 1, said metal constituent being selected from the group consisting of Group II, Group III, Group IV, Group V, Group VIB, Group VIIB, and Group VIII of the Periodic Table of Elements and mixtures thereof; (b) heating said thermally decomposable metal com-pound within said chargestock at an elevated temperature in the presence of a gas selected from the group consisting of hydrogen-containing gas, a hydrogen sulfied-containing gas, and a gas comprising hydrogen and hydrogen sulfide to pro-duce a solid high surface area catalyst within said charge-stock, and (c) recovering said high surface area catalyst.
Claim 3
Dependent Claim
32 words
The catalyst of claim 1 wherein said thermally decomposable metal compound is selected from the group con-sisting of inorganic metal compounds, salts of organic acids, organometallic compounds and salts of organic amines.
Claim 4
Dependent Claim
31 words
The catalyst of claim 1 wherein said thermally decomposable metal compound is selected from the group con-sisting of salts of acyclic aliphatic carboxylic acids and salts of alicyclic aliphatic carboxylic acids.
Claim 5
Dependent Claim
18 words
The catalyst of claim 1 wherein said thermally decomposable metal compound is a salt of a naphthenic acid.
Claim 6
Dependent Claim
33 words
The catalyst of claim 1 wherein the metal con-stitutent of said thermally decomposable metal compound is selected from the group consisting of molybdenum, tungsten, chromium, vanadium, cobalt, titanium, iron, nickel and mix-tures thereof.
Claim 7
Dependent Claim
14 words
The catalyst of claim 1 wherein said thermally decomposable metal compound is molybdenum naphthenate.
Claim 8
Dependent Claim
14 words
The catalyst of claim 1 wherein said thermally decomposable metal compound is phosphomolybdic acid.
Claim 9
Dependent Claim
22 words
The catalyst of claim 1 wherein said gas of step (b) comprises from about 1 to about 90 mole percent hydrogen sulfide.
Claim 10
Dependent Claim
23 words
The catalyst of claim 1 wherein said atomic ratio of Conradson carbon to said metal constituent is less than about 600 to 1.
Claim 11
Dependent Claim
23 words
The catalyst of claim 1 wherein said atomic ratio of Conradson carbon to said metal constituent is less than about 100 to 1.
Claim 12
Dependent Claim
26 words
The catalyst of claim 1 wherein said atomic ratio of Conradson carbon to metal constituent ranges from about 2 to 1 to about 600 to 1.
Claim 13
Dependent Claim
18 words
The catalyst of claim 1 wherein said added thermally decomposable metal compound comprises a mixture of metal compounds.
Claim 14
Dependent Claim
22 words
The catalyst of claim 12 wherein said mixture of added thermally decomposable metal compounds comprises a molybdenum compound and a cobalt compound.
Claim 15
Dependent Claim
22 words
The catalyst of claim 1 wherein at least one additional catalytic metal component is composited with said recovered high surface area catalyst.
Claim 16
Dependent Claim
21 words
The high surface area catalyst of claim 1 wherein said catalyst has a surface area of at least about 50 m2/g.
Claim 17
Dependent Claim
41 words
The high surface area catalyst of claim 1 wherein said metal constituent of said thermally decomposable compound is present in said catalyst in an amount of at least 10 weight percent, calculated as the elemental metal, based on the total catalyst.
Claim 18
Dependent Claim
176 words
A hydrocarbon treating process which comprises contacting a hydrocarbonaceous oil feed at treating conditions with a high surface area catalyst prepared by the steps which comprise: (a) adding to a hydrocarbon oil chargestock having a Conradson carbon content up to about 50 weight percent, a thermally decomposable metal compound in an amount sufficient to provide a ratio of atoms of oil chargestock Conradson car-bon to atoms of metal constituent of said thermally decompos-able metal compound of less than about 750 to 1, said metal constituent being selected from the group consisting of Group II, Group III, Group IV, Group V, Group VIB, Group VIIB and Group VIII of the Periodic Table of Elements and mixtures thereof; (b) heating said thermally decomposable metal com-pound within said chargestock at an elevated temperature in the presence of a gas selected from the group consisting of a hydrogen-containing gas, a hydrogen sulfide-containing gas and a gas comprising hydrogen and hydrogen sulfide, to pro-duce a solid high surface area catalyst within said charge-stock, and (c) recovering said high surface area catalyst.
