Anneal technique for reducing amount of electronic trap in gate oxide film of transistor
Assignee: Toshiba Corp
•
Filing: 1997-12-19
•
Granted: 2001-02-13
•
Expires: 2017-12-19
Abstract
Abstract A memory cell of EEPROM having a floating gate, a control gate, a drain region, and a source region is formed on a silicon substrate. Thereafter, a BPSG film (interlayer insulating film) covering the memory cell is formed by CVD. After a wire including a bit line, an SiON film (passivation film), covering the silicon substrate and serving as an uppermost layer, is formed on an upper portion of the silicon substrate. Thereafter, annealing is performed to discharge water in the BPSG film to an outer portion of an LSI. The annealing is performed under a condition satisfying the following equation ofwhere t is anneal time (minutes), L is a thickness (nm) of the passivation film, and T is anneal temperature (absolute temperature). Thereby, an amount of electronic trap in a gate oxide film of the transistor can be reduced.
Inventors
- 👤 Susumu Shuto
- 👤 Miwa Tanaka
- 👤 Masahisa Sonoda
- 👤 Toshiaki Idaka
- 👤 Kenichi Sasaki
- 👤 Seiichi Mori
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 02:11
CPC Classifications
H; H10; H10B; H10B41/00; H10B41/30; H10B69/00; H10D; H10D64/00; H10D64/60; H10D64/66; H10D64/68; Y; Y10; Y10S; Y10S438/00; Y10S438/902; Y10S438/904
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
82 words
A method for manufacturing a semiconductor device comprising the steps of: forming a transistor having a gate insulating film an interlayer insulating film, and a wire on a semiconductor substrate; forming a first passivation film, covering said transistor, said interlayer insulating film, and said wire; annealing after forming said first passivation film; and forming a second passivation film, serving as an uppermost layer, having high moisture vapor resistance higher than said first passivation film, on said first passivation film after said annealing.
Claim 2
Independent Claim
82 words
A method for manufacturing a semiconductor device comprising the steps of: forming a transistor having a gate insulating film an interlayer insulating film, and a wire on a semiconductor substrate; forming a first passivation film, covering said transistor, said interlayer insulating film, and said wire; annealing after forming said first passivation film; and forming a second passivation film, serving as an uppermost layer, having high moisture vapor resistance higher than said first passivation film, on said first passivation film after said annealing.
Claim 3
Dependent Claim
48 words
The method according to claim 1 , further comprising the steps of: monitoring an amount of electronic trap in the gate insulating film of said transistor after annealing before said second passivation film is formed; and annealing again when said amount of electronic trap exceeds a predetermined value.
Claim 4
Dependent Claim
28 words
The method according to claim 1 , wherein said annealing is performed under at least one of conditions of temperature exceeding 350° C. and time exceeding 60 minutes.
Claim 5
Dependent Claim
21 words
The method according to claim 3 , wherein said annealing is performed at temperature below a melting point of said wire.
Claim 6
Dependent Claim
51 words
The method according to claim 1 , wherein said annealing is performed under a condition satisfying the following equation: t≧ 7.86×10 −11 ×L 2 ×exp (9115 /T ) where t is anneal time (minutes), L is a thickness (nm) of said first passivation film, and T is anneal temperature (absolute temperature).
Claim 7
Dependent Claim
17 words
The method according to claim 1 , wherein said annealing is performed under pressure lower than atmosphere.
Claim 8
Dependent Claim
20 words
The method according to claim 1 wherein said transistor is a transistor constituting a memory cell of a semiconductor memory.
Claim 9
Dependent Claim
37 words
The method according to claim 1 , wherein said first and second passivation films are one insulating film selected from silicon oxide, silicon nitride and silicon oxynitride, and each of said passivation films is formed by CVD.
Claim 10
Dependent Claim
23 words
The method according to claim 1 , wherein said second passivation film is formed such that its refractive index is 1.65 or more.
Claim 11
Dependent Claim
38 words
The method according to claim 1 , wherein said interlayer insulating film is formed of silicon glass, and water in said interlayer insulating film is discharged to an outer portion of said first passivation film by said anneal.
Claim 12
Dependent Claim
24 words
The method according to claim 1 , wherein said first passivation film has moisture vapor resistance higher than that of said interlayer insulating film.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2004-02-13 | 2004-08-14 | 2005-02-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2008-02-13 | 2008-08-14 | 2009-02-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2012-02-13 | 2012-08-14 | 2013-02-13 | $7700.00 | Window Closed / Lapsed |