Non-destructive low melt test for off-composition solder
Assignee: International Business Machines Corp
•
Filing: 1997-10-21
•
Granted: 2000-01-25
•
Expires: 2017-10-21
Abstract
Abstract A non-destructive method for identifying off-composition solder columns of for example, a ceramic column grid array. The method is performed at the ceramic module level prior to card assembly to avoid costly loss or rework post card assembly. The assembly of solder columns on a substrate is heated to a temperature below the melting temperature of pure-composition solder and above the temperature of attachment of a solder column to an organic board. Heating the assembly produces visually detectable changes characteristic of off-composition solder which are used for identifying which solder columns are composed of off-composition solder.
Inventors
- 👤 Timothy W. Donahue
- 👤 Ellyn M. Ingalls
- 👤 Chon Cheong Lei
- 👤 Wai Mon Ma
- 👤 Horatio Quinones
- 👤 Charles L. Reynolds, Jr.
- 👤 Peter J. Brofman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 12:08
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/30; H05K3/32; H05K3/34; H05K3/3465; H05K1/00; H05K1/02; H05K1/0266; H05K1/0269; H05K2203/00; H05K2203/01; H05K2203/0104; H05K2203/0113; H05K2203/03; H05K2203/0338; H05K2203/16; H05K2203/163; H10; H10P; H10P74/00; H10P74/20; H10P74/203
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
86 words
A method of testing for and detecting off-composition solder columns comprising the steps of: attaching a plurality of solder columns to a substrate to form an assembly; before attachment of the assembly of the substrate and the solder columns to a circuit board, heating the assembly of the substrate and the solder columns according to a temperature profile which will produce visually detectable changes in off-composition solder columns; and visually inspecting the solder columns for changes representative of off-composition solder columns to identify off-composition solder columns.
Claim 2
Independent Claim
86 words
A method of testing for and detecting off-composition solder columns comprising the steps of: attaching a plurality of solder columns to a substrate to form an assembly; before attachment of the assembly of the substrate and the solder columns to a circuit board, heating the assembly of the substrate and the solder columns according to a temperature profile which will produce visually detectable changes in off-composition solder columns; and visually inspecting the solder columns for changes representative of off-composition solder columns to identify off-composition solder columns.
Claim 3
Dependent Claim
15 words
A method according to claim 1, further including the step of discarding off-composition solder columns.
Claim 4
Dependent Claim
43 words
A method according to claim 1, wherein the changes in off-composition solder columns include at least one of: (a) solder columns having a frosty appearance, and (b) solder columns having a diameter smaller than the diameter of other solder columns of the assembly.
Claim 5
Dependent Claim
31 words
A method according to claim 3, wherein (a) the plurality of solder columns are sheared; and (b) the changes in off-composition solder columns further includes solder columns lacking visible shear marks.
Claim 6
Dependent Claim
39 words
A method according to claim 1, wherein the temperature profile has a maximum temperature less than the melting temperature of a pure-composition solder column and greater than the temperature of attachment of a solder column to a circuit board.
Claim 7
Dependent Claim
21 words
A method according to claim 1, wherein the assembled solder columns are attached to a substrate before the assembly is heated.
Claim 8
Dependent Claim
91 words
A method according to claim 1, wherein the step of heating the assembly comprises the steps of: (a) inserting the solder columns into a furnace, (b) increasing the furnace temperature to a first temperature above which the furnace is maintained for a first duration, (c) further increasing the furnace temperature to a peak temperature less than the melting point of a pure-composition solder column, (d) decreasing the temperature of the furnace to an exit temperature which is less than the first temperature, and (e) removing the solder columns from the furnace.
Claim 9
Dependent Claim
29 words
A method according to claim 1, wherein a pure-composition solder column comprises 90% lead and 10% tin and the temperature profile does not exceed the temperature of 224° C.
Claim 10
Dependent Claim
40 words
A method according to claim 7, wherein (a) a pure-composition solder column comprises 90% lead and 10% tin, (b) the peak temperature is 224° C., (c) the first temperature is 183° C., and (d) the first duration is 3.5 minutes.
Claim 11
Dependent Claim
59 words
A method according to claim 6, further including one of the two following steps: (a) discarding a substrate and its attached solder columns when a solder column is determined to be an off-composition solder column, and (b) attaching a substrate with the attached solder columns to a circuit board when all the solder columns are determined to be pure-composition.
Claim 12
Independent Claim
121 words
A method of testing for and detecting off-composition solder columns comprising the steps of: assembling a substrate and a plurality of solder columns together; heating the assembly according to the following steps: (a) inserting the solder columns into a furnace, (b) increasing the furnace temperature to a first temperature above which the furnace is maintained for a first duration, (c) further increasing the furnace temperature to a peak temperature less than the melting point of a pure-composition solder column, (d) decreasing the temperature of the furnace to an exit temperature which is less than the first temperature, and (e) removing the solder columns from the furnace; visually inspecting the solder columns for changes in physical characteristics representative of off-composition solder columns.
Claim 13
Independent Claim
121 words
A method of testing for and detecting off-composition solder columns comprising the steps of: assembling a substrate and a plurality of solder columns together; heating the assembly according to the following steps: (a) inserting the solder columns into a furnace, (b) increasing the furnace temperature to a first temperature above which the furnace is maintained for a first duration, (c) further increasing the furnace temperature to a peak temperature less than the melting point of a pure-composition solder column, (d) decreasing the temperature of the furnace to an exit temperature which is less than the first temperature, and (e) removing the solder columns from the furnace; visually inspecting the solder columns for changes in physical characteristics representative of off-composition solder columns.