Claim 19
Dependent Claim
176 words
A hydrocarbon treating process which comprises contacting a hydrocarbonaceous oil feed at treating conditions with a high surface area catalyst prepared by the steps which comprise: (a) adding to a hydrocarbon oil chargestock having a Conradson carbon content up to about 50 weight percent, a thermally decomposable metal compound in an amount sufficient to provide a ratio of atoms of oil chargestock Conradson car-bon to atoms of metal constituent of said thermally decompos-able metal compound of less than about 750 to 1, said metal constituent being selected from the group consisting of Group II, Group III, Group IV, Group V, Group VIB, Group VIIB and Group VIII of the Periodic Table of Elements and mixtures thereof; (b) heating said thermally decomposable metal com-pound within said chargestock at an elevated temperature in the presence of a gas selected from the group consisting of a hydrogen-containing gas, a hydrogen sulfide-containing gas and a gas comprising hydrogen and hydrogen sulfide, to pro-duce a solid high surface area catalyst within said charge-stock, and (c) recovering said high surface area catalyst.
Claim 20
Dependent Claim
28 words
The hydrocarbon treating process of claim 17 wherein said process is a hydroprocess and wherein said oil and said catalyst are contacted in the presence of added hydrogen.
Claim 21
Dependent Claim
20 words
The process of claim 17 wherein said hydro-carbon treating process is catalytic cracking conducted in the absence of added hydrogen.
Claim 22
Dependent Claim
12 words
The process of claim 18 wherein said hydro-process is a hydrocracking process.
Claim 23
Dependent Claim
12 words
The process of claim 18 wherein said hydro-process is a hydrodesulfurization process.
Claim 24
Dependent Claim
32 words
The process of claim 17 wherein said thermally decomposable metal compound is selected from the group con-sisting of inorganic metal compounds, salts or organic acids, organometallic compounds and salts of organic amines.
Claim 25
Dependent Claim
31 words
The process of claim 17 wherein said thermally decomposable metal compound is selected from the group con-sisting of salts of acyclic aliphatic carboxylic acids and salts of alicyclic aliphatic carboxylic acids.
Claim 26
Dependent Claim
18 words
The process of claim 17 wherein said thermally decomposable metal compound is a salt of a naphthenic acid.
Claim 27
Dependent Claim
33 words
The process of claim 17 wherein the metal constituent of said thermally decomposable metal compound is selected from the group consisting of molybdenum, tungsten, chromium, vanadium, cobalt, titanium, iron, nickel and mixtures thereof.
Claim 28
Dependent Claim
14 words
The process of claim 17 wherein said thermally decomposable metal compound is molybdenum naphthenate.
Claim 29
Dependent Claim
14 words
The process of claim 17 wherein said thermally decomposable metal compound is phosphomolybdic acid.
Claim 30
Dependent Claim
43 words
The process of claim 17, wherein said hydro-carbonaceous oil feed of said hydrocarbon treating process is selected from the group consisting of petroleum derived oils, tar sand oil, shale oil, liquid products derived from coal liquefaction processes, coal liquefaction bottoms, and mixtures thereof.
Claim 31
Dependent Claim
12 words
The process of claim 28 wherein said hydro-process is a reforming process.
Claim 32
Dependent Claim
22 words
The process of claim 17 wherein said gas of step (b) comprises from about 1 to about 90 mole percent hydrogen sulfide.
References Cited (Backward Citations)
No citation records indexed.
USPTO Annuity & Maintenance Windows
Maintenance schedule is calculated for granted US utility patents.