Abstract
Abstract A method of using titanium chloride to etchback CVD-Ti on a patterned oxide wafer and the product formed by this process. Titanium is deposited onto a wafer composed of a silicon base and a pattern oxide layer which exposes portions of the silicon. The titanium is deposited onto the wafer by CVD-Ti. The titanium is deposited as metallic Ti on the oxide layer and reacts with the silicon substrate to form titanium silicide. The wafer is then exposed to a flow of titanium tetrachloride (TiCl4) gas. The TiCl4 etches away the metallic Ti on the oxide layer and does not substantially etch the titanium silicide. Optionally titanium nitride and tungsten may then be deposited on the substrate.
Inventors
- 👤 Michael S. Ameen
- 👤 Gert Leusink
- 👤 Joseph T. Hillman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 10:45
CPC Classifications
H; H10; H10P; H10P50/00; H10P50/20; H10P50/26; H10P50/264; H10P50/266; H10P50/267; C; C23; C23C; C23C16/00; C23C16/06; C23C16/08; C23C16/14; H10D; H10D64/00; H10D64/01; H10D64/011; H10D64/0111; H10D64/0112; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/032; H10W20/033
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
85 words
A method of forming a TiSi 2 film on exposed portions of an Si substrate, comprising the steps of: providing a substrate having a silicon base and an overlying oxide layer which is patterned to expose portions of the silicon base; depositing titanium on said substrate by chemical vapor deposition to form metallic titanium on said oxide layer and titanium silicide on the exposed silicon base; and subjecting said substrate to an etchant gas comprising titanium tetrahalide to remove substantially all said metallic titanium layer.
Claim 2
Independent Claim
85 words
A method of forming a TiSi 2 film on exposed portions of an Si substrate, comprising the steps of: providing a substrate having a silicon base and an overlying oxide layer which is patterned to expose portions of the silicon base; depositing titanium on said substrate by chemical vapor deposition to form metallic titanium on said oxide layer and titanium silicide on the exposed silicon base; and subjecting said substrate to an etchant gas comprising titanium tetrahalide to remove substantially all said metallic titanium layer.
Claim 3
Dependent Claim
32 words
The method of claim 1 wherein the reaction steps are performed in a single reaction chamber without removing said substrate from said chamber until all of the reaction steps have been completed.
Claim 4
Dependent Claim
24 words
The method of claim 1 further comprising the step of: depositing a layer of titanium nitride over said titanium silicide and said exposed oxide.
Claim 5
Dependent Claim
32 words
The method of claim 3 wherein the reaction steps are performed in a single reaction chamber without removing said substrate from said chamber until all of the reaction steps have been completed.
Claim 6
Dependent Claim
17 words
The method of claim 3, further comprising the step of: depositing tungsten over the titanium nitride layer.
Claim 7
Dependent Claim
22 words
The method of claim 5 wherein said tungsten deposition step is performed by chemical vapor deposition from a WF 6 source gas.
Claim 8
Dependent Claim
21 words
The method of claim 1 wherein said titanium layer is formed by chemical vapor deposition from a titanium tetrahalide source gas.
Claim 9
Dependent Claim
15 words
The method of claim 7 wherein said titanium tetrahalide source gas is TiCl 4 .
Claim 10
Dependent Claim
37 words
The method claimed in claim 1 wherein a pressure in the range of 0.5 to 10 torr is established in said reaction chamber and said pressure is maintained in said range throughout all of said reaction steps.
Claim 11
Dependent Claim
24 words
The method of claim 1 wherein said patterned oxide layer exposes a plurality of silicon electrodes separated by a plurality of silicon dioxide insulators.
Claim 12
Dependent Claim
24 words
The method of claim 1 wherein the substrate is maintained at a temperature between about 500° C. and 600° C. during said subjecting step.
Claim 13
Dependent Claim
14 words
The method of claim 11 wherein the substrate is maintained at approximately 575° C.
Claim 14
Dependent Claim
12 words
The method of claim 1 wherein the etchant gas is titanium tetrachloride.
Claim 15
Dependent Claim
18 words
The method of claim 13 wherein the flow rate of titanium tetrachloride is greater than about 3.5 sccm.
Claim 16
Dependent Claim
19 words
The method of claim 13 wherein the flow rate of titanium tetrachloride is between about 3.5 and 15 sccm.
Claim 17
Dependent Claim
15 words
The method of claim 13 wherein the titanium tetrachloride is mixed with an inert gas.
Claim 18
Dependent Claim
16 words
The method of claim 16 wherein said inert gas is hydrogen flowing at approximately 300-1,550 sccm.
Claim 19
Dependent Claim
16 words
The method of claim 16 wherein said inert gas is argon flowing at approximately 300-1,500 sccm.
Claim 20
Dependent Claim
14 words
The method of claim 1 wherein said etchant gas energized to form a plasma.
Claim 21
Dependent Claim
15 words
The method of claim 19 wherein the plasma energy is a 250 watt RF field.
Claim 22
Independent Claim
78 words
A method of forming titanium silicide over at least one selected region of silicon on a semiconductor substrate adjacent an oxide layer, comprising the steps of: depositing titanium over a surface of a semiconductor substrate including a selected region of silicon by plasma-enhanced chemical vapor deposition of titanium, thereby forming titanium silicide on said selected region of silicon and metallic titanium on the adjacent oxide layer; and exposing said metallic titanium to titanium tetrachloride to etch the titanium.
Claim 23
Independent Claim
78 words
A method of forming titanium silicide over at least one selected region of silicon on a semiconductor substrate adjacent an oxide layer, comprising the steps of: depositing titanium over a surface of a semiconductor substrate including a selected region of silicon by plasma-enhanced chemical vapor deposition of titanium, thereby forming titanium silicide on said selected region of silicon and metallic titanium on the adjacent oxide layer; and exposing said metallic titanium to titanium tetrachloride to etch the titanium.
Claim 24
Dependent Claim
16 words
The method of claim 21 wherein said selected region of silicon defines one or more electrodes.
Claim 25
Dependent Claim
23 words
The method of claim 21 wherein said selected region of silicon defines a discontinuity selected from the group consisting of holes and vias.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-07-19 | 2003-01-18 | 2003-07-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-07-19 | 2007-01-18 | 2007-07-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-07-19 | 2011-01-18 | 2011-07-20 | $7700.00 | Window Closed / Lapsed |