Claim 14
Dependent Claim
43 words
A method according to claim 11, wherein the changes in off-composition solder columns include at least one of: (a) solder columns having a frosty appearance, and (b) solder columns having a diameter smaller than the diameter of other solder columns of the assembly.
Claim 15
Dependent Claim
34 words
A method according to claim 12, wherein (a) the plurality of solder columns are sheared; and (b) the changes in physical characteristics of off-composition solder columns further includes solder columns lacking visible shear marks.
Claim 16
Dependent Claim
58 words
A method according to claim 11, further including one of the two following steps: (a) discarding a substrate and its attached solder columns when a solder column is determined to be off-composition solder column, and (b) attaching a substrate with the attached solder columns to a circuit board when all the solder columns are determined to be pure-composition.
Claim 17
Independent Claim
214 words
A method of testing for and detecting off-composition solder columns where a pure-composition solder column comprises 90% lead and 10% tin, the method comprising the steps of: assembling the solder columns and a substrate together by: (a) loading solder segments into a graphite mold, (b) applying flux on a surface of the substrate, (c) placing the substrate and the solder segments together, (d) processing the substrate and the mold loaded with solder segments through a furnace to form cast solder columns joined to conductive I/O pads of the substrate; heating the assembly of solder columns and substrate by: (a) inserting the assembly into a furnace, (b) increasing the furnace temperature to 183° C., (c) further increasing the furnace temperature to a peak temperature of 224° C., (d) decreasing the temperature of the furnace to an exit temperature of 75° C. at a rate such that the furnace temperature is maintained above 183° C. for 3.5 minutes, and (e) removing the assembly from the furnace; and inspecting the solder columns by at least one of: (a) visually inspecting the solder columns for a frosty appearance, (b) visually inspecting the solder columns for a diameter smaller than the diameter of other solder columns, and (c) visually inspecting the solder columns for the absence of shear marks.
Claim 18
Independent Claim
214 words
A method of testing for and detecting off-composition solder columns where a pure-composition solder column comprises 90% lead and 10% tin, the method comprising the steps of: assembling the solder columns and a substrate together by: (a) loading solder segments into a graphite mold, (b) applying flux on a surface of the substrate, (c) placing the substrate and the solder segments together, (d) processing the substrate and the mold loaded with solder segments through a furnace to form cast solder columns joined to conductive I/O pads of the substrate; heating the assembly of solder columns and substrate by: (a) inserting the assembly into a furnace, (b) increasing the furnace temperature to 183° C., (c) further increasing the furnace temperature to a peak temperature of 224° C., (d) decreasing the temperature of the furnace to an exit temperature of 75° C. at a rate such that the furnace temperature is maintained above 183° C. for 3.5 minutes, and (e) removing the assembly from the furnace; and inspecting the solder columns by at least one of: (a) visually inspecting the solder columns for a frosty appearance, (b) visually inspecting the solder columns for a diameter smaller than the diameter of other solder columns, and (c) visually inspecting the solder columns for the absence of shear marks.
Claim 19
Dependent Claim
58 words
A method according to claim 15, further comprising one of the two following steps: (a) discarding a substrate and its attached solder columns when a solder column is determined to be off-composition solder column; and (b) attaching a substrate with the attached solder columns to a circuit board when all the solder columns are determined to be pure-composition.
Claim 20
Dependent Claim
17 words
A method according to claim 1, wherein said solder columns are of a ceramic column grid array.
Claim 21
Dependent Claim
17 words
A method according to claim 11, wherein said solder columns are of a ceramic column grid array.
Claim 22
Dependent Claim
17 words
A method according to claim 15, wherein said solder columns are of a ceramic column grid array.
Claim 23
Independent Claim
101 words
A method of testing for and detecting off-composition solder columns comprising the steps of: attaching a plurality of solder columns to a substrate to form an assembly; before attachment of the assembly of the substrate and the solder columns to a circuit board, heating the assembly of the substrate and the solder columns according to a temperature profile which will produce visually detectable changes in off-composition solder columns; performing a visual inspection of the solder columns to detect changes representative of off-composition solder columns; and identifying whether solder columns are off-composition solder columns based on changes detected by the visual inspection.
Claim 24
Independent Claim
101 words
A method of testing for and detecting off-composition solder columns comprising the steps of: attaching a plurality of solder columns to a substrate to form an assembly; before attachment of the assembly of the substrate and the solder columns to a circuit board, heating the assembly of the substrate and the solder columns according to a temperature profile which will produce visually detectable changes in off-composition solder columns; performing a visual inspection of the solder columns to detect changes representative of off-composition solder columns; and identifying whether solder columns are off-composition solder columns based on changes detected by the visual inspection.
References Cited (Backward Citations)
US4076164A
Cited
US4914814A
Cited
US5324892A
Cited
US5516028A
Cited
US5620132A
Cited
US5641990A
Cited
US5718361A
Cited
US5718367A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2003-01-24 | 2003-07-26 | 2004-01-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2007-01-24 | 2007-07-26 | 2008-01-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2011-01-24 | 2011-07-26 | 2012-01-25 | $7700.00 | Window Closed / Lapsed |